The photocatalytic membranes have been reported to treat textile dye effluents; however, it is challenging to maintain their long-term functionality due to the poor binding stability of nanoparticles on the membrane surface and the low stability of the membrane to UV radiation. To address this, PVDF photocatalytic hollow fiber membranes were prepared by coating with polydopamine (PDA) for 1–4 h, then with titanium dioxide nanoparticles (TiO 2) in the current study. SEM and EDX results showed that TiO 2 adhered firmly to the PDA-pretreated membrane after ultrasonic treatment. The PDA layer protected the membranes from UV irradiation. The PVDF-TiO 2 membrane without PDA pretreatment was destroyed after 24 h of UV irradiation, while after 9 days of continuous irradiation, the membranes treated with PDA for 2 h remained unchanged. Compared with the original membrane, applying PVDF membranes coated with PDA for 2 h and TiO 2 for 1 h increased the Reactive Red 239 rejection and flux recovery rates by 13% and 40%, respectively, achieving 60% COD removal. The permeate flux and dye rejection rate were stable after 5 cycles (20 h of operation). This study demonstrates that the obtained membranes can perform prolonged membrane filtration with high-performance durability for dye wastewater treatment. [Display omitted] • TiO 2 was strongly bonded to the PVDF membrane pretreated with PDA. • Introducing PDA-TiO 2 enhanced the stability of dye permeate flux and dye rejection. • The PVDF-PDA-TiO 2 membranes significantly improved the COD removal efficiency. • PVDF-PDA-2h-TiO 2 -1 h membrane showed excellent resistance to UV and reusability. • Self-protecting/cleaning, hydrophilicity, and durability of membrane all improved. [ABSTRACT FROM AUTHOR]

In this work, a positively charged hollow fiber nanofiltration (NF) membrane based on twice interfacial polymerization (IP) reactions was developed for water soften and heavy metal ions removal. The first IP reaction was conducted on the polyethersulfone (PES) hollow fiber substrate using a mixture of branched polyethyleneimine (PEI) and piperazine (PIP) as the aqueous phase monomers in the aqueous phase reacting with trimesoyl chloride (TMC) in the cyclohexane solution. Then, a secondary IP reaction was performed between tris(2-aminoethyl) amine (TAEA) solution and the residual acyl chloride groups on the membrane to increase the positive charge density on the membrane surface. Consequently, a NF membrane with intensified positive surface charge density was successfully fabricated. The optimized membranes achieved a high rejection of MgCl 2 of 97.6% while maintaining a pure water permeability (PWP) of 16.0 L m−2 h−1 bar−1. Meanwhile, the membranes exhibit high rejection values of 99.8% to Cu2+ and 99.7% to Zn2+, respectively. In conclusion, this work provides a facile way to prepare a positively charged membrane for efficient water softening and metal ions removal. [Display omitted] • A novel polyamide NF hollow fiber membrane via a secondary IP reaction had been successfully fabricated. • The secondary IP reaction between TAEA and the residual acyl chloride groups effectively enhances the positive change density on membrane surface. • This modification method has no influence on membrane structure. • The optimum membrane shows more than 90% rejection of Mg2+ and Ca2+ and 99% rejection of heavy metals. [ABSTRACT FROM AUTHOR]

• An acid-stable polyamine NF hollow fiber module was prepared for phosphorus recovery via the IP method. • Tannic acid interlayer was first constructed onto the PES substrate to assist the spreading of the aqueous phase. • The resultant NF membrane shows only 9.6% rejection of phosphorus, alongside over 93.5% rejection of metal ions at pH 2. • Membrane water permeability can reach 20.3 LMH/bar. The hazardous heavy metals coexisting with phosphorus-containing sewage sludge seriously limit phosphorus recovery. Nanofiltration (NF) membrane, which can selectively separate heavy metals and phosphorus, has a promising potential for recovering high-quality phosphorus from sewage sludge. In this work, we utilized the undissociated form of H 3 PO 4 at pH <2 and customized an acid-stable polyamine NF membrane via interfacial polymerization (IP) for separating phosphorus and heavy metals under acidic conditions. An interlayer formed via co-deposition of tannic acid (TA) and diethylenetriamine (DETA) was firstly coated onto the polyethersulfone (PES) hollow fiber module to assist the spreading of aqueous phase on the substrate surface. Consequently, a tight and positively charged polyamine layer with a mean pore size of 0.77 nm was successfully constructed on the PES substrate, which is smaller than that of the membrane without interlayer (1.39 nm). This polyamine membrane maintained excellent stability during 15-day acid testing with 0.1 M HCl as feed solution. When it was used to recover phosphorus at acidic condition (pH 2), the phosphorus rejection of the NF membrane was only 9.8 %, much lower than that at neutral pH (46.7 %), which is due to the fact that most phosphorus existed in the undissociated form of H 3 PO 4 at pH 2. Meanwhile, given the fine-tuning pore size and Donnan exclusion effect of this membrane, it could effectively retain 96.9 % of Mg2+ and over 93.5 % of most heavy metal ions such as Pb2+, Cu2+, Fe3+, Zn2+, and Cr3+, alongside outstanding water permeability of 20.3 LMH/bar at 2-bar operation pressure. This result demonstrates the potential of our homemade polyamine membrane in phosphorus recovery. [ABSTRACT FROM AUTHOR]

