Search

Photocatalysis is a new type of renewable energy technology used in environmental treatment and hydrogen energy production. In this regard, a new class of photocatalysts, TiO2 aerogels, are attractive for having the chemical characteristics of TiO2 nanomaterials such as high catalytic activity, good stability, non-toxic, and non-polluting, and the structural characteristics of aerogels such as large specific surface area, high porosity, the 3-dimensional interconnected network structure composed of relatively uniform nanoparticles, and high light transmittance. Here we review the recent progress in TiO2 aerogels for photocatalysis, focusing on preparation techniques, the crystalline phases’ influence on photocatalytic properties, the modification of photocatalytic properties, and the analysis and discussion of future development. In particular, we first summarize various preparation techniques, including sol–gel method, nanoparticles self-assembly synthesis, and high-temperature aerosol technique, then detail the structure and composition of TiO2 crystalline phases that affect the photocatalytic properties. Subsequently, we discuss strategies to further enhance the photocatalytic properties of TiO2 aerogels by the composite of SiO2 aerogel semiconductors, the doping of metal dopants, and the doping or composite of non-metallic substances, and elaborate the modification mechanism and the modification effect achieved. Finally, combined with the research status of TiO2 aerogels and the development experience of other aerogels, we conduct a reasonable analysis and discussion on their further research directions and industrialization roads.

Conventional SiO2 aerogels composed of 0-dimensional nanoparticles do not have large-scale compression, tensile, and shear deformation capabilities, and the poor mechanical properties hinder their further development and application. We report a scalable strategy to construct the nanoporous network of a SiO2 aerogel by alternately linking octa-(aminophenyl)-T8-POSS and hexaphthalic acid. The resulting SiO2 aerogel exhibits high strengths (compression, tensile and shear strengths are 26.4, 9.16, and 8.31 MPa, respectively), excellent deformabilities (fracture compression, tensile, and shear strains are 82.63%, 57.81% and 108.02%, respectively), flexbile processability and good structural stability (only 1.7% plastic deformation occurs after 100 load–unload cycles at a large compression strain of 70%). Also, the mesoporous interconnected nanoskeleton with high porosity and the composition of fully hydrophobic groups also give the aerogel low thermal conductivities (0.02854 W/(m K) at 25 °C and 0.04638 W/(m K) at 300 °C) and superhydrophobic properties (hydrophobic angle 160° and saturated mass moisture absorption rate about 0.375%). The combination of these excellent properties ensures that the aerogel can be used as an efficient thermal insulation material for extreme environments, such as those where comprehensive mechanical and hydrophobic properties are strictly required. [ABSTRACT FROM AUTHOR]

Transparent conductive oxide (TCO) film acts as the window layer and carrier transport layer of silicon heterojunction (SHJ) solar cells. The optoelectrical and contact properties of TCO films, as well as the sputtering damage, limit the further efficiency improvement. Herein, the microstructure, morphology, and optoelectrical properties of sputtering‐prepared zinc‐doped indium oxide (IZO) are analyzed. The substrate temperature has a significant impact on the film growth and the cell performance. The IZO film is amorphous when substrate temperature is below 200 °C, while it seems the emergence of nanocrystals with the increased temperature, resulting in the highest conductivity (3070 S cm−1) and carrier mobility (47.9 cm2 V−1 s−1). In addition, the low carrier concentration and surface potential of IZO promote less optical parasitic absorption and higher work function. The IZO films are applied as the contact layer of SHJ solar cells. An impressive efficiency of 24.02% on an M2‐sized wafer is achieved, indicating great potential for the mass production application after careful optimization. [ABSTRACT FROM AUTHOR]

Spinel Li4Mn5O12 was successfully prepared by the wet chemical method to modify the surface of Li1.2Ni0.2Mn0.6O2. The results showed that an ultrathin spinel Li4Mn5O12 surface-modified layer with a thickness of approximately 10 nm was successfully constructed on the raw material surface, and that the cationic order was improved. In addition, the lithium ion diffusion coefficients (DLi+) of the raw materials and the modified materials were calculated using the EIS test and impedance fitting. The results indicated that the ultrathin Li4Mn5O12 surface modification shell can increase the lithium ion diffusion rate of the material and improve the rate capability of the material. So, the surface modification layer of spinel Li4Mn5O12 can reduce the oxygen loss of the first cycle and improve the cationic order of the material. Therefore, the first coulombic efficiency of Li4Mn5O12/Li1.2Ni0.2Mn0.6O2 material at the current density of 12.5 mA·g−1 reaches 80.46%, and the capacity retention rate reaches 91.74% after 50 cycles, which are 3.36% and 21.23% higher than those of the raw materials, respectively. It showed better electrochemical reversibility and cyclic stability. This study provides a straightforward and convenient modification method for improving the stability of cobalt-free lithium-rich manganese cathode materials and has a favorable application prospect. [ABSTRACT FROM AUTHOR]