Search

Yb,Tb:YAG crystals with various Yb3+ and Tb3+ concentration were grown by the micro-pulling-down method (μ -PD). The absorption spectra, fluorescence spectra and fluorescence decay curves of Yb,Tb:YAG crystals were measured at room temperature. Under 980 nm excitation, Yb,Tb:YAG crystals exhibited intense visible up-conversion luminescence due to the cooperative energy transfer from two Yb3+ ions to one Tb3+ ion. Under 485 nm excitation, Yb,Tb:YAG crystals yielded near-infrared down-conversion emission, ascribing to the cooperative absorption of pumping photons and cooperative energy transfer from one Tb3+ ion to two Yb3+ ions. The energy transfer processes from Yb3+ ions to Tb3+ ions were discussed, and the energy transfer efficiency was calculated. Based on studies of the obtained results, Yb3+/Tb3+ co-doped YAG crystal shows promising potential for sensing, volumetric displays, optical data storage, light emitting diodes. • Yb,Tb:YAG single crystals grown by the micro-pulling-down technique. • The cooperative energy transfer process was analyzed. • The effect of doped concentration on energy transfer efficiency was discussed. [ABSTRACT FROM AUTHOR]

Tm3+-doped bismuth germanate crystals (Tm:BGO) with various doping concentrations of 0.5, 0.75, 1.0, 1.5, and 2.0 at.% were grown by the micro-pulling-down method (μ-PD). The effect of thulium concentration on the growth, structure, absorption spectra, emission spectra and fluorescence lifetime of 3H 4 and 3F 4 state was studied. Under excitation of 792 nm, Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. The fluorescence lifetime of 3H 4 state decreased strongly as the thulium concentration increased, while the lifetime of 3F 4 state was relatively constant for all thulium concentrations. • Tm:BGO crystals with different Tm3+ concentration were grown by the micro-pulling-down method. • The effect of Tm3+ concentration on the growth, structure and spectroscopic properties of Tm:BGO crystals was studied. • Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. [ABSTRACT FROM AUTHOR]

Photograph of Yb,Ho:YAG crystals grown by the μ-PD method. (a) Yb = 0.05, (b) 0.1, (c) 0.15. • Y 3 Al 5 O 12 (YAG) single crystals doped with a fixed Ho3+ content of 0.5 at.% and various Yb3+ contents (Yb = 5, 10 and 15 at.%) have been successfully grown by the micro-pulling-down (μ-PD) method. Y 3 Al 5 O 12 (YAG) single crystals doped with a fixed Ho3+ content of 0.5 at.% and various Yb3+ contents (Yb = 5, 10 and 15 at.%) have been successfully grown by the micro-pulling-down (μ-PD) method. The absorption spectra, fluorescence spectra and fluorescence decay curves were recorded at room temperature. The intense emission of Yb,Ho:YAG crystal centered at 2 μm corresponds to the 5I 7 → 5I 8 transition. Three intense emissions centered at 524–569 nm, 623–691 nm and 744–746 nm, correspond to the 5F 4 + 5S 2 → 5I 8 , 5F 5 → 5I 8 and 5F 4 + 5S 2 → 5I 7 transitions, respectively. The possible energy transfer mechanisms were discussed intensively. [ABSTRACT FROM AUTHOR]

Dy3+-doped Y 3 Al 5 O 12 (YAG) and Y 3 ScAl 4 O 12 (YSAG) single crystals have been successfully grown by the micro-pulling-down (μ-PD) technique for the first time. The room temperature absorption spectra, fluorescence spectra and fluorescence decay curves were measured. Dy:YAG and Dy:Y 3 ScAl 4 O 12 crystals exhibit strongest emission centered at 583 nm, corresponding to the 4F 9/2 → 6H 13/2 transition. The decay lifetime of the 4F 9/2 level was measured to be 634 μs and 667 μs, respectively. All these results indicate that the Dy:YAG and Dy:Y 3 ScAl 4 O 12 crystals are promising candidates for yellow laser operation. • Dy:YAG and Dy:YSAG crystals were grown by the micro-pulling-down method. • Dy:YAG and Dy:YSAG crystals exhibit strong emission centered at 583 nm. • Dy:YSAG crystal has a wide emission bandwidth due to the disordered crystalline structure. [ABSTRACT FROM AUTHOR]