Search

The nature of mass transport in plants has recently inspired the development of low-cost and sustainable wood-based electronics. Herein, we report a wood electrochemical transistor (WECT) where all three electrodes are fully made of conductive wood (CW). The CW is prepared using a two-step strategy of wood delignification followed by wood amalgamation with a mixed electron-ion conducting polymer, poly(3,4-ethylenedioxythiophene)-polystyrene sulfonate (PEDOT:PSS). The modified wood has an electrical conductivity of up to 69 Sm-1 induced by the formation of PEDOT:PSS microstructures inside the wood 3D scaffold. CW is then used to fabricate the WECT, which is capable of modulating an electrical current in a porous and thick transistor channel (1 mm) with an on/off ratio of 50. The device shows a good response to gate voltage modulation and exhibits dynamic switching properties similar to those of an organic electrochemical transistor. This wood-based device and the proposed working principle demonstrate the possibility to incorporate active electronic functionality into the wood, suggesting different types of bio-based electronic devices. [ABSTRACT FROM AUTHOR]

The need for achieving sustainable technologies has encouraged research on renewable and biodegradable materials for novel products that are clean, green, and environmentally friendly. Nanocellulose (NC) has many attractive properties such as high mechanical strength and flexibility, large specific surface area, in addition to possessing good wet stability and resistance to tough chemical environments. NC has also been shown to easily integrate with other materials to form composites. By combining it with conductive and electroactive materials, many of the advantageous properties of NC can be transferred to the resulting composites. Conductive polymers, in particular poly(3,4-ethylenedioxythiophene:poly(styrene sulfonate) (PEDOT:PSS), have been successfully combined with cellulose derivatives where suspensions of NC particles and colloids of PEDOT:PSS are made to interact at a molecular level. Alternatively, different polymerization techniques have been used to coat the cellulose fibrils. When processed in liquid form, the resulting mixture can be used as a conductive ink. This review outlines the preparation of NC/PEDOT:PSS composites and their fabrication in the form of electronic nanopapers, filaments, and conductive aerogels. We also discuss the molecular interaction between NC and PEDOT:PSS and the factors that affect the bonding properties. Finally, we address their potential applications in energy storage and harvesting, sensors, actuators, and bioelectronics. [ABSTRACT FROM AUTHOR]

Abstract The conductive polymer poly(3,4-ethylenedioxythiphene):poly(styrenesulfonate) (PEDOT:PSS) is widely used in organic electronics and printed electronics due to its excellent electronic and ionic conductivity. PEDOT:PSS films exhibit anisotropic conductivities originating from the interplay of film deposition processes and chemical structure. The previous studies found that high boiling point solvent treated PEDOT:PSS exhibits an anisotropy of 3–4 orders magnitude. Even though both the in-plane and out-of-plane conductivities are important for the device performance, the out-of-plane conductivity is rarely studied due to the complexity with the experiment procedure. Cellulose-based paper or films can also exhibit anisotropic behavior due to the combination of their intrinsic fibric structure and film formation process. We have previously developed a conductive paper based on PEDOT:PSS and cellulose which could be used as the electrodes in energy storage devices. In this work we developed a novel measurement set-up for studying the anisotropy of the charge transport in such composite materials. A tool with two parallel plates mounted with spring loaded probes was constructed enabling probing both lateral and vertical directions and resistances from in-plane and out-of-plane directions to be obtained. The measurement results were then input and analyzed with a model based on a transformation method developed by Montgomery, and thus the in-plane and out-of-plane conductivities could be detangled and derived. We also investigated how the conductivity anisotropy depends on the microstructure of the cellulose template onto which the conductive polymer self-organizes. We show that there is a relatively small difference between the in-plane and out-of-plane conductivities which is attributed to the unique 3D-structure of the composites. This new knowledge gives a better understanding of the possibilities and limitations for using the material in electronic and electrochemical devices. Graphical abstract Image 1 Highlights • Developed a simple to use generic tool for measuring 3-D resistances of thick conducting self-standing films. • The in-plane and out-of-plane conductivities were deduced by a method developed by Montgomery. • Both CNF-PEDOT:PSS and pulp-PEDOT:PSS films exhibit anisotropic conductivity. • CNF-PEDOT:PSS films show thickness independent anisotropic conductivity. • Pulp-PEDOT:PSS became less anisotropic with increasing thicknesses. [ABSTRACT FROM AUTHOR]

Advances in organic electronics necessitates, ultrathin and miniaturized implantable energy storage modules. Here, an approach for the fabrication of on-chip, ultraflexible electrochemical capacitors is demonstrated. Two different electroactive conjugated polymers are utilized in a fabrication route that allows the patterning of finger electrodes for an ultraflexible energy storage technology. A strategy is demonstrated to realize supercapacitors with a total device thickness of 4 μm, including substrate, polymer electrode, and electrolyte. Interdigitated 20-finger electrodes from either Poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) or polythiophene functionalized with tetraethylene glycol side chains P(g42T-T), with 50 μm or 90 μm electrode spacings, are fabricated using a parylene peel off method, followed by electrolyte deposition. The miniaturized devices show 0.77 mF/cm2 areal capacitance for PEDOT:PSS and 0.06 mF/cm2 for P(g42T-T). Furthermore, the devices exhibit excellent mechanical durability, showing robust operational performance at a bending radius of 6.5 mm. [Display omitted] • Scalable fabrication route for polymer IDE structures using parylene peel off method. • PEDOT:PSS and P(g42T-T) microsupercapacitors with more than 0.6 mF/cm2 capacitance. • Ultrathin organic electronics device technology with total thickness of 4 μm. • Excellent mechanical durability, showing robust operational performance at a bending radius of 6.5 mm. [ABSTRACT FROM AUTHOR]

A novel patterning technique of conductive polymers produced by vapor phase polymerization is demonstrated. The method involves exposing an oxidant film to UV light which changes the local chemical environment of the oxidant and subsequently the polymerization kinetics. This procedure is used to control the conductivity in the conjugated polymer poly(3,4-ethylenedioxythiophene):tosylate by more than six orders of magnitude in addition to producing high-resolution patterns and optical gradients. The mechanism behind the modulation in the polymerization kinetics by UV light irradiation as well as the properties of the resulting polymer are investigated. [ABSTRACT FROM AUTHOR]