Search

A series of cross‐linked AEMs (c‐DQPPO/PVA) are synthesized by using rigid polyphenylene oxide and flexible poly(vinyl alcohol) as the backbones. Dual cations are grafted on the PPO backbone to improve the ion exchange capacity (IEC), while glutaraldehyde is introduced to enhance compatibility and reduce swelling ratio of AEMs. In addition to the enhanced mechanical properties resulting from the rigid‐flexible cross‐linked network, c‐DQPPO/PVA AEMs also exhibit impressive ionic conductivity, which can be attributed to their high IEC, good hydrophilicity of PVA, and well‐defined micro‐morphology. Additionally, due to confined dimension behavior and ordered micro‐morphology, c‐DQPPO/PVA AEMs demonstrate excellent chemical stability. Specifically, c‐DQPPO/PVA‐7.5 exhibits a wet‐state tensile strength of 12.5 MPa and an elongation at break of 53.0 % at 25 °C. Its OH− conductivity and swelling degree at 80 °C are measured to be 125.7 mS cm−1 and 8.2 %, respectively, with an IEC of 3.05 mmol g−1. After 30 days in a 1 M NaOH solution at 80 °C, c‐DQPPO/PVA‐7.5 experiences degradation rates of 12.8 % for tensile strength, 27.4 % for elongation at break, 14.7 % for IEC, and 19.2 % for ion conductivity. With its excellent properties, c‐DQPPO/PVA‐7.5 exhibits a peak power density of 0.751 W cm−2 at 60 °C in an H2‐O2 fuel cell. [ABSTRACT FROM AUTHOR]

AuCo alloys were prepared by magnetron sputtering for the first time without considering the insolubility on the phase diagram. The electronic effect between Au and Co can change the oxygen adsorption energy and the ORR activity. The ORR activity of the Au46Co54 alloy electrode not only exceeded that of Au, but also exceeded that of Pt in basic solution. [ABSTRACT FROM AUTHOR]

Nano-network Ru with definite lattice defects on amorphous Co nanosheets is obtained for the first time. Amorphous Co support can promote the surface Ru to obtain special morphology and modified electronic structure, thus improving HER activity in alkaline solution. A current density of 10 mA cm−2 can be obtained only with an overpotential of 33.5 mV. [ABSTRACT FROM AUTHOR]

A series of cross-linked AEMs (c-DQPPO/PVA) are synthesized by using rigid polyphenylene oxide and flexible poly(vinyl alcohol) as the backbones. Dual cations are grafted on the PPO backbone to improve the ion exchange capacity (IEC), while glutaraldehyde is introduced to enhance compatibility and reduce swelling ratio of AEMs. In addition to the enhanced mechanical properties resulting from the rigid-flexible cross-linked network, c-DQPPO/PVA AEMs also exhibit impressive ionic conductivity, which can be attributed to their high IEC, good hydrophilicity of PVA, and well-defined micro-morphology. Additionally, due to confined dimension behavior and ordered micro-morphology, c-DQPPO/PVA AEMs demonstrate excellent chemical stability. Specifically, c-DQPPO/PVA-7.5 exhibits a wet-state tensile strength of 12.5 MPa and an elongation at break of 53.0 % at 25 °C. Its OH - conductivity and swelling degree at 80 °C are measured to be 125.7 mS cm -1 and 8.2 %, respectively, with an IEC of 3.05 mmol g -1 . After 30 days in a 1 M NaOH solution at 80 °C, c-DQPPO/PVA-7.5 experiences degradation rates of 12.8 % for tensile strength, 27.4 % for elongation at break, 14.7 % for IEC, and 19.2 % for ion conductivity. With its excellent properties, c-DQPPO/PVA-7.5 exhibits a peak power density of 0.751 W cm -2 at 60 °C in an H 2 -O 2 fuel cell., (© 2023 Wiley-VCH GmbH.)

The food hygiene problems caused by bacterial biofilms in food processing equipment are directly related to human life safety and health. Therefore, it is of great strategic significance to study new food sterilization technology. An acidic electrolyzed water (AEW) disinfectant is an electrochemical sterilization technology which has the characteristics of wide adaptability, high efficiency, and environmental friendliness. However, since the sterilization efficiency of AEW for biofilms is not ideal, it is necessary to increase the available chlorine content (ACC) in AEW. A feasible method to increase the ACC is by increasing the chlorine evolution reaction (CER) selectivity of the electrode for AEW preparation. In this paper, the RuO 2 @TiO 2 electrode was prepared by thermal decomposition combined with high-vacuum magnetron sputtering. Compared with the oxygen evolution reaction (OER) activity of an ordinary RuO 2 electrode, the OER activity of the RuO 2 @TiO 2 electrode is significantly reduced. However, the CER activity of the RuO 2 @TiO 2 electrode is close to the OER activity of RuO 2 . The CER mechanism of the RuO 2 @TiO 2 electrode is the second electron transfer, and the OER mechanism is the formation and transformation of OH ads . The potential difference between the CER and OER of the RuO 2 @TiO 2 electrode is 174 mV, which is 65 mV higher than that of the RuO 2 electrode, so the selectivity of the CER of the RuO 2 @TiO 2 electrode is remarkably improved. During the preparation of AEW, the ACC obtained with the RuO 2 @TiO 2 electrode is 1.7 times that obtained with the RuO 2 electrode. In the sterilization experiments on Escherichia coli and Bacillus subtilis biofilms, the logarithmic killing values of AEW prepared the by RuO 2 @TiO 2 electrode are higher than those of AEW prepared by the RuO 2 electrode., Competing Interests: The authors declare no competing financial interest., (© 2022 The Authors. Published by American Chemical Society.)

A nano Ir x Mn (1- x ) O y hybrid electrode with a L1 2 -IrMn 3 phase was used as a bifunctional catalyst with ultra-low iridium loading for overall water electrolysis in an acid solution for the first time. The HER activity of the Ir x Mn (1- x ) O y hybrid electrode not only exceeded that of IrO 2 , but also exceeded that of Pt/C. The OER activity of the Ir x Mn (1- x ) O y hybrid electrode also exceeded that of IrO 2 .