Search

AZ61 magnesium alloy metal matrix composites (MMCs) with different weight percentages (0, 1 and 2) of micro-silicon carbide particles (SiCp) were fabricated using stir casting method. Effects of SiCp on the microstructural distributions, mechanical and fatigue properties, and fracture surfaces have been investigated. The microstructural observations of as-cast MMCs unveil the existence of primary α-Mg phase and the presence of large amount of β-Mg17Al12 secondary phase at grain boundary. The specimens are subjected to homogenization heat treatment at 410 °C for 24 h; the β-Mg17Al12 phases are significantly dissolved in the matrix grain boundaries which enhance the ductility and decrease the hardness compared with the as-cast materials. The addition of SiCp reinforcement led to improved yield strength (YS) and ultimate tensile strength (UTS) of AZ61/SiCp composite compared to the unreinforced alloy. The maximum values of YS and UTS have been attained at AZ61/1wt%SiCp composites. The enhancement of YS and UTS was due to the presence of a uniformly distributed reinforced SiCp, which depends on grain refinement of the matrix and strong interfacial bonding between the matrix and reinforcement. In the case of fatigue test results, the addition of SiCp reduced the fatigue life and strength of AZ61 alloy composite. However, addition of 1wt%SiCp showed good mechanical and fatigue properties compared to pure AZ61 magnesium alloy and AZ61/2wt%SiCp composite. Furthermore, the effects of addition of SiCp on the mechanical and fatigue properties of the composite were confirmed by using the scanning electron microscope observation of fracture surfaces. [ABSTRACT FROM AUTHOR]

AZ91 reinforced with four different concentrations (0,0.3,0.6,1)wt% of WS 2 micro particles were fabricated using stir casting method. The samples were deformed by equal channel angular pressing (ECAP) after homogenization. The scanning electron microscopy and X-ray diffraction were used to investigate the microstructure and phase composition respectively. The results reveal that rod-like precipitates produced during the homogenization process are refined and bounded in the grain boundaries by the combined effect of WS 2 enrichment and increasing number of passes of ECAP. The needle precipitates are eminent in 1pass 0.3 wt%WS 2 /AZ91. The β-Mg 17 Al 12 and extracted Al particles are dissolved and secondary phases are produced by dynamic recrystallization after 2pass 1 wt%WS 2 /AZ91. The maximum crystallite size and microstrain distribution have been observed for 1pass 0.6 wt%WS 2 /AZ91. The mechanical properties investigation represents that 2pass 0.6 wt%WS 2 /AZ91 has optimal yield strength and ultimate tensile strength. The (22.143)%, (44.735)% and (92) % increment in yield strength, ultimate tensile strength and elongation have been observed in 2pass 1 wt%WS 2 /AZ91 compared with homogenized monolithic AZ91 alloy respectively. The maximum young's modulus (6696.218MPa) has been found for 1pass homogenized WS2/AZ91 and minimum (4108.165MPa) for homogenized 0.6 wt%WS 2 /AZ91. The ECAP deformed 1pass 0.3 wt%WS 2 /AZ91 exhibits the maximum strain hardening rate. The YTS, UTS, and elongation are (30.41) %, (47.6) % and (51.9)% increased after 2pass-0.6 wt%WS 2 /AZ91. [ABSTRACT FROM AUTHOR]

In this work, AZ91 magnesium alloy reinforced with a low fraction (0–1) wt.% tungsten disulfide(WS 2) microparticles have been fabricated using stir casting method. Effects of WS 2 microparticles on mechanical properties, microstructure, and their correlation have been analyzed. The microstructure of composites has been investigated by scanning electron microscope (SEM) equipped with energy dispersive spectroscopy (EDS) and X-ray diffractometer. Results indicate that density, hardness, ultimate tensile strength (UTS), and tensile ductility have a direct relation with reinforcement (WS 2) contents and has optimal value for 0.6 wt% WS 2 /AZ91 composites then slightly decrease afterward. The UTS and hardness of 0.6 wt%WS 2 /AZ91 were increased by 23.23% and 10.65% respectively with respect to monolithic AZ91. The ultimate compressive strength(UCS) is directly related with WS 2 concentration and 10.07% enhancement in UCS for 1 wt%WS 2 /AZ91 composites have been noted. The trend is interlinked with density and hardness of composites. SEM images depict, WS 2 micro-particles suppress β-Mg 17 Al 12 precipitates, refine the microstructure and enhance the grain size resulting in an increase in mechanical properties. The improvement in microstructure and mechanical properties is attributed to the dispersion of WS 2 particles which hinder the grain growth. The increase in porosity has causes the decrease in mechanical behavior of 1 wt%WS 2 /AZ91. Twin boundary fracture has been found major fracture phenomenon in fractured WS 2 /AZ91 surfaces. • WS 2 /AZ91 metal matrix composites have been manufacture by stir casting method. • Density and porosity of WS 2 /AZ91 composites has been assessed. • Mechanical behavior under compression and tension has been analyzed. • Effect of WS 2 on microstructure has been investigated. • Fracture behavior of composites has been studied. [ABSTRACT FROM AUTHOR]