Search

The durability of concrete has a profound impact on the service life of structural elements. Indonesia has extensive peat soils, which provide a highly aggressive environment for concrete structures. Geopolymer concrete has demonstrated good durability when exposed to acid /sulphate conditions similar to those encountered in peat soils. This paper investigates the performance of geopolymer concretes produced using Indonesian type F fly ash under sulphate and acid chemical attack. Geopolymer concrete specimens have been exposed for 12-months in a range of solutions: 5% sodium sulphate, 5% magnesium sulphate, 1% and 3% sulphuric acid, and simulated peat solution. The mechanical and durability properties of specimens together with a control concrete have been monitored for compressive strength, change in mass, water absorption and volume of permeable voids, ultra pulse velocity, air and water permeability, pH profile, and microstructural analysis (XRD, SEM/EDS). The control immersed in water achieved 56.93 MPa at 12-months of age. Magnesium sulphate exposure had a significant deterioration impact on the compressive strength of geopolymer concrete, demonstrating an 11% reduction in strength, while those exposed to sodium sulphate had an 8.9% increase in strength. Specimens exposed to peat solution displayed a slightly increased strength and those in acid conditions a 1.2% and 4.5% decrease in 1% acid and 3% acid, respectively. In general, the geopolymer concrete displayed a high level of resistance against sodium sulphate, 1% sulphuric acid and simulated peat attack.

In this study, carpet waste fibers--namely, polypropylene (PP) and polytrimethylene terephthalate (PTT) in the form of mono microfibers and hybrid combinations--were studied. The optimization of mono fiber parameters for fiber content (0.1, 0.3, and 0.5%) and length (6, 12, and 24 mm [0.236, 0.742, and 0.945 in.]) were conducted to achieve the optimum strength properties and minimize drying shrinkage. The microstructure, pore structure, and fiber-matrix interfacial properties of the optimized samples were characterized at 7, 28, and 90 days by means of scanning electron microscopy (SEM), X-ray micro-computed tomography (CT), and nanoindentation. The research data revealed that the inclusion of either the optimized mono PP fiber (υf = 0.5% and l = 12 mm [0.472 in.]) or PTT fiber (υf = 0.1% and l = 12 mm [0.472 in.]) improved the compressive strength of 4.3% and 16.1%, and the flexural strength by 11.5% and 9.2% at 28 days, respectively. Hybrid carpet fibers (0.4% PP + 0.1% PTT) provided a greater enhancement in compressive strength of 6.6%, and flexural strength by 13% at 28 days. Drying shrinkage mitigation of mortar over 120 days was recorded as 18.4, 22.3, and 25.8%, corresponding to the addition of 0.5% PP fibers, 0.1% PTT fibers, and hybrid PP/PTT carpet fibers. A pore-refining effect was also observed for mortars with 0.5% PP and hybrid PP/PTT carpet microfibers. The SEM images indicated that the trilobal cross-sectional shape of PTT carpet fibers had a stronger anchoring effect with cement hydrates than the rounded shape of PP carpet fibers. Nanoindentation identified the thickness of the fiber-matrix interfacial transition zone (ITZ) as approximately 15 µm (5.9 × 10-4 in.) for both mono PP and PTT fibers. Approximately 50% of the phases in the vicinity of the fiber-matrix interface comprised a porous structure at 7 days. However, the hydration of clinker over the 90-day period promoted the formation of calcium-silicate-hydrate (C-S-H) and portlandite to form a dense microstructure. [ABSTRACT FROM AUTHOR]

