Search

The exterior application of fire-retardant (FR) timber necessitates it to have high durability because of the possibility to be exposed to rainfall. In this study, water-leaching resistance of FR wood has been imparted by grafting phosphate and carbamate groups of the water-soluble FR additives ammonium dihydrogen phosphate (ADP)/urea onto the hydroxyl groups of wood polymers via vacuum-pressure impregnation, followed by drying/heating in hot air. A darker and more reddish wood surface was observed after the modification. Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, solid-state 13C cross-polarization magic-angle-spinning nuclear magnetic resonance (13C CP-MAS NMR), and direct-excitation 31P MAS NMR suggested the formation of C–O–P covalent bonds and urethane chemical bridges. Scanning electron microscopy/energy-dispersive X-ray spectrometry suggested the diffusion of ADP/urea into the cell wall. The gas evolution analyzed by thermogravimetric analysis coupled with quadrupole mass spectrometry revealed a potential grafting reaction mechanism starting with the thermal decomposition of urea. Thermal behavior showed that the FR-modified wood lowered the main decomposition temperature and promoted the formation of char residues at elevated temperatures. The FR activity was preserved even after an extensive water-leaching test, confirmed by the limiting oxygen index (LOI) and cone calorimetry. The reduction of fire hazards was achieved through the increase of the LOI to above 80%, reduction of 30% of the peak heat release rate (pHRR2), reduction of smoke production, and a longer ignition time. The modulus of elasticity of FR-modified wood increased by 40% without significantly decreasing the modulus of rupture. Validerad;2023;Nivå 2;2023-04-21 (joosat);Funder: OP RDE (Grant no.CZ.02.1.01/0.0/0.0/16_019/0000803); CT WOOD, Luleå University of TechnologyLicens fulltext: CC BY License

Chemical modification of wood typically requires the impregnation of wood with reactive compounds capable of undergoing covalent bonding to functional groups present in the cell wall. Creating such reactive agents in situ, with the use of low-priced chemicals, would prove more attractive for commercial applications. In this study, Scots pine (Pinus sylvestris L.) sapwood was impregnated with an aqueous solution of urea (30%), dried at 40°C for 24 h, and subsequently heat treated in an oven at 150°C for 24 h to produce the reactive isocyanic acid. By using accelerated fungal tests under laboratory conditions, provisional tests demonstrated a high biological resistance against selected moulds and rots. Migration of urea into the wood structure and grafting to its polymers during subsequent heat treatment, led to a bulked cell wall and enhanced resistance to water swelling, even after cycling water treatments. The bending strength (MOR) of modified pine wood was reduced by the treatment applied, while its modulus of elasticity (MOE) remained unchanged. Validerad;2023;Nivå 2;2023-06-30 (joosat);Licens fulltext: CC BY-NC-ND License Biobased fire protection of wood panel for exterior conditions by using phosphorylated lignin from wheat straw

Fire-retardant (FR) treated wood-based panels, used commonly in furniture and construction, need to meet stringent fire safety regulations. This study presents a novel treatment for imparting fire resistance to wood composites by applying separate solutions of phytic acid and sodium silicate onto wood particles before the hot pressing at 160 °C. A scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDX) analysis revealed that phytic acid and sodium silicate were uniformly distributed throughout the wood particles, and the formation of silica gel resulted in the aggregation of elemental silicon. Fourier-transform infrared spectroscopy (FTIR) displayed that phytic acid caused the thermal degradation of hemicelluloses, which led to a brownish outer appearance of the FR-treated composites. Fire performance was assessed using both limiting oxygen index (LOI) and a cone calorimeter. These techniques showed a higher LOI value and a significant reduction in heat-release rate (HRR), total heat release (THR), smoke-production rate (SPR), and total smoke production (TSP). In addition, cone calorimeter and thermogravimetric (TGA) analyses consistently showed increased char residue in treated wood composites. Moreover, internal bond strength (IB) and modulus of elasticity (MOE) of the wood composite were not significantly changed compared with those of the untreated composite. Surprisingly, in the FR-treated composite, the 24 h-thickness swelling, and the water uptake were slightly decreased. Consequently, this new treatment has the potential to increase the fire retardancy of wood composites, such as particleboard, without deteriorating the key mechanical properties. Validerad;2023;Nivå 2;2023-05-22 (hanlid);Funder: Slovak Research and Development Agency (APVV-16-0223); VEGA agency (VEGA 1/0678/22); KEGA agency (KEGA 016STU4/2021); Swedish wood industry; OP RDE (CZ.02.1.01/0.0/0.0/16_019/0000803) Biobased fire protection of wood panel for exterior conditions by using phosphorylated lignin from wheat straw Advanced research supporting the forestry and woodprocessing sector’s adaptation to global change and the 4th industrial revolution

