High-temperature polymer-electrolyte membrane fuel cells (HT-PEMFCs) are a very important type of fuel cells since they operate at 150–200 °C, making it possible to use hydrogen contaminated with CO. However, the need to improve the stability and other properties of gas-diffusion electrodes still impedes their distribution. Self-supporting anodes based on carbon nanofibers (CNF) are prepared using the electrospinning method from a polyacrylonitrile solution containing zirconium salt, followed by pyrolysis. After the deposition of Pt nanoparticles on the CNF surface, the composite anodes are obtained. A new self-phosphorylating polybenzimidazole of the 6F family is applied to the Pt/CNF surface to improve the triple-phase boundary, gas transport, and proton conductivity of the anode. This polymer coating ensures a continuous interface between the anode and proton-conducting membrane. The polymer is investigated using CO2 adsorption, TGA, DTA, FTIR, GPC, and gas permeability measurements. The anodes are studied using SEM, HAADF STEM, and CV. The operation of the membrane–electrode assembly in the H2/air HT-PEMFC shows that the application of the new PBI of the 6F family with good gas permeability as a coating for the CNF anodes results in an enhancement of HT-PEMFC performance, reaching 500 mW/cm2 at 1.3 A/cm2 (at 180 °C), compared with the previously studied PBI-O-PhT-P polymer. [ABSTRACT FROM AUTHOR]

The efficient use of renewable energy sources requires development of new electrocatalytic materials for electrochemical energy storage systems, particularly fuel cells. To increase durability of high temperature polymer electrolyte fuel cell (HT-PEMFC), Pt/carbon black based catalysts should be replaced by more durable ones, for example Pt/carbon nanofibers (CNF). Here, we report for the first time the quantitative ascorbic acid assisted deposition of Pt onto electrospun polyacrylonitrile-based CNF composite materials. The effect of their subsequent post-treatment at various temperatures (250 and 500 °C) and media (vacuum or argon-hydrogen mixture) on the Pt/C catalyst morphology is investigated. All obtained samples are thoroughly studied by high resolution electron microscopy, and Pt electrochemically active specific surface area was evaluated by cyclic voltammetry. [ABSTRACT FROM AUTHOR]