ZnSe and ZnS nanocrystals (NCs) were precipitated in glasses through heat-treatment. High resolution transmission electron microscope image confirmed that ZnSe NCs were formed in the silicate glasses, and the X-ray diffraction patterns confirmed that ZnS NCs were precipitated in the borosilicate glasses. Absorption shoulders of the ZnSe NCs and ZnS NCs appeared at ~ 2.76 eV and ~ 3.78 eV, corresponding to the bandgap energies of bulk ZnSe and ZnS crystals, respectively. Instead of the intrinsic emissions, broad-band visible photoluminescence from the surface defects or color centers in the glasses was observed from these ZnSe or ZnS NCs. [ABSTRACT FROM AUTHOR]

Abstract: Optical properties of PbS quantum dots (QDs) precipitated inside the oxide glass matrix were investigated. Photoluminescence (PL) from the PbS QDs showed peak wavelengths located at 1170–1680nm with widths of 150–550nm. Radii of QDs in glasses were 2.3–4.7nm depending upon the thermal treatment. Peak wavelengths of PL bands shifted as much as 70nm as the temperatures and excitation irradiances increased. Calculated effective local temperatures indicated that these shifts of PL spectra were associated with local heating induced by the temperatures and laser beam. [Copyright &y& Elsevier]

Abstract: PbSe quantum dots (QDs) were synthesized in borosilicate glass and their optical properties were investigated. The typical quantum confinement effects were clearly observed from the absorption when the average radii of the QDs changed from 1.7 to 3.1nm. Photoluminescence from PbSe QDs was achieved in 1.1–2.2μm wavelength region that covers the entire fiber-optic telecommunication window. Borosilicate glasses containing controlled size of PbSe QDs provide potentials for the fiber-optic amplifiers. [Copyright &y& Elsevier]