Although at-home bleaching can recover the optical properties of stained CAD-CAM monolithic materials, little is known about its impact on their surface and mechanical properties, especially when successive sessions are performed. This study evaluated the effect of successive at-home bleaching sessions on the microhardness, roughness, topography, biaxial flexural strength (BFS), and reliability of CAD-CAM monolithic materials. Disks from Lava Ultimate (LU), Vita Enamic (VE), and IPS Empress CAD (EMP) were fabricated and submitted to up to three bleaching sessions. At-home bleaching was performed with 10% carbamide peroxide, and each session consisted of one application for 10 hours/day for 14 days. The analyses of the aforementioned parameters were assessed before and after the first, second, and third bleaching sessions, except for BFS, which was evaluated at baseline and after the third session. The Weibull modulus was calculated from the BFS data. The microhardness of the three materials as well as the roughness of LU were not affected by the sessions, whereas the roughness of VE and EMP increased from the second session. All materials displayed topographic changes, which became more pronounced with the increase in the number of sessions. Although bleaching decreased the BFS of the materials, it did not adversely affect their reliability. Successive at-home bleaching sessions with the protocol used in the present study cannot be considered a safe procedure for the materials evaluated., (©Operative Dentistry, 2024.)

Objectives: To assess the probability of survival of crowns made with a 3Y-TZP, a 5Y-TZP, and a lithium disilicate., Materials and Methods: CAD-CAM premolar crowns with occlusal thicknesses of 1.0 mm or 1.5 mm and cemented on a metal dye. Step-stress accelerated life testing (SSALT) was performed to access the use level probability Weibull curves and reliability were calculated for the completion of a mission of 100,000 cycles at 300 to 1200 N., Results: All ceramics showed a high probability of survival (87-99%) at 300 N, irrespective of thickness. 3Y-TZP shows no significant decrease in the probability of survival up to 1200 N (83-96%). Lithium disilicate presented lower reliability than zirconia under the 600 N mission. 5Y-TZP showed lower reliability than 3Y-TZP at 1200 N. There was no significant difference in the Weibull modulus (3.23-7.12). 3Y-TZP had the highest characteristic strength (2483-2972 N), followed by 5Y-TZP (1512-1547 N) and lithium disilicate (971-1154 N)., Conclusion: Zirconia ceramics have a high probability of survival (up to 900 N-load), while lithium disilicate survives up to 300 N load only, irrespective of the thickness (1.0 mm or 1.5 mm)., Clinical Relevance: The probability of survival of posterior crowns made with zirconia ceramics resists extreme loads while glass ceramics resist normal chewing loads. In addition, crowns with thinner occlusal face showed sufficient mechanical behavior., (© 2023. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.)