Carbon fabric reinforced phenolic (CFRP) composites filled with nano-Al2O3were prepared by a dip-coating and heat molding process and the tribological properties of the resulting composites under different sliding conditions were investigated systematically on a block-on-ring test rig. The worn surfaces were observed in a scanning electron microscope (SEM) to understand the mechanism. Nano-Al2O3particles, as the filler, were effective in reducing the friction coefficient and wear rate of the CFRP composites. The steady state friction coefficient of the CFRP composites filled with 4 wt.% nano-Al2O3particles was about 65.5% of that of unfilled CFRP composites, and the wear rate, in this case, was about 74.7% of that of unfilled CFRP composites. Tribological tests under different sliding conditions revealed that the filled CFRP composites seemed to be more suitable than unfilled CFRP composites for tribological applications under higher sliding speed and load. Moreover, the wear resistances of the unfilled and filled CFRP composites were found to be related to the stability of the transfer film on the counterface. [ABSTRACT FROM PUBLISHER]

A series of micro hollow glass beads (HGB) filled castor oil-based polyurethane/epoxy resin graft interpenetrating polymer network (IPN) composites were prepared. The tensile and impact strengths, impact fractured surfaces, damping properties and thermal stability of the IPN composites were studied systematically in terms of composition. Results revealed that the addition of HGB into polyurethane/epoxy IPN can significantly improve not only the tensile strength but also the impact strength. The tensile strength was increased by 61% and at the same time the impact strength was increased by 25% when the HGB content was 1.5%. The damping properties were better than the composition of 0.5% or 2% HGB content when the HGB content was 1% or 1.5%. The thermal decomposition temperature was also slightly improved by the incorporation of HGB. It is suggested that the HGB reinforced polyurethane/epoxy resin IPN composites could be used as structural damping materials. [ABSTRACT FROM AUTHOR]

Polyimide (PI) composites modified with nano-CuO and graphite were prepared by means of a hot press molding technique. The effects of nano-CuO and graphite on the tribological properties of the composites were studied using a block-on-ring arrangement. The results revealed that the incorporation of graphite alone improved the friction-reducing and anti-wear abilities of the PI composites, whereas incorporation of nano-CuO alone deteriorated the wear resistance of the PI composite owing to its abrasive effect. A synergistic effect was found for the combination of nano-CuO and graphite, which leads to the best tribological properties. The results showed that the filled PI composites exhibited worse tribological properties under higher load and sliding speed, and showed better friction and wear behavior under oil lubrication and worse tribological properties under water lubrication. [ABSTRACT FROM AUTHOR]