Yb:CALYGLO crystals with a dopant concentration of 5 at.% were successfully grown using the Czochralski method. The crystal samples were extensively studied to analyze their structure, room temperature and low temperature spectra, and laser properties. The highest absorption cross-section at 977 nm was calculated to be 1.83 × 10−20 cm2 for σ polarization and 5.32 × 10−20 cm2 for π polarization. Similarly, the emission cross-section was determined to be 1.38 × 10−20 cm2 at 980 nm for σ polarization and 2.28 × 10−20 cm2 at 981 nm for π polarization, with a full width at half maximum (FWHM) of 50.3 nm and 89.5 nm, respectively. The fluorescence lifetime of the 5 at.% Yb:CALYGLO crystal at 2F5/2 was measured to be 1.10 ms. Additionally, gain cross-sections were calculated for different β values. In the continuous laser experiment, the crystal demonstrated a laser output of 20.15 W at 1057 nm, with a slope efficiency of 53.3%. These experimental findings indicate that the lattice of Y3+ in the crystal is partially replaced by Lu3+ and Gd3+, resulting in a broader spectrum. Consequently, this crystal shows promising potential as a gain medium for ultrashort pulse laser crystals. [ABSTRACT FROM AUTHOR]

In this paper, the Floating zone technique was used to grow high-quality Cr3+:YScO 3 crystals. The absorption cross-sections of the 4A 2 →4T 1 transition and 4A 2 →4T 2 transitions were calculated to be 1.71 × 10−20 cm2 at 488 nm and 0.72 × 10−20 cm2 at 666 nm, respectively. The crystal field strength Dq, Racah parameters B, and C were calculated to be 1502 cm−1, 533 cm−1, and 3362 cm−1, respectively. In the Cr3+:YScO 3 crystal, the effective phonon energy and Huang-Rhys factor S were calculated to be 284 cm−1 and 8.62, respectively. The emission cross-section at 988 nm corresponding to the 4T 2 →4A 2 transition was calculated to be 1.44 × 10−20 cm2 with full width at half maximum (FWHM) of 318 nm. All the results show that Cr3+:YScO 3 crystal has the potential to be a tunable and ultrafast laser crystal. • Cr:YScO 3 crystals were successfully grown by the Floating zone technique(FZ) method. • Broad emission spectrum with full width at half maximum (FWHM) of 318 nm in Cr:YScO 3 crystals was observed. • Spectral properties and crystal field parameters of Cr:YScO 3 crystals were investigated and analysed. [ABSTRACT FROM AUTHOR]

A Nd:BGSO crystal with the dimensions of Φ2 × 131 mm3 has been grown successfully by the micro-pulling-down method. The peak absorption cross-section at 808 nm was calculated to 0.98 × 10−20 cm2 with full-width at half-maximum of 17.4 nm. The stimulated emission cross-section was obtained to be 3.15 × 10−20 cm2 at 1063 nm. The fluorescence and radiative lifetimes of 4F 3/2 level were 248 μs and 300 μs respectively. All results indicate that the Nd: BGSO single crystal would be a promising near-IR solid-state laser material. [ABSTRACT FROM AUTHOR]