[Display omitted] • Microfiltration PTFE hollow fibres were transformed into durable, high value OSN membranes. • A PEI/PIP based polyamide thin film was successfully synthesized on PTFE hollow fibre substrates. • A two-time interfacial polymerization was conducted to obtain a defect-free polyamide layer. • The resultant membranes could withstand strong aprotic solvents like DMF and DMSO. • The membranes had high solute rejections, of up to 95 % methyl orange (327 Da) rejection in DMF. Polymeric membranes have been extensively studied for organic solvent nanofiltration (OSN) but many fail to show sufficient chemical resistance in strong solvents like dimethylformamide (DMF) and dimethyl sulfoxide (DMSO). This study focuses on harnessing the outstanding chemical resistance of polytetrafluoroethylene (PTFE), to develop polyamide-PTFE thin film composite (TFC) membranes that are resistant to such aprotic solvents. A defect-free polyamide thin film layer was successfully synthesized on the microfiltration PTFE hollow fibre substrates, overcoming challenges such as large and uneven pore size, and hydrophobicity of the PTFE substrates. A simple polydopamine (PDA) coating was carried out to improve the substrate's hydrophilicity prior to the polyamide synthesis via interfacial polymerization (IP). Polyethyleneimine (PEI) and trimesoyl chloride (TMC) were used as the monomers and a two-time IP method was employed to obtain a defect-free polyamide coating. The synthesized membranes showed high acetonitrile (ACN) and DMF permeabilities of 7.94 and 3.70 lm−2h−1bar−1, respectively, with acid fuchsin (585 Da) rejections of > 90 %. The molecular weight cut-off (MWCO) of the membranes could be further reduced to ∼300 Da by the addition of piperazine (PIP) monomers. The membranes also showed excellent stability and performance in a 72-hour OSN test performed in DMF indicating their great potential in effective molecular separation in harsh solvents. This study demonstrates how a simple modification and coating technique can transform commercially available microfiltration PTFE hollow fibres into durable and high value OSN membranes. [ABSTRACT FROM AUTHOR]

Aquaporins are water channel proteins with high permeability and solute rejection, making them ideal components for the preparation of desalination biomimetic membranes. In one strategy, E. coli aquaporin Z (AqpZ) proteoliposomes are immobilized in a polyamide layer formed by interfacial polymerization at the inner surface of hollow fibers. However, once polymerization occurs, the system is almost a black box where it is difficult to disentangle the relative contribution to performance of (i) water permeation through AqpZ channels and (ii) the possible modification of the properties or structure of the polymer layer by the mere presence of protein and lipid. Indeed, the fate of protein and lipid once the polymer is formed, and how much of it is actually used, is under debate. Also, the performance of these modules has been reported to be stable over several months. This is intriguing because of the expected degradation of functional AqpZ and lipid with time. Herein, we used lipid and AqpZ, both fluorescently labeled, to unequivocally localize both components only at the inner surface of the hollow fibers. To characterize module performance, we tested about 30 half-inch modules containing five hollow fibers each. Those reconstituted with wild type AqpZ produced higher permeability (∼8.5 ± 0.9 LMH/bar) than those reconstituted with AqpZ mutant (R189A) (∼5.6 ± 1.7 LMH/bar) or lipid-only liposomes (3.7 ± 1.1 LMH/bar). However, while these differences are significant, they are smaller than expected from the comparison of relative permeabilities of membranes incorporating wild-type AqpZ, R189A mutant and only-lipid. In addition, we show that in a five-month long experiment, performance of two of these modules showed only minor deterioration, if any, which is not consistent with the observed rapid degradation of proteoliposomes at room temperature. Overall, these data obtained in this set-up suggests that although both AqpZ and lipid are localized at the inner of the hollow fibers, they mainly behave as additives that modify the properties of the robust polyamide layer. A small contribution of AqpZ channel activity to module performance is possible, but to be significant it would require full coverage and a higher protein density in the proteoliposomes, which at present cannot be achieved in the current protocol. [Display omitted] • Thirty half-inch modules (5 hollow fibers each) were tested. • Fluorescent lipid and AqpZ are only found co-localized with the IP layer. • Modules perform better with wild type AqpZ than with R189A inactive mutant. • Module performance does not directly correlate with proteoliposome permeability. • Long-term module performance is inconsistent with degradation of proteoliposomes. [ABSTRACT FROM AUTHOR]

