Abstract: In this paper, we present results on upconversion luminescence performed on Yb3+-doped yttrium aluminum garnets under 940nm excitation. The upconversion luminescence was ascribed to Yb3+ cooperative luminescence and the presence of rare earth impurity ions. The cooperative luminescence spectra as a function of Yb concentration were measured and the emission intensity variation with Yb concentration was discussed. Yb3+ energy migration quenched the cooperative luminescence of Yb:YAG crystals with doping level over 15at%. [Copyright &y& Elsevier]

Abstract: In this paper, single crystal of ytterbium (Yb) doped Ca5(PO4)3F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (σ abs) is 5.117×10−20 cm2 with an FWHM of 4nm at 982nm. The emission cross-section (σ em) is 3.678×10−20 cm2 at 1042nm. Favorable values of the absorption cross-section at about 982nm are promising candidates for laser diode (LD) pumping. [Copyright &y& Elsevier]

Abstract: Ytterbium-doped calcium pyroniobate single crystal has been grown for the first time. Spectral properties of Yb: Ca2Nb2O7 were investigated by emission and absorption spectra. Its cooperative luminescence and fluorescence lifetime were also studied. Yb ions in Ca2Nb2O7 showed very broad absorption and emission bandwidth and relatively large absorption and emission cross-sections. Along with other optical properties, this Yb-doped crystal would be a potential self-frequency doubling femtosecond laser gain material. [Copyright &y& Elsevier]

Abstract: Gd2SiO5 (GSO) single crystal codoped with Yb3+ and Er3+ (Abbr. as Er:Yb:GSO) was successfully grown by the Czochralski (CZ) method for the first time and the spectral characteristics were investigated. The absorption and fluorescence spectra were measured. The emission lifetime of the 4I13/2–Er-level was measured to be 5.84ms and the emission cross-section at 1529nm was calculated to be 1.03×10−20 cm2. The results indicate that Er:Yb:GSO is a potential laser material at ∼1.55μm wavelength region. [Copyright &y& Elsevier]