Search

Whitlockite-type structure phosphors have received extensive attention and research due to their adjustable chemical compositions in isomorphic compounds and providing rich crystal positions for doping activators. Ca 2.6 K 0.2 La 0.2 (PO 4) 2 whitlockite-type phosphors with Dy3+ singly doping and Dy3+, Eu3+ co-doping were prepared via high temperature solid-phase reaction, and the crystallographic characteristics, luminescence properties and temperature sensing performance were investigated in detail. The prepared phosphors are pure phase and both Dy3+ and Eu3+ enter into the matrix and produce blue, yellow and red emissions. The CCT values of the emitted light from Ca 2·6 K 0·2 La 0·2 (PO 4) 2 : Dy3+, Eu3+ phosphors increase with the Eu3+ concentration rises, changing from cold white light to warm white light. The integrated emission intensity of Dy3+ in the phosphor decreases with the change in the doping ratio of Dy3+ and Eu3+, causing by the energy transfer from Dy3+ to Eu3+. The Ca 2·6 K 0·2 La 0·13 (PO 4) 2 :0.06Dy3+, 0.01Eu3+ phosphor shows temperature sensing performance based on FIR technique, with the maximum relative sensitivity calculated to be 0.181% K−1. All the results reveal that the Ca 2·6 K 0·2 La 0·2 (PO 4) 2 : Dy3+, Eu3+ phosphors can be applied to w-LEDs and display devices, and can be used as a new type of optical thermometer. Dy3+/Eu3+ co-doped Ca 2·6 K 0·2 La 0·2 (PO 4) 2 phosphor applied for w-LEDS and temperature sensing. [Display omitted] • Single-phase luminescent materials Dy3+, Eu3+ co-doped Ca 2·6 K 0·2 La 0·2 (PO 4) 2 phosphor with whitlockite structure was synthesized for the first time. • The concentration quenching and energy transfer mechanisms were investigated. • The emission color of Ca 2·6 K 0·2 La 0·2 (PO 4) 2 : Dy3+, Eu3+phosphors changes from natural white light to warm white light with the increase of Eu3+ concentration. • The samples showed temperature sensing performance with maximum S a to be 2.06 × 10−3 K−1 and S r to be 0.181% K−1 under 303 K. [ABSTRACT FROM AUTHOR]

Rare earth doped luminescent sensing materials as non-contact thermometers have attracted extensive research interests due to their wide applications in areas like military, medical care, aerospace, etc. How to expand the working temperature range and improve the sensitivity has become the focus. In this work, we synthesized a series of apatite-structured luminescent temperature sensors M 2 La 7.9 Ce 0.1 (SiO 4) 6 O 2 (M = Ca, Sr, Ba) via isomorphic substitution. By monitoring the differential changes of emission intensities from Ce3+ at the 7-coordinate and 9-coordinate site respectively when temperature varies, the real-time temperature can be determined. These materials were proven to possess the maximum absolute sensitivity up to 0.825 × 10−3 K−1, 2.63 × 10−3 K−1 and 4.33 × 10−3 K−1, respectively. Meanwhile interesting regular patterns were observed for their temperature sensitivities with the substitution of Ca, Sr and Ba. Furthermore, through studying the temperature sensitivity of Ba 2 La 8 (SiO 4) 6 O 2 : x Ce3+ samples with different concentrations, it was found that when the Ce3+ content was at the optimal doping concentration of 0.7, the absolute sensitivity of the sample reached 14.64 × 10−3 K−1 at 573 K. This finding has opened up a new avenue for designing fluorescent temperature sensors. Synopsis: In this work, Ce3+ were doped into a series of phosphor-structured matrices containing two cationic sites (7-coordinated Ce1 and 9-coordinated Ce2 sites) via the solid-state high-temperature method. Due to the different temperature dependencies of luminescence intensities between the two Ce3+ sites, their intensity ratio could be used for temperature calibration. [Display omitted] [ABSTRACT FROM AUTHOR]

