Search

Nickel ferrite owns a lot of advantages as electrode materials for supercapacitor, such as high energy density and excellent theoretical capacity. Whereas, the electrochemical performances of NiFe 2 O 4 in terms of rate performance and cycle stability are not satisfactory due to the low conductivity. While carbon fiber is a kind of material with high conductivity. Hence, NiFe 2 O 4 @ slit modified hollow carbon fiber is obtained through the coaxial electrospinning method. The slits on hollow carbon fibers are beneficial to the contact of inner NiFe 2 O 4 nanoparticles with electrolyte. Results of electrochemical tests show that at a current density of 1 A/g, the specific capacitance of NiFe 2 O 4 @ slit modified hollow carbon fiber is calculated to be 225.4 F/g, higher than that of NiFe 2 O 4 nanoparticles of 134.8 F/g. Moreover, a better cycle and rate performances (100 % vs 80 %; 71.9 % vs 47.5 %) are achieved. This work displays that slit modified hollow carbon fiber can improve the electrochemical performance of NiFe 2 O 4 efficiently. [Display omitted] • Carbon fibers are introduced to enhance the rate and cycle performances of NiFe 2 O 4. • Slits are obtained utilizing Al 2 O 3 sacrificial hard templates. • Slits are beneficial to the contact of NiFe 2 O 4 and electrolyte. [ABSTRACT FROM AUTHOR]

• The partial S-doping NiFe 2 O 4 was obtained through a facile hydrothermal method. • The d-spacing of NiFe 2 O 4 was expended caused by partial S-doping. • The impact of partial S-doping to NiFe 2 O 4 is exposed by VASP analysis. • The optimal electrode exhibited the highest specific capacitance of 284 F/g. Nickel ferrite exhibits many advantages as electrode materials in the application of supercapacitor, such as high energy capacity and excellent cycle stability. Whereas, compared with identical-metal sulfides, the specific capacitance of NiFe 2 O 4 is still insufficient. Hence, to combine the superiorities of oxides and sulfides, partial sulfur doping NiFe 2 O 4 is obtained through hydrothermal synthesis method. Analyzed by Vienna Ab-initio Simulation Package (VASP) software and high-resolution transmission electron microscopy, the lattice parameters of NiFe 2 O 4 are confirmed to be expanded by introducing sulfur atoms, which is beneficial to electrochemical performances. At a current density of 1 A/g, the specific capacitance of partial sulfur doping NiFe 2 O 4 is calculated to be 284 F/g, higher than that of the original NiFe 2 O 4 of 182.2 F/g. Moreover, a maximum energy density of 21.14 Wh/kg is achieved at a power density of 375 W/kg. This work shows that partial sulfur doping could improve the electrochemical performance of NiFe 2 O 4. To sum up, this work provides an effective way to enhance the poor electrochemical performance of oxides, greatly encouraging the application of oxides in energy storage field. [Display omitted] [ABSTRACT FROM AUTHOR]

Transitional metal nitrides (TMNs) are regarded as comparatively promising electrode materials for supercapacitor due to the high electronic conductivity, good corrosion resistance and special electron structure. Herein, in this work a heterostructure Co 2 N-Ni 3 N nanosheets-nanowires arrays grown on Ni foam (NF) are designed and synthesized by a simple hydrothermal reaction and nitriding treatment. The prepared Co 2 N-Ni 3 N/NF nanoarrays has a high electrical conductivity, abundant surface active sites, charge transfer channels and the synergy effect between each component, which makes it exhibit outstanding electrochemical performance. Electrochemical test results revealed that the areal capacitance of Co 2 N-Ni 3 N/NF was 2.17 F cm−2 at 1 mA cm−2 using a three-electrode system in 1 M KOH. Meanwhile, when the current density increases to 20 mA cm−2, it can still retain 62.21% of the original capacitance, suggesting a good rate capability. In addition, in two-electrode test with Co 2 N-Ni 3 N/NF as the positive electrode and activated carbon as the negative electrode, a maximum energy density of 145.65 μWh cm−2 is shown when the power density is 0.75 mW cm−2. And it has 85.90% capacitance retention after 5000 cycles. [Display omitted] • Unique Co 2 N-Ni 3 N nanoarray heterostructure was successfully synthesized. • Co 2 N-Ni 3 N/NF achieves an areal capacitance 2.17 F cm-2 at current density of 1 mA cm-2. • The Co 2 N-Ni 3 N/NF // AC exhibits good electrochemical performance in two-electrode tests. [ABSTRACT FROM AUTHOR]