The particle-size distribution in silica powder prepared by the sol-gel method has been determined by dynamic light scattering analysis. The average diameter of the particles was found to be 250 nm. Using a low-temperature nitrogen adsorption-desorption technique, it was found that the synthesised powder may be referred to as mesoporous materials. Polystyrene/silica composite films were fabricated by casting from o-xylene solutions. It was found, using thermogravimetry, that incorporation of silica leads to an increase in both the onset temperature of polymer degradation and in the temperature at which the maximum rate of weight loss occurs. Using differential scanning calorimetry, the phase transitions from the glassy state to the elastic one were studied for the polymeric materials. New data relating to the effect of silica on the glass-transition temperature, Tg, of composites with a low weight fraction of SiO2 were found. Specifically, we found a non-monotonic concentration dependence of the value of Tg. The present results advocate for employing silica as an effective filler for producing polymer composites with enhanced thermal properties. [ABSTRACT FROM AUTHOR]

In this study, an ionic liquid (IL), 1-butyl-3-methylimidazolium acetate, was used to prepare ionogels with microcrystalline cellulose (MCC) and halloysite (Hal). SEM, XRD, TG, DSC, FTIR spectroscopy, conductometry and mechanical tests were used to study the morphology, structure, thermal behaviour and electrophysical and mechanical characteristics of synthesised ionogels. XRD analysis showed a slight decrease in the interlayer space of halloysite in ionogels containing MCC, which may have been associated with the removal of residual water molecules resulting from hydrophilic IL anions and polymer macromolecules. A change in conductivity and glass-transition temperature of the ionic liquid was revealed due to intercalation into halloysite (a confinement effect) and modification with cellulose. For triple IL/Hal/MCC ionogels, the characteristic thermal degradation temperatures were higher than the corresponding values for IL/Hal composites. This indicates that the synthesised IL/Hal/MCC ionogels are characterised by a greater thermal stability than those of IL/Hal systems. [ABSTRACT FROM AUTHOR]