Search

The efficiency of high-power operation of multiple quantum well (QW) light emitting diodes (LEDs) to a large degree depends on the realization of uniform hole distribution between the QWs. In long wavelength InGaN/GaN QW LEDs, the thermionic interwell hole transport is hindered by high GaN barriers. However, in polar LED structures, these barriers may be circumvented by the lateral hole injection via semipolar 10 1 ¯ 1 QWs that form on the facets of V-defects. The efficiency of such carrier transfer depends on the transport time since transport in the semipolar QWs is competed by recombination. In this work, we study the carrier transfer from the semipolar to polar QWs by time-resolved photoluminescence in long wavelength (green to red) LEDs. We find that the carrier transfer through the semipolar QWs is fast, a few tens of picoseconds with the estimated room temperature ambipolar diffusion coefficient of ∼5.5 cm2/s. With diffusion much faster than recombination, the hole transport from the p-side of the structure to the polar QWs should proceed without a substantial loss, contributing to the high efficiency of long wavelength GaN LEDs. [ABSTRACT FROM AUTHOR]

A highly relaxed InGaN buffer layer was demonstrated over a full two-inch c-plane sapphire substrate by metalorganic chemical vapor deposition. The InGaN buffer layer was grown on a 100 nm GaN decomposition stop layer with a 3 nm thick high indium composition InGaN underlayer. After thermal decomposition of the underlayer at 1000 °C, a 200 nm thick In0.04Ga0.96N buffer showed 85% biaxial relaxation measured by a high resolution x-ray diffraction reciprocal space map. When used as a pseudo-substrate for the regrowth of InGaN/InGaN multi-quantum wells, the sample showed a 75 nm red-shift in room temperature photoluminescence when compared to a co-loaded GaN template reference. The longer emission wavelength is associated with higher indium incorporation in the InGaN layers from the lessening of the compositional pulling effect caused by compressive strain. Using this technique, a simple red light emitting diode was demonstrated with an active layer growth temperature of 825 °C and a peak wavelength of 622 nm at a current density of 20 A cm−2. This work represents a unique method to relax a III-nitride based layer over a full substrate. [ABSTRACT FROM AUTHOR]

Nitride based light emitting diodes (LEDs) have demonstrated very high efficiency in the blue and green wavelength ranges. For full color LED based displays, efficient and small sized devices emitting in the three primary colors - red, green and blue are required. While phosphide based red LEDs are highly efficient, high surface recombination velocities limit their scaling to small dimensions. Nitride emitters can be scaled to smaller sizes, however for longer emission wavelength such as yellow, orange, and red, the indium content in the active region of the devices needs to be >30%. Due to the large lattice mismatch between GaN and InN, the needed high indium content introduces a large strain in the structure, often resulting in poor material quality. Recently, a novel technique to mitigate this lattice mismatch induced strain was demonstrated with the use of compliant porous GaN underlayer based substrates. In our previous reports, we have discussed the surface morphology, strain state evolution and device demonstrations using these substrates, however a detailed discussion regarding the pore cross-sections and dislocation propagation for each generation of these porous GaN substrates was yet to be reported. In this work, we will discuss the cross-sectional transmission electron microscopy (TEM) results of these substrates across multiple stages of the substrate technology development. [ABSTRACT FROM AUTHOR]

Purpose: This study aims to focus on roughening N-face (backside) GaN substrate prior to GaN-on-GaN light-emitting diode (LED) growth as an attempt to improve the LED performance. Design/methodology/approach: The N-face of GaN substrate was roughened by three different etchants; ammonium hydroxide (NH4OH), a mixture of NH4OH and H2O2 (NH4OH: H2O2) and potassium hydroxide (KOH). Hexagonal pyramids were successfully formed on the surface when the substrate was subjected to the etching in all cases. Findings: Under 30 min of etching, the highest density of pyramids was obtained by NH4OH: H2O2 etching, which was 5 × 109 cm–2. The density by KOH and NH4OH etchings was 3.6 × 109 and 5 × 108 cm–2, respectively. At standard operation of current density at 20 A/cm2, the optical power and external quantum efficiency of the LED on the roughened GaN substrate by NH4OH: H2O2 were 12.3 mW and 22%, respectively, which are higher than its counterparts. Originality/value: This study demonstrated NH4OH: H2O2 is a new etchant for roughening the N-face GaN substrate. The results showed that such etchant increased the density of the pyramids on the N-face GaN substrate, which subsequently resulted in higher optical power and external quantum efficiency to the LED as compared to KOH and NH4OH. [ABSTRACT FROM AUTHOR]