The ultra-permeable membranes (UPMs) are expected to reduce the specific energy consumption (SEC) of desalination, but the potential of UPMs in hollow fiber configuration has not been well quantified. Herein, we analyse the SEC and footprints of UPM modules in three feed salinities: seawater reverse osmosis (SWRO), brackish water RO (BWRO) and low-pressure RO (LPRO). Through the modelling the fluid dynamics and mass transport of RO systems, we find that a tripling in spiral-wound SWRO membrane permeability (based on the current value of 1 L m−2 h−1 bar−1; LMH/bar) could result in 16% decrease in SEC. Contrastingly, the quadrupling of hollow fiber SWRO membrane permeability (based on the current value of 0.25 LMH/bar) could reduce the SEC by 23%. According to our analysis, hollow fiber and spiral-wound SWRO membranes with permeabilities up to 1 LMH/bar and 3 LMH/bar, respectively, can reduce the SEC of seawater desalination. On the other hand, membranes with permeabilities up to 9 LMH/bar and 12 LMH/bar can lead to SEC savings in BWRO and LPRO desalination, respectively. This study provides a general guidance to RO membrane researchers on the permeability upper-limit of which UPMs could bring about SEC and footprint savings at a system level. [Display omitted] • Energy savings achievable by high permeability RO membranes were quantified. • Modelling was performed by simulating fluid dynamics in various RO configurations. • Hollow fiber SWRO membranes (up to 1 LMH/bar) could reduce energy consumption. • Spiral-wound SWRO membranes (up to 3 LMH/bar) could reduce energy consumption. • High permeability RO membranes could bring about greater benefits in BWRO/LPRO. [ABSTRACT FROM AUTHOR]

The layer-by-layer (LbL) self-assembly is a common method for fabricating nanofiltration (NF) membranes. However, most multilayers are usually too thick and lack the necessary attributes to endow NF membranes with good permselectivity. In this study, we present a polyelectrolyte multilayered method by integrating dopamine as a "bio-glue". A three-step deposition was applied to the negatively charged PES substrate surface, following an alternate sequence of poly(allylamine hydrochloride) (PAH), dopamine (DA) and poly(sodium 4-styrenesulfonate) (PSS). The dopamine molecules were intercalated between the PAH and PSS layers to achieve a thinner thickness, higher hydrophilicity, smaller surface roughness and narrower pore size distribution. The resultant flat sheet (PAH/DA/PSS)4 polyelectrolyte multilayered (PEM) membranes exhibited enhanced water permeability (more than 60% increment from 13.5 to 21.9 LMH/bar) and higher rejection toward divalent ions (increasing MgCl 2 rejection from 91.0% to 94.8%) as compared with the control (PAH/PSS)4 NF membrane. Furthermore, the developed LbL method was applied on hollow fiber membrane modules and was able to achieve a higher Li+/Mg2+ selectivity from 15.6 to 37.8 and Na+/Mg2+selectivity from 11.0 to 19.1 using different simulated brines as feed solutions. On the whole, this polyelectrolyte multilayered method shows great potential for practical applications, including groundwater softening, seawater pretreatment and lithium extraction. [Display omitted] • A novel three-step LbL self-assembly method was proposed by integrating dopamine. • Dopamine intercalated selective layer exhibited a thinner and smoother surface. • The NF (PAH/DA/PSS)4 membrane showed better water permeability and higher divalent ion rejection. • Higher Na+/Mg2+ and Li+/Mg2+ selectivity was achieved due to the smaller pore size distribution. [ABSTRACT FROM AUTHOR]

