Search

A functional textile immobilized by microcapsules of the lime peel essential oils of C. aurantifolia (LPEO) was prepared and characterized. A varied amount of Chitosan/Alginate (CH/AG) ratios, followed by a mass of LPEO and concentration of sodium tripolyphosphate (STPP) crosslinker, was optimized sequentially to coacervate LPEO using a Tween 80 emulsifier. An antibacterial assay against both Gram-positive and Gram-negative bacteria was further evaluated for the embedded microcapsules. The LPEO (0.2 g) was effectively coacervated by CH/AG (5:3) crosslinked by 2% of STTP to give a yield, oil content (OC), and encapsulation efficiency (EE) of 53.45 ± 2.16%, 65.08 ± 2.60% and 85.04 ± 0.70% respectively. A rough spherical shape of LPEO microcapsules was homogeneously observed with an average particle size of 0.757 mm. An Avrami's kinetic model revealed the release mechanism of the core following zero-order kinetics (k = 1.11 ± 0.13 × 10−9 s−1, Ea = 70.21 kJ/mol). The LPEO microcapsules demonstrated good thermal stability up to 122 °C and maintained 38% OC at ambient temperature for four weeks. A 70.34 ± 4.16% of the LPEO microcapsules were successfully overlaid onto the gauze with citric acid binder and sodium phosphate catalyst. Overall, the immobilized microcapsules exhibited strong inhibition against S. aureus and moderate against S. epidermidis, E. coli, and K. pneumonia. [ABSTRACT FROM AUTHOR]

A functional textile immobilized by microcapsules of the lime peel essential oils of C. aurantifolia (LPEO) was prepared and characterized. A varied amount of Chitosan/Alginate (CH/AG) ratios, followed by a mass of LPEO and concentration of sodium tripolyphosphate (STPP) crosslinker, was optimized sequentially to coacervate LPEO using a Tween 80 emulsifier. An antibacterial assay against both Gram-positive and Gram-negative bacteria was further evaluated for the embedded microcapsules. The LPEO (0.2 g) was effectively coacervated by CH/AG (5:3) crosslinked by 2% of STTP to give a yield, oil content (OC), and encapsulation efficiency (EE) of 53.45 ± 2.16%, 65.08 ± 2.60% and 85.04 ± 0.70% respectively. A rough spherical shape of LPEO microcapsules was homogeneously observed with an average particle size of 0.757 mm. An Avrami's kinetic model revealed the release mechanism of the core following zero-order kinetics ( k  = 1.11 ± 0.13 × 10 -9 s -1 , Ea = 70.21 kJ/mol). The LPEO microcapsules demonstrated good thermal stability up to 122 °C and maintained 38% OC at ambient temperature for four weeks. A 70.34 ± 4.16% of the LPEO microcapsules were successfully overlaid onto the gauze with citric acid binder and sodium phosphate catalyst. Overall, the immobilized microcapsules exhibited strong inhibition against S. aureus and moderate against S. epidermidis, E. coli, and K. pneumonia .

A functional fabric immobilized by the microcapsules of C. aurantifolia lime essential oil (LO) was prepared and characterized. A varied amount of CaCl 2 crosslinker was optimized to coacervate LO using alginate-gelatin biopolymers and Tween 80 emulsifier. A further evaluation of the immobilized LO microcapsules for the antibacterial effect against both Gram-positive and Gram-negative bacteria was conducted. The optimized alginate/gelatin-based microcapsules were effectively crosslinked by 15% CaCl 2 with an yield, oil content (OC), and encapsulation efficiency (EE) of 39.91 ± 3.10%, 78.33 ± 7.53%, and 90.27 ± 5.84%, respectively. A spherical shape of LO microcapsules was homogeneously found with an average particle size of 1.394 μm. A first-order kinetics mechanism for the release of LO out of the microcapsules was modeled by Avrami's kinetic equation ( k = 1.60 ± 3.68 × 10 -5 s -1 ). The LO microcapsules demonstrated good thermal stability up to 100 °C and maintained 51.07% OC and 43.56% EE at ambient temperature for three weeks. Using a pad dry method and citric acid binder, LO microcapsules were successfully immobilized on a cloth with a % add on 30.60 ± 1.80%. The LO microcapsules and the immobilized one exhibited a moderate ZoI of bacterial growth for Gram-positive S. aureus and S. epidermidis as well as Gram-negative E. coli and K. pneumonia . Further washing test toward the functional fabric showed that the LO microcapsules incorporated into the fabric were resistant to five cycles of normal washing with a mass reduction of 22.01 ± 1.69%., Competing Interests: There are no conflicts to declare., (This journal is © The Royal Society of Chemistry.)