Search

This study conducts low-vacuum sulfidation to form a sulfidation layer on the serpentinite-derived magnesium iron silicate, thereby enhancing its electrochemical properties. Results show (Mg,Fe)2SiO4 calcined at 900 °C has the best crystallinity, and the cubic FeS2 is synthesized on the surface of the orthorhombic magnesium iron silicate (MFS). Two distinct charge plateaus can be distinguished during the first charge process, and the discharge capacities increased significantly. This study confirms that the surface FeS2 layer provides extra ion pathways, allowing more lithium/magnesium ions to be extracted and inserted in the serpentinite-derived magnesium iron silicate. Accordingly, the serpentinite electrode boasts straightforward exploitation with low-cost advantages and potential. [ABSTRACT FROM AUTHOR]

Currently, the primary commercial aluminum alloy fillers used are 4043 and 5356. However, when welded with high-strength work pieces like 6061 and 7075 aluminum alloys, the strength of weld beads significantly lags behind that of the original welded material. Both 4043 and 5356 aluminum alloys cannot be strengthened through heat treatment. The strength difference between the weld bead and base material doubles after heat treatment. In this study, an Al-Si-Cu-Mg alloy (SCM) filler modified using a heat-treatable A319 aluminum alloy was employed to investigate the post-welding microstructural and mechanical properties of specimens under room- and high-temperature conditions and after prolonged exposure in a saltwater environment (3.5 wt.% NaCl). The aim was to demonstrate that commercial aluminum alloy fillers could be substituted with a high-silicon aluminum alloy boasting excellent solidification and mechanical properties. The results revealed that, after heat treatment of the weld bead, dendrites were not eliminated, but the tensile strength increased to 310 MPa, closely matching that of commercial 6061 aluminum alloy. The strength of the weld bead remained higher than 250 MPa in high-temperature (240 °C) and saltwater environments. These findings underscore the potential application of this material. [ABSTRACT FROM AUTHOR]

Al–Mg–Sc–Zr alloy fabricated through selective laser melting (SLM) is an additive manufacturing alloy with promising industrial potential. In this study, as-printed specimens were subjected to either single-stage or two-stage heat treatment processes to investigate the effect of temperature from room temperature to high temperature on the specimens' tensile and fatigue properties to establish a reliable reference for aerospace applications. The tensile test results indicated that the heat treatment contributed to determine the properties of the nanoprecipitate Al3(Sc, Zr) with a strengthening phase, improving tensile strength. Moreover, the dynamics strain aging (DSA) effect vanished as temperature increased. It is noteworthy that the nanoprecipitation was distributed at the boundary of the melting pool after single-stage heat treatment with the highest tensile properties in all tests. In addition, the microstructure observed after the two-stage heat treatment indicated a melting pool interface decomposition, and the nanoprecipitation was homogeneously scattered over the Al matrix, increasing strength and further delaying fatigue crack transmission. Those features build a high-fatigue-resistance foundation. TEM analysis also confirmed the promotion of Sc thermal diffusion and an Al3(Sc, Zr) precipitation transformation mechanism under two-stage heat treatment, corresponding to aforementioned inferences. The SLM Al–Mg–Sc–Zr alloy with two-stage heat treatment brings about balance between tensile properties and fatigue resistance, providing new insight into additive manufacturing with Al alloys. [ABSTRACT FROM AUTHOR]