A scaled-up hollow fibre thin-film composite (TFC) module was successfully developed for organic solvent forward osmosis (OSFO) application in the pharmaceutical industry. The membrane consists of cross-linked P84 polyimide substrate with a polyamide selective layer, formed via interfacial polymerisation. The performance of the lab-scale module was compared to the scaled-up module in reverse osmosis and forward osmosis modes. The results from both tests revealed that the solvent permeability of the scaled-up module decreased while its selectivity increased slightly. This might be caused by the uneven distribution of liquids during interfacial polymerisation, leading to varied membrane performance. The scaled-up module was further tested for OSFO performance using a range of PEG-400 concentrations (0.5–2 M) in acetone and isopropanol as draw solutions. At 2 M PEG-400 concentration, the module demonstrated high isopropanol and acetone permeability of 0.63 LMH and 13.9 LMH, respectively. Moreover, the reverse solute flux of PEG-400 in acetone and isopropanol were relatively low at 0.188 g/l and 0.153 g/l, respectively. The module was further tested for OSFO application in the pharmaceutical industry by concentrating levofloxacin in acetone, using 2 M PEG-400 as draw solution. The process was able to concentrate levofloxacin from 1000 ppm to 16,000 ppm with very low reverse solute flux of 0.178 g/l. Therefore, this work presents a scalable TFC membrane for OSFO application in the pharmaceutical industry. [Display omitted] • Scaled-up module (0.4 m2) of TFC hollow fibre membrane for organic solvent forward osmosis process was successfully fabricated. • High porosity (79%) and low structural parameter (217 μm) for membrane substrate was achieved. • Membrane exhibited excellent acetone and IPA solvent flux of 13.9 LMH and 0.63 LMH, respectively, using a 2 M PEG-400 draw solution. • A pharmaceutical stream was concentrated to a factor of 16 with low specific reverse solute flux [ABSTRACT FROM AUTHOR]

A scaled-up hollow fibre thin-film composite (TFC) module was successfully developed for organic solvent forward osmosis (OSFO) application in the pharmaceutical industry. The membrane consists of cross-linked P84 polyimide substrate with a polyamide selective layer, formed via interfacial polymerisation. The performance of the lab-scale module was compared to the scaled-up module in reverse osmosis and forward osmosis modes. The results from both tests revealed that the solvent permeability of the scaled-up module decreased while its selectivity increased slightly. This might be caused by the uneven distribution of liquids during interfacial polymerisation, leading to varied membrane performance. The scaled-up module was further tested for OSFO performance using a range of PEG-400 concentrations (0.5–2 M) in acetone and isopropanol as draw solutions. At 2 M PEG-400 concentration, the module demonstrated high isopropanol and acetone permeability of 0.63 LMH and 13.9 LMH, respectively. Moreover, the reverse solute flux of PEG-400 in acetone and isopropanol were relatively low at 0.188 g/l and 0.153 g/l, respectively. The module was further tested for OSFO application in the pharmaceutical industry by concentrating levofloxacin in acetone, using 2 M PEG-400 as draw solution. The process was able to concentrate levofloxacin from 1000 ppm to 16,000 ppm with very low reverse solute flux of 0.178 g/l. Therefore, this work presents a scalable TFC membrane for OSFO application in the pharmaceutical industry. [Display omitted] • Scaled-up module (0.4 m2) of TFC hollow fibre membrane for organic solvent forward osmosis process was successfully fabricated. • High porosity (79%) and low structural parameter (217 μm) for membrane substrate was achieved. • Membrane exhibited excellent acetone and IPA solvent flux of 13.9 LMH and 0.63 LMH, respectively, using a 2 M PEG-400 draw solution. • A pharmaceutical stream was concentrated to a factor of 16 with low specific reverse solute flux [ABSTRACT FROM AUTHOR]

