Oak (Quercus robur L.), iroko (Milicia excelsa (Welw.) C.C. Berg), and tauari (Couratari spp.) wood were subjected to cyclic thermo-mechanical treatment (CTMT). The densification temperature amounted to 100 °C or 150 °C. The greatest changes in the modulus of rupture (MOR) value of the iroko wood, depending on the number of thermo-mechanical modification cycles, were noted. The MOR of the iroko wood, densified at 100 °C or 150 °C, after second thermo-mechanical modification cycle was twice as high as before the modification. No significant differences were observed between the modulus of elasticity (MOE) of oak wood before and after one modification cycle. Similar dependencies were noted in iroko wood. The thermo-mechanical modification performed over two cycles led to the highest increase, by about 56%, in MOE in oak wood densified at 150 °C. It was demonstrated that modification at 150 °C had a negative impact on iroko wood, which was manifested in the lower compression ratio of iroko at 150 °C than at 100 °C. [ABSTRACT FROM AUTHOR]

Black poplar (Populus nigra L.) was subjected to thermal modification in superheated steam. The modification was performed at 160 °C, 190 °C, and 220 °C for 2 h. The equilibrium moisture content of the black poplar wood was examined when it was exposed to 76% ± 2% relative humidity at a temperature of 20 °C ± 2 °C. The thermal modification of the poplar wood changed its moisture-exchange-related physical properties to a large extent. The effects of temperature on individual properties (density, mass loss, hygroscopicity, swelling, and water absorption) were diverse, and the intensity of these effects increased with increasing temperature of the thermal treatment process. In most cases, no significant differences were observed between the changes in properties of the sapwood and the heartwood. [ABSTRACT FROM AUTHOR]

This study examined the influence of temperature and time of treatment on the density profile and hardness of surface-densified birch wood (Betula pendula Roth). An analysis of the wood density profile was conducted on the basis of the following parameters: thickness, maximum density, and the distance between the maximum density and the wood surface. Depending on the technological parameters' values, the degree of compression of the wood was 13% to 22%, and its maximum density was 808 kg/m3 to 994 kg/m3. As a result of the modification of birch wood at a temperature of 100 °C and 125 °C, the wood was densified on one side. As the temperature of the thermo-mechanical treatment was raised from 150 °C to 200 °C, the wood became densified on both sides. The maximum density of the wood increased gradually with the increase of the temperature of the press plate. The longer the time of thermomechanical treatment, the more distant the maximum density area was from the wood surface. Depending on the temperature and the time of treatment, the hardness of the surface-densified birch wood was 1.4 to 2.2 times greater than the hardness of non-densified wood. [ABSTRACT FROM AUTHOR]