The constructed high-efficient cyan-emitting phosphors establish a bifunctional platform involving high-color-quality lighting and anti-counterfeiting application. [Display omitted] • Ca 8 ZnY(PO 4) 7 :Eu2+ phosphors exhibited a broad cyan-emitting spectra (FWHM = 78 nm). • The quantum yield of Ca 8 ZnY(PO 4) 7 :Eu2+ phosphor is as high as 72.11 %. • The CRI value of warm w -LED devices was greatly enhanced from 83.9 to 90.5. • The transparent anticounterfeiting film held great potentials in packaging field. Constructing the broad-band emitting luminescent materials with high quantum yield is of great significance towards their widespread applications. Herein, series of Eu2+ activated, whitlockite-type Ca 8 ZnY(PO 4) 7 phosphors are developed towards bifunctional platform involving the white LED and anti-counterfeiting field. Benefiting from the typical 5d-4f transitions among Eu2+ ions, the broad asymmetric cyan-emission spectra (FWHM = 78 nm) is generated under 365 nm excitation with a highest quantum yield of ∼72.11 %. The optimal doping concentration of Eu2+ ions in the Ca 8 ZnY(PO 4) 7 host is determined as 4 % and the concentration quenching mechanism is mainly attributed to a dipole–dipole interaction. Impressively, after exploiting the newly discovered cyan-emitting phosphors Ca 8 ZnY(PO 4) 7 :Eu2+, the CRI value of as-prepared warm w -LED devices is remarkably enhanced from 83.9 to 90.5. Moreover, the w -LED exhibits an applicable correlated color temperature (CCT = 4176 K) and good color stability. Additionally, the transparent anticounterfeiting film is fabricated based on the highly efficient phosphors and soluble PVA, which presents anticounterfeiting performances due to their bright cyan emission upon UV light. Notably, their sustainability, excellent flexibility and foldability provide more possibilities applied for anticounterfeiting field. These results suggest the highly efficient phosphors Ca 8 ZnY(PO 4) 7 :Eu2+ are promising bifunctional luminescent platforms, for both high-color-quality lighting and anticounterfeiting applications. [ABSTRACT FROM AUTHOR]

LED occupies a broad market due to its many advantages as a fourth-generation solid-state light source. However, single-component white LED generally has the disadvantages of high coloring temperature, low thermal stability, and low luminous efficiency. In order to solve these problems, Gd 5 Si 2 BO 13 :Dy3+,Eu3+ was prepared by a high temperature solid state method using a newer borate matrix based on Gd 5 Si 2 BO 13. A colour-tunable warm white phosphor was achieved by energy transfer between Dy3+ and Eu3+. The crystal structure, luminescence characteristics, thermal stability of luminescence, fluorescence lifetime and energy transfer mechanism were systematically studied, and the samples obtained had excellent luminescence performance. Its thermal stability of 150 °C luminescence was 83.77%. By adjusting the ratio of Eu3+, its color changes from cool white light to warm white light and finally moves to red light. Its corresponding color temperature can be adjusted to a range of 5475k∼2128 K. The packaging w-LED application test and the application test of colorless fluorescent anti-counterfeiting printing ink were carried out, and both showed excellent performance. This is the first time that Dy3+ and Eu3+ have been studied in Gd 5 Si 2 BO 13 , further understanding the newer substrate Gd 5 Si 2 BO 13 , and promoting the application of single-component warm white LED. Therefore, Gd 5 Si 2 BO 13 :Dy3+,Eu3+ have good market application prospects. [Display omitted] • Through the energy transfer between Dy3+ and Eu3+, Gd 5 Si 2 BO 13 :Dy3+/Eu3+ shows excellent Warm white light performance. • The phosphor showed good luminescence thermal stability, UV stability and wet resistance stability. • The color temperature of the sample was adjusted from 5475K to 2128K by adjusting the doping concentration of Eu3+. • The LED application test with Gd 5 Si 2 BO 13 :Dy3+,Eu3+ package shows good performance. [ABSTRACT FROM AUTHOR]

Cryolite was considered to be an ideal up-conversion host material due to its low phonon energy, which can effectively suppress the radiation-free transition process of excited state energy levels. In the present paper, a novel up-conversion material K 3 YF 6 :Ho3+, Yb3+ with cryolite structure was prepared successfully using a high-temperature solid state method. The up-conversion luminescence properties of K 3 YF 6 doped with different Ho3+/Yb3+ doping ratio were investigated and the optimal doping ratio were confirmed in this system. Under 980 nm excitation, Ho3+/Yb3+ co-doped K 3 YF 6 revealed a strong green emission at the 541 nm, 549 nm and a weak red emission peaking at 666 nm, corresponding to the 5F 4 , 5S 2 →5I 8 and 5F 5 →5I 8 transitions of Ho3+, respectively. All the red and green up-conversion emission of K 3 YF 6 :Ho3+, Yb3+ belong to two-photon process and energy transfer from Yb3+ to Ho3+ simultaneously. Additionally, to understand the energy transfer and electronic transition process of the red and green light emitted, the possible luminescence mechanism were also analyzed in this paper. All the results indicate that Ho3+/Yb3+ co-doped K 3 YF 6 have potential application value in green up-conversion luminescent materials. • Single-phase up-conversion luminescent materials K 3 YF 6 : Ho3+,Yb3+ with cryolite structure were obtained for the first time. • The up-conversion luminescence properties and mechanism of the as-prepared samples were analyzed under excitation of 980 nm. • Two-phonon up-conversion phenomenon was confirmed. [ABSTRACT FROM AUTHOR]