Thin-film composite (TFC) membranes are generally preferred over integrally skinned asymmetric (ISA) membranes in pressure retarded osmosis (PRO) process due to their much higher water permeability, but they cannot operate in the active layer facing feed solution (AL-FS) orientation because of potential delamination of the rejection layer under the high applied pressure. However, operating under AL-FS orientation is preferred as a strategy for better fouling control. Hence, in this study, three ISA hollow fiber membranes were fabricated using a dry-jet wet-spinning method, followed by chemical cross-linking to obtain membranes for PRO application. The best-performing membrane was subjected to fouling test in two orientations. Our results demonstrate that the AL-FS orientation is better for a sustainable long-term PRO operation, given the stable performance throughout the two-day testing. Also, the current use of power density per membrane area as a performance benchmark may not be practical for large-scale PRO operation, and the volumetric power density per module is more relevant. In terms of volumetric power density for a hypothetical 5-in. module, our best-performing membrane is predicted to generate a 3.6 to 10 times better power density than commercial modules, rendering our ISA hollow fiber membranes promising for scaling-up to bigger modules. [Display omitted] • Operating under AL-FS orientation is preferred as a strategy for better fouling control. • Integrally skinned asymmetric hollow fiber membranes were developed for AL-FS orientation in PRO. • The membranes achieved sustainable power production when wastewater was employed. • The volumetric power density was predicted to yield promising solution for practical application. [ABSTRACT FROM AUTHOR]

Thin-film composite (TFC) membranes are generally preferred over integrally skinned asymmetric (ISA) membranes in pressure retarded osmosis (PRO) process due to their much higher water permeability, but they cannot operate in the active layer facing feed solution (AL-FS) orientation because of potential delamination of the rejection layer under the high applied pressure. However, operating under AL-FS orientation is preferred as a strategy for better fouling control. Hence, in this study, three ISA hollow fiber membranes were fabricated using a dry-jet wet-spinning method, followed by chemical cross-linking to obtain membranes for PRO application. The best-performing membrane was subjected to fouling test in two orientations. Our results demonstrate that the AL-FS orientation is better for a sustainable long-term PRO operation, given the stable performance throughout the two-day testing. Also, the current use of power density per membrane area as a performance benchmark may not be practical for large-scale PRO operation, and the volumetric power density per module is more relevant. In terms of volumetric power density for a hypothetical 5-in. module, our best-performing membrane is predicted to generate a 3.6 to 10 times better power density than commercial modules, rendering our ISA hollow fiber membranes promising for scaling-up to bigger modules. [Display omitted] • Operating under AL-FS orientation is preferred as a strategy for better fouling control. • Integrally skinned asymmetric hollow fiber membranes were developed for AL-FS orientation in PRO. • The membranes achieved sustainable power production when wastewater was employed. • The volumetric power density was predicted to yield promising solution for practical application. [ABSTRACT FROM AUTHOR]

Municipal solid waste (MSW) gasification is an attractive waste-to-energy (WTE) technology with promise for future solid waste management, owing to the production of syngas which can be used as an alternative energy resource. However, quality of produced syngas is not meeting expectation. One promising solution is to use oxygen-enriched gas (OEG) to elevate produced syngas quality but producing OEG is costly. Herein, we demonstrated an asymmetric defect-free hollow fiber membrane made up of Matrimid® 5218 polyimide for scaling-up to 2-inch membrane modules. Our modules have an effective surface area up to 2.6 m2 with a packing density of up to 44% to produce OEG of 45% O 2 purity. The 2-inch membrane module was integrated into a lab-scale gasification process to produce syngas using refuse derived fuel (RDF) generated from MSWs collected from the university campus. Prior to this, the lab-scale gasification was first optimized by tuning the gasification temperature, O 2 purity and equivalence ratio (ER). Then, MSW gasification using membrane-based OEG was carried out, and compared against air gasification and synthetic OEG of the same O 2 purity. Our results showed that, at O 2 purity of 45%, gasification temperature of 900 °C and ER of 0.15, the quality of produced syngas was elevated with a lower heating value (LHV) of 9.15 MJ/m3 and H 2 /CO ratio of 1.43, which was substantially higher than air gasification with LHV and H 2 /CO ratio reported at 5.38 MJ/m3 and 0.81, respectively. Gasification results for membrane-based OEG and synthetic OEG were also comparable, while process simulation evidence suggested that membrane-based separation was at least 2-fold less energy-intensive than cryogenic distillation and pressure swing adsorption. Overall, this proof-of-concept successfully demonstrates the viability and competitiveness of membrane process for producing OEG at medium O 2 purity (i.e. , 40–50%) to support MSW gasification for WTE conversion. [Display omitted] • Hollow fiber membrane modules with up to 2.6 m2 surface area were developed. • OEG with O 2 purity of c.a. 45% can be produced at close to 2 L/min flow rate. • Membrane-based OEG gasification produces syngas with 70% higher LHV as that of air gasification. • Membrane-based OEG produces syngas with comparable LHV as that of synthetic OEG. • Simulation shows that membrane separation is less energy-intensive for producing OEG of medium purity. [ABSTRACT FROM AUTHOR]