Hole injection through V-defect sidewalls into all quantum wells (QWs) of long wavelength GaN light emitting diodes had previously been proposed as means to increase efficiency of these devices. In this work, we directly tested the viability of this injection mechanism by electroluminescence and time-resolved photoluminescence measurements on a device in which QW furthest away from the p-side of the structure was deeper, thus serving as an optical detector for presence of injected electron–hole pairs. Emission from the detector well confirmed that, indeed, the holes were injected into this QW, which could only take place through the 10 1 ¯ 1 V-defect sidewalls. Unlike direct interwell transport by thermionic emission, this transport mechanism allows populating all QWs of a multiple QW structure despite the high potential barriers in the long wavelength InGaN/GaN QWs. [ABSTRACT FROM AUTHOR]

We investigate the unexpected high-energy electroluminescence (EL) peaks observed in long-wavelength InGaN light-emitting diodes (LEDs) with ground state emission peaks between ∼495 and 685 nm by studying the EL spectra of LEDs with varying quantum well (QW) thicknesses and indium compositions. In addition to the ground state emission, two high-energy emission peaks were observed in the LEDs with thick QWs and high indium compositions. The less energetic high-energy emission peak (2.4–2.6 eV) is attributed to the optical transitions involving excited states. Factors influencing the excited state transitions, such as the QW thickness and indium compositions, were also examined by simulations to better understand the occurrence of these transitions. The more energetic high-energy emission peak (2.8–3.1 eV) originates from V-defect sidewalls and was verified through micro-photoluminescence measurements. Identification of the high-energy emission peaks is essential as it enables targeted epitaxial or growth optimizations to minimize or eliminate these undesirable emission peaks. This work demonstrates the importance of using thin QWs to suppress the unwanted high-energy emissions due to excited state transitions and V-defect sidewalls for long-wavelength InGaN LEDs. [ABSTRACT FROM AUTHOR]