In the current research, the moisture-resistant of Mg-MOF-74 was successfully improved by coating with two-dimensional (2-D) hexagonal boron nitride (h -BN) during the facile hydrothermal synthesis process. Both TEM and SEM results revealed that 2-D h -BN is coated on Mg-MOF-74's surface. The crystal structure, morphology, surface area, thermal stability and CH 4 uptake capacity of Mg-MOF-74 were not drastically influenced by coating with h -BN as examined by XRD, FTIR, SEM, and TEM. Further, the coated Mg-MOF-74 demonstrated better stability than uncoated Mg-MOF-74, when being exposed to high humidity, in terms of surface area and CH 4 uptake capacity. It was observed that the coated Mg-MOF-74 with 1 ​wt % h -BN has reached to 1959 ​m2 ​g−1 surface area and CH 4 uptake capacity of 43 ​cm3 ​g−1 after exposure to high humidity for a duration of 1 month. Thus, this research work has opened a new window towards the improvement of the water stability of Mg-MOF-74. [Display omitted] • The water resistance capacity of Mg-MOF-74 could be improved by coating with two dimensional materials h -BN. • Application of h -BN as coating material of Mg-MOF-74. • h -BN coated Mg-MOF-74 provide high surface area and enhanced CH 4 uptake capacity. • The sample Mg-MOF-74@1 wt.% h -BN exhibited the highest water stability. [ABSTRACT FROM AUTHOR]

Three layered compounds CsLiCoS 2 , CsAgCoS 2 and CsLiFeS 2 have been synthesized by conventional solid-state reaction method. All of three compounds exhibit semiconducting behavior in electrical transport with small thermal activation energy gap. The crystal structure of CsLiCoS 2 is isostructural to ThCr 2 Si 2 -type CsCo 2 S 2 with random mixture of Li+ and Co2+. The latter two compounds exhibit √2 ​× ​√2 ​× ​1 superstructure of ThCr 2 Si 2 -type because the monovalent Ag+/Li+ and divalent Co2+/Fe2+ independently occupy inequivalent sites in [AMS 2 ]- layer. Through comprehensive investigation of the crystallographic lattice in CsAMS 2 , a phase boundary between disorder and ordered phases may be identified, which highlights the importance of the atomic size and lattice mismatch in determining the crystal structure. Image 1 • Three layered sulfides CsAMS 2 (A ​= ​Li, Ag; M ​= ​Co, Fe) are synthesized by solid state reaction method. • Introducing monovalent Li+/Ag+ could significantly change the structure and property of Co-based sulfides. • A phase boundary between random and ordered occupation in the [AMS 2 ]- layers is determined by the atomic size difference. [ABSTRACT FROM AUTHOR]