Search

[Display omitted] • The effect of structure evolution under working condition of MNC electrocatalysts on the OER activity and stability has been studied with the DFT method. • This work conducted a comprehensive evaluation method for MNC electrocatalysts by taking ΔG *OH as the screening criterion for OER activity and ΔE b of electrocatalysts under working conditions as the stability descriptor. • The stability of MNC electrocatalysts under working conditions, including high temperature, dynamic condition, local electric field and strong specific adsorption has been studied in detail. Developing low-cost, high activity and stability oxygen evolution reaction (OER) catalysts is significantly important but still challenging for water electrolyzers. In this work, we calculated the OER activity and stability of Metal-Nitrogen-Carbon (MNC, M = Co, Ru, Rh, Pd, Ir) based electrocatalyst with different structures (MN 4 C 8 , MN 4 C 10 , MN 4 C 12) using density functional theory (DFT) method. These electrocatalysts were divided into three groups based on the value of ΔG *OH , that is ΔG *OH > 1.53 eV (PdN 4 C 8 , PdN 4 C 10 , PdN 4 C 12), ΔG *OH < 1.23 eV (RuN 4 C 8 , RuN 4 C 10 , RuN 4 C 12 , CoN 4 C 8 , CoN 4 C 10) and 1.23 eV < ΔG *OH < 1.53 eV (RhN 4 C 8 , RhN 4 C 10 , RhN 4 C 12 , IrN 4 C 8 , IrN 4 C 10 , IrN 4 C 12 , CoN 4 C 12), and ΔG *OH determine whether the structure evolution will appear. The results proved that MNC (M = Rh, Ir) with 1.23 eV < ΔG *OH < 1.53 eV shows higher OER activity due to moderate binding energy between reaction intermediates and MNC. Furthermore, these catalysts could maintain M N C structure without further oxidation and structural evolution under working conditions (high temperature, dynamic condition, local electric field and strong specific adsorption), therefore show excellent stability. However, MNC electrocatalyst with ΔG *OH > 1.53 eV or ΔG *OH < 1.23 eV revealed less stability under working conditions, due to their low intrinsic stability or structural evolution under working conditions, respectively. In conclusion, we proposed a comprehensive evaluation method for MNC electrocatalysts by taking ΔG *OH as the screening criterion for OER activity and stability, as well as ΔE b under working condition as descriptor of stability. This is of great significance for the design and screening of ORR, OER and HER electrocatalysts under working conditions. [ABSTRACT FROM AUTHOR]

[Display omitted] • Design of the prior PA-resistance electrocatalysts through theoretical calculation. • Discovery of different scaling relationship of the adsorption energy difference of O 2 and H x PO(3-x)- 4 on Pt 3 M(1 1 1) alloy surface. • Pt X Cu as the object for the research of internal mechanism of the potentially high PA resistance property. • Higher PA-resistance performance of Pt 2 Cu compared to the commercial PtC in half-cell and full-cell tests. In high temperature polymer electrolyte membrane fuel cells (HT-PEMFCs), dissociative H 3 PO 4 in cathode will block the active sites of Pt-based electrocatalyst, which thus failure to catalyze the oxygen reduction reaction (ORR). Therefore, the electrocatalysts for the ORR in HT-PEMFCs with high resistance to H 3 PO 4 poisoning are significantly important. Due to the similar bonding structure between H x PO 4 3-x/O 2 and Pt (Pt-O), the design of catalysts which could selectively reduce the adsorption energy of the H 3 PO 4 is urgently needed. In this work, we screen proper H 3 PO 4 resistance electrocatalysts through theoretical calculation based on the adsorption energy difference between H x PO 4 3-x and O 2 as an evaluation criterion. Then, we prepared a series of Pt x Cu catalysts based on the theoretical calculation results and further studied the structure-performance relationship of phosphoric acid-resistant catalysts through combining physical property characterization and electrochemical tests including half-cell and single-cell. The mass activity of Pt 2 Cu/C is 0.51 A/mg Pt , exceeding the DOE's 2020 target of 0.44 A/mg Pt. After add 0.1 M H 3 PO 4 into the HClO 4 electrolyte, the half-wave potential (E 1/2) of Pt 2 Cu/C is only negatively shifted by 47 mV, much lower than 90 mV of TKK Pt/C. Furthermore, the HT-PEMFC with Pt 2 Cu/C in the cathode shows a peak power density of 383.4 mW/cm2, which surpasses that of TKK Pt/C for 231.0 mW/cm2. Our strategy of screening catalysts based on the adsorption energy difference study and further verified by experimental methods provides a promising strategy for the design of practical electrocatalyst in the cathode of HT-PEMFCs. [ABSTRACT FROM AUTHOR]