Search

Dy3+-doped CaF2-SrF2 crystals with various Dy3+ dopant concentrations were synthesized by multicrucible temperature gradient technology (MC-TGT). Dy:CaF2-SrF2 crystals were fluorite structured and crystallized in cubic F m 3 ¯ m space group, as characterized by X-ray diffraction. The crystallographic site concentration was calculated from the measured density by Archimedes' hydrostatic weighing principle. The optical transmission reached over 90% with a sample thickness of 1.0 mm. The Sellmeier dispersion formula was obtained following the measured refractive index in a mid-IR range of 1.7–11 μm. Absorption coefficients of 6.06 cm−1 and 12.71 cm−1 were obtained at 804 nm and 1094 nm in 15% Dy:CaF2-SrF2 crystal. The fluorescence spectra of 15 at.% Dy:CaF2-SrF2 showed the strongest wavelength peak at 2919 nm with a full width at half maximum (FWHM) of 267 nm under an excitation wavelength of 808 nm. The fluorescence lifetimes were illustrated for different Dy3+ dopant levels of 5%, 10% and 15%. The results indicate that the Dy:CaF2-SrF2 crystal is a promising candidate for compact mid-IR lasers. [ABSTRACT FROM AUTHOR]

Sm:YAlO 3 (Sm:YAP) crystal with size of Φ28 × 80 mm3 was grown by Czochralski (Cz) method. Polarized absorption spectra and fluorescence spectra of Sm:YAP crystal were discussed for the first time. The peak emission cross-sections were calculated to be 0.80 × 10−21 cm2 (604 nm for a-polarization), 1.82 × 10−21 cm2 (604 nm for b-polarization) and 1.63 × 10−21 cm2 (610 nm for c-polarization), respectively. The Judd-Ofelt (JO) intensity parameters were calculated to be Ω 2 = 2.59 × 10−20 cm2, Ω 4 = 1.78 × 10−20 cm2 and Ω 6 = 2.98 × 10−20 cm2, respectively. The decay lifetime of 4G 5/2 energy level was measured to be 2.51 ms. All above results indicate the Sm:YAP crystal may be a potential candidate of reddish-orange laser pumped directly by the GaN/InGaN laser diode. • Sm:YAlO 3 crystal was grown by Cz method. • Polarized optical spectra of Sm:YAlO 3 crystal were investigated. • The transitions of 4G 5/2 → 6H 7/2 have the highest branching ratio value, which is suitable for reddish-orange laser. [ABSTRACT FROM AUTHOR]

Pr 3+ -doped YAlO 3 (YAP) single crystal was successfully grown by the Czochralski (Cz) method. Polarized absorption and polarized fluorescence spectra were measured at the room temperature. The spectroscopic parameters based on the polarized absorption spectra were calculated by Judd-Ofelt (J-O) theory for the first time. The fluorescence lifetime of 3 P 0 energy level was fitted to be 19.16 μs with the quantum efficiency of 95.8%. Through the analyzing of the spectroscopic properties, Pr:YAP crystal was demonstrated to be a promising candidate for solid state laser operation. [ABSTRACT FROM AUTHOR]

GdScO 3 single crystal codoped with Tm3+ and Tb3+ ions was successfully grown by the Edge-defined Film-fed Growth Method (EFG) for the first time. Absorption, fluorescence spectrum and fluorescence lifetimes of the grown crystal at room temperature were measured. The absorption cross-section at 789 nm was calculated to be 8.20 × 10−21 cm2. The emission cross-section was 1.35 × 10−21 cm2 at 1504 nm with the FWHM of 95.3 nm. The fluorescence lifetimes of the 3H 4 state and the 3F 4 state were fitted to be 253 μs and 1460 μs, respectively. Compared with Tm3+ single doped GdScO 3 crystal, the codoping of Tb3+ successfully depopulated the 3F 4 energy level and enhanced the emission at 1.5 μm region. It indicated that Tm,Tb:GdScO 3 could be favorable laser medium for 1.5 μm-laser operation. • Tm3+ and Tb3+ co-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed method (EFG) for the first time. • Spectral parameters and Judd-Ofelt parameters of Tm,Tb:GdScO3 crystal were obtained and compared. • The fluorescence mechanism of Tm3+ and Tb3+ co-doped GdScO 3 crystal has been studied. [ABSTRACT FROM AUTHOR]