A new Mg-4Zn X Ti-6Al-4V (TC4, of 0, 1, and 3 wt.%) alloy was successfully fabricated by a simple and low-cost gravity casting method and heat treatment at 150 °C for 24 h. The composite was examined by XRD, uniaxial tests, FESEM/EDS, potentiostat/EIS, and immersion tests for the material's microstructures, mechanical properties, electrochemical characteristics, and corrosion resistance. Experimental results indicate that heat treatment enables the precipitation of Zn along the Mg grain boundaries and drives the co-precipitation of Al around the TC4 particles and nearby grain boundaries. Uniaxial tensile tests reveal that TC4 reinforces the Mg-Zn matrix material with higher elastic modulus, ultimate tensile stress, and toughness. The heat treatment further enhanced these mechanical properties. Electrochemical tests show that 1 wt.% TC4 composite exhibits the highest open circuit potential among all tested samples, which implies the 1 wt.% TC4-added Mg-Zn is better resistant to the oxidation of the essential metals Mg, Zn, and Al. The immersion tests in the HBSS solution further show that the 1 wt.% TC4 composite has the lowest rise of pH values after 14 days, and EDS for the corroded surface signifies that Mg is the main element vulnerable to oxidation by corrosion. [ABSTRACT FROM AUTHOR]

AZ61 magnesium alloy metal matrix composites (MMCs) with different weight percentages (0, 1 and 2) of micro-silicon carbide particles (SiCp) were fabricated using stir casting method. Effects of SiCp on the microstructural distributions, mechanical and fatigue properties, and fracture surfaces have been investigated. The microstructural observations of as-cast MMCs unveil the existence of primary α-Mg phase and the presence of large amount of β-Mg17Al12 secondary phase at grain boundary. The specimens are subjected to homogenization heat treatment at 410 °C for 24 h; the β-Mg17Al12 phases are significantly dissolved in the matrix grain boundaries which enhance the ductility and decrease the hardness compared with the as-cast materials. The addition of SiCp reinforcement led to improved yield strength (YS) and ultimate tensile strength (UTS) of AZ61/SiCp composite compared to the unreinforced alloy. The maximum values of YS and UTS have been attained at AZ61/1wt%SiCp composites. The enhancement of YS and UTS was due to the presence of a uniformly distributed reinforced SiCp, which depends on grain refinement of the matrix and strong interfacial bonding between the matrix and reinforcement. In the case of fatigue test results, the addition of SiCp reduced the fatigue life and strength of AZ61 alloy composite. However, addition of 1wt%SiCp showed good mechanical and fatigue properties compared to pure AZ61 magnesium alloy and AZ61/2wt%SiCp composite. Furthermore, the effects of addition of SiCp on the mechanical and fatigue properties of the composite were confirmed by using the scanning electron microscope observation of fracture surfaces. [ABSTRACT FROM AUTHOR]