Search

This study aimed to obtain and characterize a mortar with perlite aggregate and thermal-treated materials that could substitute for Portland cement. First, the thermally treated materials were obtained by calcinating old Portland cement (OC-tt) and concrete demolition waste (CC-tt) at 550 °C, for 3 h. Second, plastic mortars with a perlite: cement volume ratio of 3:1 were prepared and tested for water absorption, mechanical strength, and thermal conductivity. The microstructure was also analyzed. Portland cement (R) was partially substituted with 10%, 30%, and 50% OC-tt. Thermal-treated materials negatively influenced the compressive and flexural strengths at 7 and 28 days. With an increase in the substitution percentage to 50%, the decrease in the compressive strength was 40% for OC-tt and 62.5% for CC-tt. The presence of 10% OC-tt/CC-tt positively influenced the water absorption. The thermal conductivity of the tested mortars was in the range of 0.37–0.48 W/m·K. SEM analysis shows the expanded perlite pores remained unbroken. [ABSTRACT FROM AUTHOR]

The aim of the research was to prepare silica adsorbents using an environmentally friendly pathway, a template synthesis with saponin biosurfactant as a structure-directing agent. The adsorbents prepared in this way exhibit improved adsorption properties while maintaining environmental innocuousness. For the preparation of porous silica, the biosurfactant template sol–gel method was used with tetraethoxysilane as a silica precursor. The silica adsorbents were analyzed by FTIR spectroscopy, nitrogen adsorption–desorption and SEM/EDX microscopy, TEM/HRTEM microscopy, and thermogravimetric analyses. Batch tests were carried out to remediate Pb(II)/Cd(II) ions in single/binary aqueous solutions, and the effect of the surfactant on the adsorption properties was assessed. The optimal adsorption parameters (pH, contact time, initial concentration of metal ions) have been determined. The adsorption was fitted using Langmuir and Freundlich adsorption isotherms and kinetic models. Mathematical modeling of the retention process of Pb(II) and Cd(II) ions from binary solutions indicated a competitive effect of each of the two adsorbed metal ions. The experimental results demonstrated that saponin has the effect of modifying the silica structure through the formation of pores, which are involved in the retention of metal ions from aqueous solutions and wastewater. [ABSTRACT FROM AUTHOR]

Polymer nanodielectrics characterized by good flexibility, processability, low dielectric loss and high dielectric permittivity are materials of interest for wearable electronic devices and intelligent textiles, and are highly in demand in robotics. In this study, an easily scalable and environmentally friendly method was applied to obtain polysiloxane/nanosilica nanocomposites with a large content of nanofiller, of up to 30% by weight. Nanosilica was dispersed both as individual particles and as agglomerates; in nanocomposites with a lower amount of filler, the former prevailed, and at over 20 wt% nanosilica the agglomerates predominated. An improvement of both the tensile strength and modulus was observed for nanocomposites with 5–15 wt% nanosilica, and a strong increase of the storage modulus was observed with the increase of nanofiller concentration. Furthermore, an increase of the storage modulus of up to seven times was observed in the nanocomposites with 30 wt% nanosilica. The tensile modulus was well fitted by models that consider the aggregation of nanoparticles and the role of the interface. The dielectric spectra showed an increase of the real part of the complex relative permittivity with 33% for 30 wt% nanosilica in nanocomposites at a frequency of 1 KHz, whereas the loss tangent values were lower than 0.02 for all tested nanodielectrics in the radio frequency range between 1 KHz and 1 MHz. The polysiloxane–nanosilica nanocomposites developed in this work showed good flexibility; however, they also showed increased stiffness along with a stronger dielectric response than the unfilled polysiloxane, which recommends them as dielectric substrates for wearable electronic devices. [ABSTRACT FROM AUTHOR]