Search

Cellulosic-based materials such as hemp fabric and paper have combined characteristics of renewability, biodegradability, flexibility, and recyclability. However, regular products are not suitable for use in unconventional applications due to inherent limitations, and accordingly, enabling new capabilities is a necessity. To this end, the conversion of regular hemp fabric and paper into high-strength products with hydrophobic function via surface engineering was explored. The fluorinated waterborne polyurethane (FWPU) emulsions were first synthesized as functional coatings by in-situ polymerization. The structure and properties of the FWPU emulsion and film were characterized by FTIR, XRD, SEM, TG, and XPS. The results showed that the grafting of perfluorooctanol imparts WPU film excellent hydrophobicity, and the water contact angle increases from 71.2° to 105.9°. After the FWPU coating, the water contact angles of the hemp fabric and paper increase from 0° to 117.1° and 112.8°, respectively. Quite encouragingly, the coating generation of waterborne polyurethane-derived functional additives led to the increase of mechanical strength by more than 23% and 82%, in the case of qualitative filter paper and hemp fabric. Meanwhile, the folding strength of filter paper is increased by 132 times. Overall, this functionalized waterborne polyurethane coating would direct paper and hemp fabric toward diversified applications. [ABSTRACT FROM AUTHOR]

Hemp hurd fiber, a low-value waste stream from the hemp industry, has potential downstream applications as an alternative to non-renewable plastics for single-use food service ware and packaging applications. Packaging paper substrates made from chemically pulped hemp hurd, mixed in varying ratios with bleached thermomechanical radiata pine pulp were developed and tested. Handsheets were characterized using several mechanical property tests including tensile strength, tearing resistance, burst strength, short-span compression, ring crush, together with Gurley air resistance, contact angle, and Cobb60 tests. Generally, addition of hemp hurd fibers significantly improved handsheet mechanical properties. Hot-pressing of the handsheets so as to approximate molded fiber thermoforming further enhanced their performance, with pure hemp hurd handsheets having the highest mechanical properties and barrier performance. A prototype was successfully thermoformed from hemp fiber, demonstrating overall feasibility of this fibre source for molded fibre objects. [ABSTRACT FROM AUTHOR]

A significant increase in the consumption of recycled fiber products has been observed worldwide, and the industry is forced to solve the challenges of recycled fiber quality and add strength agents and/or virgin fibers to reach sufficient properties. In order to investigate whether the mechanical and air permeability properties of waste fiber (WF) material can be significantly improved by adding wood kraft fibers (KF), hemp soda fibers (HF), and ammonium persulfate oxidated cellulose nanofibrils (CNF), different fiber blends were prepared and tested. Results revealed the excellence of hemp fibers over wood fibers regarding the improvement of WF products. The results of WF after the addition of 10% mixed fibers (KF + HF) were higher than the results of a 50% KF addition. The impact of CNF depended on fiber composition and properties. A formula for modeling the CNF impact on different fiber compositions was proposed. Obtained fiber material samples showed suitability for home composting, thus contributing to the goals of the European Green Deal regarding reducing landfill waste and the development of cleaner products. [ABSTRACT FROM AUTHOR]

The study describes the preparation of nanocellulose from organosolv hemp pulp and its application in the production of food packaging paper as an alternative to petroleum products. OHP was obtained from renewable plant materials hemp fibers by extraction with NaOH solution and cooking using a mixture of acetic acid and hydrogen peroxide. A stable transparent nanocellulose gel was extracted from OHP by acid hydrolysis followed by ultrasonic treatment. It was found that an increase in the consumption of sulfuric acid, temperature and duration of the OHP hydrolysis process improved the quality indicators of hemp nanocellulose. A linear dependence of the tensile strength and transparency of nanocellulose films on their density has been established. Morphological (SEM), structural (FTIR and XRD) and thermal analysis (TGA) of hemp fibers, OHP and nanocellulose were carried out. Nanocellulose films had a density of up to 1.56 g/cm3, a tensile strength of up to 66.7 MPa, a transparency of up to 87.3%. Atomic force microscopy method showed that the transverse dimension of nanocellulose particles is from 8 to 23 nm. Hemp nanocellulose had a higher crystallinity index (87.2%) than OHP (72.0%), but lower thermal stability. The positive effect of adding nanocellulose from hemp on improving all quality parameters of paper for food packaging has been shown. The addition of 2% hemp nanocellulose makes it possible to obtain paper that exceeds the breaking force requirements of premium grade paper by 40%, and the breaking length increases by 42% compared to paper without chemical additives. [ABSTRACT FROM AUTHOR]

The features of the primary preparation of hemp straw stalks suitable for obtaining cellulosecontaining materials and paper are considered in the article. The primary processes of the preparation of hemp raw materials for pulp production, which include harvesting, storage of straw stalks, transportation, and primary processing of raw materials suitable for obtaining cellulose-containing materials, are described. Methods of shortening stems and fibers applied in the pulping process are studied in detail. Technological methods of shortening straw stalks of technical hemp and cleaning raw materials from grains and garbage impurities are mentioned. The necessity of applying the processes of stalks crushing and wet purification of chopped straw stalks of technical hemp is proved. [ABSTRACT FROM AUTHOR]