Search

Sn60Pb40 alloy powders were fabricated using the planar flow casting (PFC) atomization process. By using OM, SEM and EPMA, the characteristics of the morphologies and microstructures of the powders have been investigated. It is observed that the environment of ambient gas in the atomization box has great effects on the morphology of the alloy powders. The microstructures of Sn60Pb40 alloy powders produced by the PFC atomization process are completely composed of eutectic, which is made up of both oversaturated α solid solution and β solid solution. The microstructures of small size powders are extraordinarily undeveloped dendritic eutectic, in which the large majority of the α phase appears nearly spherical, evidently since the cooling rate is higher and the under-cooling is larger. As for the large size powders, since the cooling rate and undercooling are relatively low, lamellar α phase apparently increases in the eutectic microstructures of these powders, and there is even typical lamellar eutectic structure clearly observed in some micro-areas. After remelting tests by DTA, the microstructures of small size powders are transformed, which become composed of large crumby α phase and eutectic (α+β), while those of large size powders change into classical tin-lead structures of primary α phase plus lamellar eutectic (α+β). By studying the microstructures of tin-lead alloy powders, a model has been proposed to predict the microstructure formation of Sn60Pb40 alloy powders.

Post-bond heat treatment (PBHT) is an effective way to improve the bonding quality of a brazed joint. Herein, brazing of a nickel-based single crystal superalloy is carried out using a Ni-Cr-Co-B-Si-Al-Ti-W-Mo filler alloy, and the microstructure and creep property of the brazed joint are systematically investigated using scanning electron microscopy (SEM), Thermo-Calc software, an electron probe micro-analyzer (EPMA), X-ray diffractometer, confocal scanning laser microscope (CSLM), and transmission electron microscopy (TEM). The results reveal that the as-prepared joint only consists of an isothermally solidified zone (ISZ) and an athermally solidified zone (ASZ), where the cubic γ′ phase is observed in the ISZ, and skeleton-like M3B2, γ + γ′ eutectic and reticular G phases are observed in the ASZ. Furthermore, the γ + γ′ eutectic and G phases disappear and the M3B2 alters from a skeleton-like to block-like shape in the ASZ after PBHT. Meanwhile, some lath-like M3B2 phases are precipitated at the edge of the ISZ and several M3B2 phases are precipitated in the base metal, forming a new zone in the brazed joint, namely at the diffusion affected zone (DAZ). Owing to the removal of low melting point eutectics from the as-prepared joint, the creep life also increases from 188 h to 243 h after PBHT. The current work provides a method for the optimization of brazed joints based on the Ni-based single crystal superalloy. [ABSTRACT FROM AUTHOR]

The influences of minor amounts of scandium on the microstructure and mechanical properties of as-cast ZA27 alloy have been experimentally investigated. The experimental results show that as far as the Sc addition is individually concerned, the refinement result of the as-cast ZA27 alloy with 0.5wt.%Sc addition is comparatively better. After alloying with minor amounts of Sc, the coarse dendrites of the ZA27 alloy are refined and transformed into the uniform and small equiaxed grain microstructure; also the eutectics among the grain boundaries become finer. The test results of mechanical properties show that the tensile strength and hardness of the as-cast ZA27 alloy containing 0.5wt.%Sc approach 495 MPa and 120.2 HB, increase by 28.5% and 33.1%, respectively, compared with those of the ZA27 alloy with no addition of Sc element, while the elongation of the alloy is improved to 7.6% from 2.7%. The SEM, EDAX and XRD analyses show that in the ZA27 alloy, the trace element Sc combines with Al to form the square AI3Sc phase particles, which serve as heterogeneous nuclei, facilitating the refinement of the microstructure and the improvement of the mechanical properties of the alloy. [ABSTRACT FROM AUTHOR]