One of the most promising techniques for manufacturing low-cost solar cells is a solution processing method. In this study, it is proposed that solution-grown ZnO nanorods (NRs) are used as antireflection coatings on metal-insulator-semiconductor (MIS) solar cells with sol-gel SiO2. Except Al electrodes prepared by thermal evaporation, no other vacuum process was utilized during fabrication. The ZnO NRs were produced with a hydrothermal method and suppressed Fresnel reflection. With the solution-grown ZnO NRs, it was observed the average reflectance of the MIS solar cell decreased from 38.7% to 15.8%, and the short circuit density (JSC) increased from 5.22 mA/cm2 to 6.71 mA/cm2 (28.4% enhancement). Meanwhile, the open circuit voltage (VOC) was improved from 0.39 V to 0.47 V owing to a passivation effect. The MIS solar cell with the ZnO NRs exhibited a 35.5% efficiency enhancement compared to that without ZnO NRs. The performance improvement in MIS solar cells with ZnO NRs could be due to multiple reflections of an incident light between the vertically arranged NRs, and then light coupling into the cell. The results show a potential application of ZnO NRs for the performance enhancement of MIS solar cells.

An Al2O3 thin film is deposited on the interdigitated electrodes to fabricate a resistive hydrogen sensor. In addition, the Pd nanoparticles (NPs)/Pd film by vacuum thermal evaporation system on the Al2O3 film acts as catalytic metals for hydrogen detection. Due to the Pd NPs with an increased surface area to volume ratio as well as the spill-over effect, the catalytic activity could be improved to enhance the gas sensing performance. The experimental results showed that the sensing response ratio is 14.4% in 1000 ppm H2/air at 300 °C, which is suitable for high-temperature hydrogen detection. The studied Pd NPs/Pd/Al2O3 resistive sensor exhibits the advantages of in high-temperature operation, simple structure, easy fabrication process, and relatively low cost.