Search

Under natural application conditions, water in the forms of condensates and high-speed raindrops tend to form Wenzel contact with the surface of superhydrophobic coatings, and in this case, the effect of the standing water on the abrasion mechanisms of superhydrophobic coatings is not clear. To investigate the issue, comparative tests of abrasion-induced aging on the surface of the superhydrophobic coating under dry, and water infiltration conditions are conducted. A theoretical prediction model of the friction magnitude on the surface of the superhydrophobic coating under the above two conditions is established, and the experimental phenomenon is analyzed based on the theoretical results of the model. The results show that once water wets superhydrophobic surfaces in Wenzel mode, the microscopic rough structures on the surfaces are more likely to fall off under external friction due to the presence of Laplace pressure, which means that the presence of water makes the superhydrophobic surfaces more prone to abrasion-induced aging in this condition. [Display omitted] [ABSTRACT FROM AUTHOR]

Using micro-nanostructure superhydrophobic coating with the unique self-cleaning phenomenon is a feasible method to further reduce the frequency of insulator pollution flashover. However, the research on the anti-pollution flashover performance of superhydrophobic coating is still insufficient. This paper analyzes the various types of forces on the polluted particles accumulated on the superhydrophobic coating surface, and calculates that the vertical force or the horizontal force on the nano-scale and micro-scale particles is positive when they are in contact with most types of droplets. After being fully wetted, these particles are easily absorbed or pulled by the droplets and leave the coating surface. So it is necessary to establish a new DC pollution flashover mechanism model of superhydrophobic coatings surface from the electric field perspective. Based on this model, the relationship between the pollution flashover voltage and the dry flashover voltage is clarified in the state of extremely small leakage current. Furthermore, the anti-pollution flashover performance experiment was carried out on superhydrophobic coating, RTV coating, and uncoated surface to test the leakage current under different conditions. The experimental results show that at any pollution degree, the leakage current of superhydrophobic coating surface always remains about 16.3μA after being completely wetted. [Display omitted] [ABSTRACT FROM AUTHOR]

The application of the superhydrophobic coating is expected to be an effective method to further improve the pollution flashover voltage of insulators. However, so far, the relationship between electric field strength, droplet volume, and sliding angle in strong electric fields is not clear. This is not conducive to the evaluation of the practical application effect of superhydrophobic insulators. In this paper, the self-cleaning property of superhydrophobic coating and the critical motion condition of droplets in the electric field were analyzed theoretically. Then an experimental platform was set up to observe the movement of the droplet driven by the electric field, and the critical electric field strength for droplet motion was measured. Experimental and theoretical analysis results show that the critical electric field strength for positive droplet motion is less than that for the negative droplet. The droplet driven by the electric field can also remove water-insoluble pollution particles. And the maximum pollution concentration that droplets can remove by means of self-cleaning performance is calculated theoretically. The theoretical calculation method of the sliding angle of superhydrophobic coating in uniform DC electric field is obtained, which is in good agreement with the experimental results. This paper provides theoretical support for evaluating the practical performance of the superhydrophobic insulator in strong electric fields. [Display omitted] [ABSTRACT FROM AUTHOR]