The automobile industry uses magnesium for load-bearing components due to its low density, durability, and ductility. This study investigated a nanocomposite containing Nb2O5 (3 and 6 wt%) nanoparticles as reinforcement with AZ31 magnesium alloy made by stir casting. A severe plastic deformation was conducted on the cast samples via equal-channel angular pressing (ECAP) after homogenization at 410 °C for 24 h and aging at 200 °C for 10 h. The microstructural distributions and mechanical properties of the magnesium metal matrix composites (MMCs) reinforced with Nb2O5 nanoparticles were investigated via ECAP. With the increase in the number of ECAP passes, the grain sizes became uniform, and the size of secondary phases reduced in the pure Nb2O5/AZ31 MMC. The grain size decreased remarkably after the ECAP process from 31.95 µm to 18.41µm due to the dynamic recrystallization during plastic deformation. The mechanical properties of hardness, ultimate tensile strength, and elongation effectively improved after each ECAP pass. The maximum values achieved for the Nb2O5/AZ31 composite subjected to ECAP were 64.12 ± 12 HV, 151.2 MPa, and 52.71%. [ABSTRACT FROM AUTHOR]

In this study, the AZ31 magnesium alloy was reinforced with tungsten disulfide (WS2) nanotubes to fabricate the nanocomposite using the stir casting method. The microstructural analysis, mechanical and wear behaviors were investigated with the effect of WS2 on the AZ31 alloy. Scanning electron microscopy (SEM) was used to conduct the microstructural analysis. The microstructures are revealed to incorporate the aluminum content with the WS2 nanotube, disclose the presence of the secondary phase, which was increased compared with the AZ31 alloy and was detected by energy dispersive spectroscopy (EDS). The mechanical properties of hardness and yield strength (YS) were significantly improved with the addition of WS2 nanotubes. This is mainly due to the strengthening mechanisms of Orowan, the coefficient of thermal expansion (CTE) mismatch and the load transfer mechanism. The theoretical YS was calculated and compared with the experimental results. However, the ultimate tensile strength (UTS) and the fracture strain were decreased with the addition of reinforcement which might be owing to the clustering of nanotubes. Finally, the wear behavior of the wear weight loss and depth of cut was investigated. This test revealed that the addition of WS2 nanotubes reduced the weight loss and depth of the material cutting that was mainly due to the presence of hard WS2 nanotubes. [ABSTRACT FROM AUTHOR]