Search

Cost-effective and controllable synthesis of M0.25Ni0.15Cu0.25Co0.35Fe2O4 (M2+ = Mg2+, Mn2+, and Cd2+) ferrites via the sol–gel auto-combustion technique. The impact of divalent cations on the structural, dielectric, and optoelectrical properties of ferrites was examined by XRD, FTIR, Raman, LCR, UV–Vis, and two probe I-V measurement techniques. The crystallite size was 52.66 nm, and the minimum specific surface area was observed 5.1507 m2/g for Mg2+ doped NCCF ferrite. The FTIR and Raman analysis also confirmed the substitution of divalent cations (M2+ = Mg2+, Mn2+, and Cd2+) at their respective lattice sites. The maximum energy bandgap was 1.67 eV Mg2+-doped NCCF ferrite as compared to other divalent ion-doped ferrites. The dielectric loss decreased while the ac conductivity increased with increasing frequency, and the minimum values were observed for Mg2+-doped NCCF ferrite. The activation energy was observed maximum for Mg2+-doped NCCF ferrite (0.2234 eV). Due to incredible properties including small specific surface area, large energy band gap, high resistivity, and loss dielectric loss of Mg2+-doped NCCF ferrite have potential applications in different fields. [ABSTRACT FROM AUTHOR]

Cadmium ferrites belong to normal spinel ferrites, and they exhibit interesting electrical, magnetic, and optical properties. The pure and cerium-doped cadmium ferrites CdFe2−xCexO4 (x = 0.0, 0.125, 0.250, 0.375, 0.5) were synthesized by a chemical co-precipitating technique using sodium hydroxide as a co-precipitating agent. The structures and phase purity of fabricated nanomaterials were analyzed by X-ray diffraction (XRD). The crystallite size for all the prepared nanomaterials was in the range of 28–46 nm. The lattice constant and unit cell volume were found to decrease with the increasing concentration of Cerium, which was confirmed by the peak shift in the XRD pattern. The X-ray density for all nano ferrites increased with the enhancement of cerium composition. The resistivity of the nanomaterials has random behavior with the enhancement of cerium composition for a temperature, but the value of resistivity at x = 0.125 has the lowest value and at x = 0.375 has the highest value for almost all temperatures. For specific concentrations, a decreasing trend of resistivity of fabricated materials was found with an increment of temperature. The activation energies were also calculated, and it increased for x = 0.125 and then decreased for all the nanomaterials. For the confirmation of the M–O bonds, FTIR analysis of all the nano ferrites was also performed. The analysis shows a higher frequency absorption band in the range of 531.24–534.84 cm−1. This absorption band confirms that metal oxides are formed in all the synthesized nanoparticles. [ABSTRACT FROM AUTHOR]

The Nickel substituted Cu-Co-Zn-Ce nano ferrites, Zn0.15Co0.45Cu0.40-xNix Fe1.85Ce0.15O4 with x=0, 0.1, 0.20, 0.30, 0.40, were synthesized using the coprecipitation technique. The sample were sintered at 900 °C for 5h. The structural, electrical, dielectric and magnetic properties of all the prepared samples were characterized by XRD, SMU2401, UV-Vis and FTIR. The powder X-ray diffraction patterns of all the prepared samples confirmed the formation of single-phase cubic spinel structures. These samples further characterized for the electrical properties by using two-probe type method. The DC resistivity of all the ferrite composition decreased as the temperature increased, showing their semiconductor nature. UV-Vis and FTIR confirmed the substitution of nickel in Cu-Co-Zn-Ce ferrites. From UV-Vis it is observed that the optical band gap changes from 3.9 eV to 5.3 eV with addition of Ni. FTIR analysis revealed that a strong variation on tetrahedral absorption frequency band is present which is due to the replacement of Ni on Cu. All these results suggested that these materials can be used for wastewater treatment. [ABSTRACT FROM AUTHOR]

Cadmium ferrites belong to normal spinel ferrites, and they exhibit interesting electrical, magnetic, and optical properties. The pure and cerium-doped cadmium ferrites CdFe2−xCexO4 (x = 0.0, 0.125, 0.250, 0.375, 0.5) were synthesized by a chemical co-precipitating technique using sodium hydroxide as a co-precipitating agent. The structures and phase purity of fabricated nanomaterials were analyzed by X-ray diffraction (XRD). The crystallite size for all the prepared nanomaterials was in the range of 28–46 nm. The lattice constant and unit cell volume were found to decrease with the increasing concentration of Cerium, which was confirmed by the peak shift in the XRD pattern. The X-ray density for all nano ferrites increased with the enhancement of cerium composition. The resistivity of the nanomaterials has random behavior with the enhancement of cerium composition for a temperature, but the value of resistivity at x = 0.125 has the lowest value and at x = 0.375 has the highest value for almost all temperatures. For specific concentrations, a decreasing trend of resistivity of fabricated materials was found with an increment of temperature. The activation energies were also calculated, and it increased for x = 0.125 and then decreased for all the nanomaterials. For the confirmation of the M–O bonds, FTIR analysis of all the nano ferrites was also performed. The analysis shows a higher frequency absorption band in the range of 531.24–534.84 cm−1. This absorption band confirms that metal oxides are formed in all the synthesized nanoparticles. [ABSTRACT FROM AUTHOR]