Wood composites are manufactured by joining wood fibres, strands, or particles together with an adhesive, but it is necessary for eliminate the use of formaldehyde-based adhesives in the manufacture of wood composites for the sake of indoor air quality and human health. This initial study has demonstrated the use of sorbitol and citric acid as a potential bio-based formaldehyde-free adhesive for wood-composite manufacture. A solution of citric acid and sorbitol in water was sprayed onto wood particles which were then pressed at 160°C, 180°C, or 200°C for 13 min, to produce boards with a target thickness of 8 mm. The FTIR spectra contained an absorption band at 1720cm−1, presumably due to the esters of citric acid and sorbitol. Pressing of a temperature of 200°C gave boards with the highest modulus of elasticity and the highest internal bond strength. The results reveal a new potential bio-adhesive for the manufacture of wood composites. Validerad;2022;Nivå 2;2022-11-25 (hanlid);Funder: OP RDE (CZ.02.1.01/0.0/0.0/16_019/0000803); Swedish wood industry CT WOOD

Brown discolouration caused by resin exudation from knots is a problem for a range of light-coloured painted pines, and will negatively affect the appearance of the finish. To solve this problem, a hot-and-cold bath impregnation process of wood prior to painting was tested. Sawn timber, 18 × 120 mm in cross-section dimension, were heated in an oven and then immediately immersed in a cold liquid containing a phenol-formaldehyde-based solution, filling a 1–5 mm thick layer beneath the surface with phenol-formaldehyde. After curing, the timbers were painted with a white coloured coating system intended for exterior use, and tested in artificial weathering test (QUV). The phenol-formaldehyde treatment greatly reduced the discolouration of the coating compared to non-impregnated wood. Validerad;2022;Nivå 2;2022-04-13 (sofila);Funder: CT WOOD; OP RDE (CZ.02.1.01/0.0/0.0/16_019/0000803)

Guanyl-urea phosphate (GUP) was introduced into furfurylated wood in order to improve fire retardancy. Modified wood was produced via vacuum-pressure impregnation of the GUP–furfuryl alcohol (FA) aqueous solution, which was then polymerized at elevated temperature. The water leaching resistance of the treated wood was tested according to European standard EN 84, while the leached water was analyzed using ultra-performance liquid chromatography (UPLC) and inductively coupled plasma–sector field mass spectrometry (ICP-SFMS). This new type of furfurylated wood was further characterized in the laboratory by evaluating its morphology and elemental composition using optical microscopy and electron microscopy coupled with energy-dispersive X-ray spectrometry (SEM-EDX). The chemical functionality was detected using infrared spectroscopy (FTIR), and the fire resistance was tested using cone calorimetry. The dimensional stability was evaluated in wet–dry soaking cycle tests, along with the mechanical properties, such as the Brinell hardness and bending strength. The fire retardancy of the modified furfurylated wood indicated that the flammability of wood can be depressed to some extent by introducing GUP. This was reflected in an observed reduction in heat release rate (HRR2) from 454.8 to 264.9 kW/m2, without a reduction in the material properties. In addition, this leaching-resistant furfurylated wood exhibited higher fire retardancy compared to conventional furfurylated wood. A potential method for producing fire-retardant treated furfurylated wood stable to water exposure has been suggested.

Guanyl-urea phosphate (GUP) was introduced into furfurylated wood in order to improve fire retardancy. Modified wood was produced via vacuum-pressure impregnation of the GUP-furfuryl alcohol (FA) aqueous solution, which was then polymerized at elevated temperature. The water leaching resistance of the treated wood was tested according to European standard EN 84, while the leached water was analyzed using ultra-performance liquid chromatography (UPLC) and inductively coupled plasma-sector field mass spectrometry (ICP-SFMS). This new type of furfurylated wood was further characterized in the laboratory by evaluating its morphology and elemental composition using optical microscopy and electron microscopy coupled with energy-dispersive X-ray spectrometry (SEM-EDX). The chemical functionality was detected using infrared spectroscopy (FTIR), and the fire resistance was tested using cone calorimetry. The dimensional stability was evaluated in wet-dry soaking cycle tests, along with the mechanical properties, such as the Brinell hardness and bending strength. The fire retardancy of the modified furfurylated wood indicated that the flammability of wood can be depressed to some extent by introducing GUP. This was reflected in an observed reduction in heat release rate (HRR