Search

The use of polycondensation urea-formaldehyde (UF) resins in the woodworking and furniture industries is widespread due to their relatively low price, high reactivity, availability of raw materials, and ease of use. After curing, they provide a transparent, brittle joint, but their main disadvantage is the continuous emission of formaldehyde. The naturally occurring biopolymer keratin and the amino acid cysteine prepared from sheep wool were chosen and tested as possible agents for UF adhesives, allowing the reduction of formaldehyde emissions from wood-based panels. Emissions of formaldehyde were determined in accordance with EN ISO 12460-4. The gluing quality was tested according to standard EN 314-1, and the tested plywood met the requirements of standard EN 314-2. The most significant decrease in formaldehyde emission by up to 44.0% was achieved by applying 1% MOD-I (pre-condensate of glutaraldehyde and urea + cysteine) to the reference UF adhesive. Therefore, samples prepared for this study have great potential for application as environmentally friendly formaldehyde scavengers. [ABSTRACT FROM AUTHOR]

Industrially important properties of wood can be changed due to the modification of birch wood (Betula pendula L.) after the process of thermal treatment with saturated water steam. The birch wood was modified by saturated water steam at 125 ± 2.5 °C for 8 hours and at a pressure of 0.18 MPa. The water contact angle of steam-treated birch wood increased from 42.1° (for untreated birch wood) to 52.4° (for steam-treated birch wood), and the stability of water drop on steam-treated birch wood surface increased. FTIR spectra showed an increase in C=O and glycoside bonds concentration on the surface of steam-treated birch wood, but the concentration of C-O-C groups decreased. XPS measurements confirmed that the concentration of oxygen as well as C=O and C-O-O groups on the surface of steamtreated birch wood showed an increment in comparison with the native wood sample. SEM micro photos confirmed the minor changes of birch wood cells due to the action of saturated water steam modification. [ABSTRACT FROM AUTHOR]

Poly(lactide) (PLA) films obtained by thermoforming or solution-casting were modified by diffuse coplanar surface barrier discharge plasma (300 W and 60 s). PLA films were used as hot-melt adhesive in joints in oak wood. It was demonstrated that lap shear strength increased from 3.4 to 8.2 MPa, respectively, for the untreated and plasma-treated series. Pull-off tests performed on particleboard for the untreated and treated PLA films showed 100% cohesive failure. Pull-off strength tests on solid oak demonstrated adhesion enhancement from 3.3 MPa with the adhesion failure mode to 6.6 MPa with the cohesion failure mode for untreated and treated PLA. XPS revealed that carbonyl oxygen content increased by two-to-three-fold, which was confirmed in the Fourier-transform infrared spectroscopy experiments of the treated PLA. The water contact angle decreased from 66.4° for the pristine PLA to 49.8° after treatment. Subsequently, the surface free energy increased from 47.9 to 61.05 mJ/m2. Thus, it was clearly proven that discharge air plasma can be an efficient tool to change surface properties and to strengthen adhesive interactions between PLA and woody substrates. [ABSTRACT FROM AUTHOR]