Search

In this study, we investigate the changes in the crystalline structure of MBE-deposited SrTiO3 layers on Si with different deviations from Sr/Ti stoichiometry as deposited but also after annealing at high temperatures (>600 °C). We show that as-grown 15 nm thick non-stochiometric SrTiO3 layers present surprisingly lower FWHM values of the (002) omega diffraction peak compared to fully stoichiometric layers of similar thickness. This can misleadingly point to superior crystalline quality of such non-stochiometric layers. However, thermal post-deposition anneals of these layers at temperatures up to 850 °C in oxygen show strong detrimental effects on the crystalline structure, surface and interface with the Si (001) substrate. On the contrary, the post-deposition anneals applied to the stoichiometric samples strongly improve the physical, optical and electrical properties of the epitaxial SrTiO3 thin films. [ABSTRACT FROM AUTHOR]

We investigate differential evolution optimization to fit Rutherford backscattering data. The algorithm helps to find, with very high precision, the sample composition profile that best fits the experimental spectra. The capabilities of the algorithm are first demonstrated with the analysis of synthetic Rutherford backscattering spectra. The use of synthetic spectra highlights the achievable precision, through which it becomes possible to differentiate between the counting statistical uncertainty of the spectra and the fitting error. Finally, the capability of the algorithm to analyze large sets of experimental spectra is demonstrated with the analysis of the position-dependent composition of a Sr x Ti y O z layer on a 200 mm silicon wafer. It is shown that the counting statistical uncertainty as well as the fitting error can be determined, and the reported total analysis uncertainty must cover both. [ABSTRACT FROM AUTHOR]

We report the synthesis and characterization of high-quality thin films of the topological semimetal (Bi2)5(Bi2Se3)7. Cryogenic magnetotransport experiments reveal strong metallic character and spin--orbit coupling in the films. By studying the temperature dependence of the electrical resistance of the topological semimetal, we observe a pronounced Kondo effect, which points toward the presence of magnetic scatterers. With the aid of density functional theory calculations, we identify Bi vacancies as intrinsic magnetic scatterers in this topological semimetal. [ABSTRACT FROM AUTHOR]

Herein, the carrier lifetime in ≈5 × 1016 cm−3 n‐doped InxGa1−xAs layers is studied by diode current–voltage analysis and by time‐resolved photoluminescence. Two sets of hetero‐epitaxial layers are grown on semi‐insulating InP or GaAs substrates. The first set corresponds with a constant In content p + n stack, while the second set has a fixed x = 0.53 for the n‐layer, while containing various extended defect densities by using a strain relaxed buffer with different x. This results in threading dislocation densities (TDDs) between ≈105 cm−2 and a few 109 cm−2. It is shown that the overall trend of the recombination lifetime versus TDD can be described by a first‐order model considering a finite recombination lifetime value inside a dislocation core of 1 nm. For the generation lifetime, a strong electric‐field enhancement factor is found. Also, the residual strain in the n‐layer has an impact. Overall, the safe limit for TDD depends on the type of application and on the operation conditions (reverse diode bias). [ABSTRACT FROM AUTHOR]

The growth of crystalline Li-based oxide thin films on silicon substrates is essential for the integration of next-generation solid-state lithionic and electronic devices including on-chip microbatteries, memristors, and sensors. However, growing crystalline oxides directly on silicon typically requires high temperatures and oxygen partial pressures, which leads to the formation of undesired chemical species at the interface compromising the crystal quality of the films. In this work, we employ a 2 nm gamma-alumina (γ-Al 2 O 3 ) buffer layer on Si substrates in order to grow crystalline thin films of Li 4 Ti 5 O 12 (LTO), a well-known active material for lithium-ion batteries. The ultrathin γ-Al 2 O 3 layer enables the formation of a stable heterostructure with sharp interfaces and drastically improves the LTO crystallographic and electrochemical properties. Long-term galvanostatic cycling of 50 nm LTO films in liquid-based half-cells demonstrates a high capacity retention of 91% after 5000 cycles at 100 C. Rate capability tests showcase a specific charge of 56 mA h g -1 at an exceptional C-rate of 5000 C (15 mA cm -2 ). Moreover, with sub-millisecond current pulse tests, the reported thin-film heterostructure exhibits rapid Li-ion (de)intercalation, which could lead to fast switching timescales in resistive memory devices and electrochemical transistors.