Search

Poly(methyl methacrylate) films and poly(methyl methacrylate)/fullerene composite films were fabricated by casting from toluene solutions. The mass fraction of fullerene (C60) was varied from 0.05-3 wt. %. The effect of the fullerene (C60) content on the thermal degradation parameters of the composite films was evaluated by thermogravimetric (TG) analysis. It was found that the incorporation of C60 improved the thermal stability of the polymers. The films eventually decomposed in three stages. Incorporation of fullerene caused a change in the distribution of mass loss over the stages of degradation in comparison with the pristine polymer. Using differential scanning calorimetry (DSC), the phase transitions from the glassy state to the elastic one was studied for the examined polymeric materials. New data relating to the effect of C60 on the glass transition temperature of composites with low weight fractions of filler were obtained. Specifically, for films containing up to 0.1 wt. % of C60, a single glass transition temperature was found, whereas for composites with a higher concentration of filler, two glass transition temperatures were recorded. [ABSTRACT FROM AUTHOR]

The particle-size distribution in silica powder prepared by the sol-gel method has been determined by dynamic light scattering analysis. The average diameter of the particles was found to be 250 nm. Using a low-temperature nitrogen adsorption-desorption technique, it was found that the synthesised powder may be referred to as mesoporous materials. Polystyrene/silica composite films were fabricated by casting from o-xylene solutions. It was found, using thermogravimetry, that incorporation of silica leads to an increase in both the onset temperature of polymer degradation and in the temperature at which the maximum rate of weight loss occurs. Using differential scanning calorimetry, the phase transitions from the glassy state to the elastic one were studied for the polymeric materials. New data relating to the effect of silica on the glass-transition temperature, Tg, of composites with a low weight fraction of SiO2 were found. Specifically, we found a non-monotonic concentration dependence of the value of Tg. The present results advocate for employing silica as an effective filler for producing polymer composites with enhanced thermal properties. [ABSTRACT FROM AUTHOR]

Organobentonite powder was synthesized and characterized using laser diffraction, X-ray diffraction, low-temperature nitrogen adsorption-desorption technique, and dynamic light scattering. Obtained powder was found as material with mesopores. The organobentonite particles were larger than pure bentonite one. Hydroxyethyl cellulose (HEC) was filled with organobentonite particles by mechanical dispersion, and produced composite films were researched by the number of methods. New data relating to structure, tensile properties, and antimicrobial activity of HEC/organobentonite composites were obtained. Using results of X-ray diffraction, the reflections assigned to crystal filler in polymer material were proved. Concentration effect of the filling agent on tensile properties of composite film was revealed. Data of infrared (IR) spectrometry indicated a decrease in the density of hydrogen-bond net in HEC/organobentonite composite as compared with pristine HEC. Using microbiological tests, it was found that the HEC/organobentonite films exhibited bacteriostatic action against S. aureus and fungistatic action against molds. [ABSTRACT FROM AUTHOR]

Polystyrene composite films with different content of C + C fullerene mix have been obtained from o-xylene solutions. The mass fraction of fullerene was varied from 0.01 to 0.1 mass%. The glass transition temperatures and specific heat capacities in range of 293-423 K have been determined for the films by DSC method. The plasticization of the polymer is observed in thermal properties of the films under influence of small fullerene additions. The values of T and C decrease and thermal coefficient of heat capacity b increase as fullerene content increases up to 0.02 mass%. The effect of interaction between polymer and fullerene molecules on thermal properties becomes evident at higher fullerene content in range from 0.02 to 0.1 mass%. At this the values of T and C increase and b coefficient decrease with increasing content of fullerene. Concentration dependence of C and b values is less steep for polymer composite films in elastic state at temperatures above T. Molecular interactions in the composites are discussed in view of our-self and literature data. [ABSTRACT FROM AUTHOR]