The long-term creep and shrinkage behaviour of two High-Volume Fly Ash (HVFA) concretes incorporating nano silica with 65% and 80% replacement of cement has been investigated. This comprised a detailed analysis of the microstructure, pore structure and chemistry of the two HVFA systems up to a period of 450 days. The compressive strength and modulus of elasticity of HVFA-65 concrete increased from 32 to 73 MPa and 30.3 to 40.5 GPa, respectively between 7 and 450 days. The HVFA-80 concrete achieved compressive strength values of 22 and 71 MPa and elastic modulus values of 28.9 and 37 GPa. After a total loading period of 450 days, HVFA-65 and HVFA-80 concretes displayed creep parameters, which were significantly below the values predicted by AS 3600, ACI 209 and CEB-FIP standard model equations. After a total drying period of 450 days 28-day cured specimens showed significantly reduced shrinkage compared to 7-day cured specimens. On the other hand, HVFA-80 concrete displayed higher shrinkage compared to the HVFA-65 specimens throughout the period. All specimens except for 7-day cured HVFA-80 concrete were within the maximum permissible shrinkage of 800 microns recommended for Australian construction practices. HVFA-65 concrete showed a denser microstructure and a stronger, better packed interfacial transition zone (ITZ) compared to HVFA-80 at all ages. The XRD and FTIR analysis data identified the formation of hydration products including C-S-H and C-A-S-H which contributed towards both the strength gain as well as the creep and shrinkage properties displayed by the HVFA concrete by minimizing the total porosity and pore size. [ABSTRACT FROM AUTHOR]

The corrosion of steel due to chloride ingress is one of the major causes of deterioration of reinforced concrete structures. In order to ensure a structure achieves the design life specified, predictive modelling is employed. To undertake this modelling, details are required on a number of variables; however, each of these variables has a level of uncertainty which can affect the reliability of the model. To address these issues, this paper reports the analysis of data taken from four distinct elements on a port structure, in Australia, constructed in three phases between 1926 and 1985, using both pre-cast and cast in situ techniques. The cover depth, surface chloride concentration and chloride diffusion coefficient were determined for different elements on the structure, with a total of 244 data points obtained. The data was analysed to identify the statistical distributions and probability density functions produced. A novel analytical model was developed based on the solutions to Fick's equation. The results showed that both surface chloride and the diffusion coefficient were positively skewed with no significant variation in the sensitivity. It was also found that controlling the diffusion coefficient has a more influential effect than increasing the cover. [ABSTRACT FROM AUTHOR]

The deposition of textile waste into landfill has reached an unsustainable level and raises serious environmental issues across the world. Transforming textile waste into fiber reinforcement in cementitious composites offers a sustainable resolution toward a circular textile economy. This article presents a comprehensive review of environmental concerns, recycling routes for textile waste, together with an in-depth review of the engineering properties of concrete incorporating recycled textiles. In general, the incorporation of these recycled fibers from textile waste enhances strain capacity, crack control, durability, and energy absorption of concrete via dual effects: bridging action (direct mechanism) and refinement of pore distribution (indirect effect). An improvement in compressive strength can be achieved by the utilization of a small dosage of recycled fibers or recycled fiber fabrics in concrete (strength < 40 MPa). Finally, the cost and environmental benefits for eco-efficient building application are also evaluated to draw the attention of researchers toward these potentially recyclable waste materials. [ABSTRACT FROM AUTHOR]

This article reports the results of an investigation into the efficiency of mechanical activation to increase the reactivity in alkali activated mortar synthesized from low-grade clay. Mechanical activation significantly changed the structure of clay, increasing the specific surface area, and decreasing the particle size. The 7-day compressive strength of mortar synthesized from untreated clay was 31.7 MPa, which increased to 35.3 after 4 h milling. A further increase of grinding time to 8 h did not result in any increase in compressive strength which is attributed to a decrease in the workability. However, the extent of reactivity did significantly increase as determined from solid-state MAS NMR, FTIR, and EDS analyses. Solid-state MAS NMR results revealed the increased formation of Q4(2Al) silicon sites, which is correlated with improved reaction. Furthermore, the EDS and FTIR analysis results indicated greater incorporation of aluminium into the matrix structure with increased grinding time. [ABSTRACT FROM AUTHOR]