Search

The future application of Li metal batteries (LMBs) at scale demands electrolytes that endow improved performance under fast-charging and low-temperature operating conditions. Recent works indicate that desolvation kinetics of Li+ plays a crucial role in enabling such behavior. However, the modulation of this process has typically been achieved through inducing qualitative degrees of ion pairing into the system. In this work, we find that a more quantitative control of the ion pairing is crucial to minimizing the desolvation penalty at the electrified interface and thus the reversibility of the Li metal anode under kinetic strain. This effect is demonstrated in localized electrolytes based on strongly and weakly bound ether solvents that allow for the deconvolution of solvation chemistry and structure. Unexpectedly, we find that maximum degrees of ion pairing are suboptimal for ultralow temperature and high-rate operation and that reversibility is substantially improved via slight local dilution away from the saturation point. Further, we find that at the optimum degree of ion pairing for each system, weakly bound solvents still produce superior behavior. The impact of these structure and chemistry effects on charge transfer are then explicitly resolved via experimental and computational analyses. Lastly, we demonstrate that the locally optimized diethyl ether-based localized-high-concentration electrolytes supports kinetic strained operating conditions, including cycling down to -60 °C and 20-min fast charging in LMB full cells. This work demonstrates that explicit, quantitative optimization of the Li+ solvation state is necessary for developing LMB electrolytes capable of low-temperature and high-rate operation.

All-climate temperature operation capability and increased energy density have been recognized as two crucial targets, but they are rarely achieved together in rechargeable lithium (Li) batteries. Herein, we demonstrate an electrolyte system by using monodentate dibutyl ether with both low melting and high boiling points as the sole solvent. Its weak solvation endows an aggregate solvation structure and low solubility toward polysulfide species in a relatively low electrolyte concentration (2 mol L-1). These features were found to be vital in avoiding dendrite growth and enabling Li metal Coulombic efficiencies of 99.0%, 98.2%, and 98.7% at 23 °C, -40 °C, and 50 °C, respectively. Pouch cells employing thin Li metal (50 μm) and high-loading sulfurized polyacrylonitrile (3.3 mAh cm-2) cathodes (negative-to-positive capacity ratio = 2) output 87.5% and 115.9% of their room temperature capacity at -40 °C and 50 °C, respectively. This work provides solvent-based design criteria for a wide temperature range Li-sulfur pouch cells.

3D hosts are promising to extend the cycle life of lithium metal anodes but have rarely been implemented with lean electrolytes thus impacting the practical cell energy density. To overcome this challenge, a 3D host that is lightweight and easy to fabricate with optimum pore size that enables full utilization of its pore volume, essential for lean electrolyte operations, is reported. The host is fabricated by casting a VGCF (vapor-grown carbon fiber)-based slurry loaded with a sparingly soluble rubidium nitrate salt as an additive. The network of fibers generates uniform pores of ≈3 µm in diameter with a porosity of 80%, while the nitrate additive enhances lithiophilicity. This 3D host delivers an average coulombic efficiency of 99.36% at 1 mA cm-2 and 1 mAh cm-2 for over 860 cycles in half-cell tests. Full cells containing an anode with 1.35-fold excess lithium paired with LiNi0.8 Mn0.1 Co0.1 O2 (NMC811) cathodes exhibit capacity retention of 80% over 176 cycles at C/2 under a lean electrolyte condition of 3 g Ah-1 . This work provides a facile and scalable method to advance 3D lithium hosts closer to practical lithium-metal batteries.