Search

The fabrication of new membrane that is able to produce stable high power density is essential for the development of pressure retarded osmosis (PRO) technology. In this work, thin film composite (TFC) polyetherimide membranes with three different substrate structures were fabricated and characterized. The PRO performance of the resultant membrane was evaluated through two pressure cycle experiments and stability tests. The primary objective of this work is to systematically study PRO membrane’s mechanical stability and mass transfer properties under high operating pressures, which determine the power density of the membrane in the PRO process. Experiments revealed that water permeability ( A p ) and salt permeability ( B p ) under different pressures varied. The A p and B p are better indicators for examining the variation of PRO membrane structure under pressure. Within the operating pressure range of 17.2 bar, the top polyamide layer of TFC PEI-2# membrane mainly experienced a reversible deformation. In the two pressure cycle tests, the water flux, specific salt flux and power density obtained in the upward and downward measurements in each cycle are close to each other. The first cycle and the second cycle also show excellent reproducibility. The membrane was able to maintain almost unchanged water flux and power density of 12.8 W/m 2 at 17.2 bar over the 10 h testing time, suggesting the membrane’s great potential to be used in practical application in the future. [ABSTRACT FROM AUTHOR]

Abstract: Hollow fiber membranes with a positively charged nanofiltration (NF)-like selective layer have been successfully fabricated by utilizing asymmetric microporous hollow fibers made of Torlon® polyamide–imide (PAI) material as the porous substrate followed by polyelectrolyte post-treatment using polyethyleneimine (PEI), which has not been reported previously. The reaction between PAI and PEI has been confirmed by experiments. The membrane structure and surface property are carefully tailored by adjusting polymer dope composition, spinning conditions and the post-treatment parameters. These membranes are, subsequently, characterized by a series of standard protocols in terms of membrane morphology, structure, permeability and salt rejection, and are applied in forward osmosis (FO) processes. The newly developed PAI hollow fiber membranes show a pure water permeability of 2.19–2.25L/m2 hbar and reasonable NaCl and MgCl2 rejections of 49% and 94% at 1bar, respectively. It is also found that in FO processes, when using 0.5M MgCl2 as a draw solution and DI water as the feed in the active layer facing feed water (AL-facing-FW) configuration at 23°C, the water fluxes of two PAI FO hollow fiber membranes are 8.36 and 9.74L/m2 h, respectively, and the J S /J V of the two membranes is smaller than 0.4g/L, which is lower than the data of 0.85g/L for commercial FO membrane from Hydration Technologies Inc. (HTI). Different from a neutral membrane, the positively charged FO membrane provides double electric repulsions to the salt transfer through the membrane in the AL-facing-FW configuration, leading to a reduction of salt penetration, while in the active layer facing draw solution (AL-facing-DS) configuration, the positive charges facilitate salt transportation. This study provides a simple and effective approach to make hollow fibers suitable for FO applications. [Copyright &y& Elsevier]

A scaled-up hollow fibre thin-film composite (TFC) module was successfully developed for organic solvent forward osmosis (OSFO) application in the pharmaceutical industry. The membrane consists of cross-linked P84 polyimide substrate with a polyamide selective layer, formed via interfacial polymerisation. The performance of the lab-scale module was compared to the scaled-up module in reverse osmosis and forward osmosis modes. The results from both tests revealed that the solvent permeability of the scaled-up module decreased while its selectivity increased slightly. This might be caused by the uneven distribution of liquids during interfacial polymerisation, leading to varied membrane performance. The scaled-up module was further tested for OSFO performance using a range of PEG-400 concentrations (0.5–2 M) in acetone and isopropanol as draw solutions. At 2 M PEG-400 concentration, the module demonstrated high isopropanol and acetone permeability of 0.63 LMH and 13.9 LMH, respectively. Moreover, the reverse solute flux of PEG-400 in acetone and isopropanol were relatively low at 0.188 g/l and 0.153 g/l, respectively. The module was further tested for OSFO application in the pharmaceutical industry by concentrating levofloxacin in acetone, using 2 M PEG-400 as draw solution. The process was able to concentrate levofloxacin from 1000 ppm to 16,000 ppm with very low reverse solute flux of 0.178 g/l. Therefore, this work presents a scalable TFC membrane for OSFO application in the pharmaceutical industry. [Display omitted] • Scaled-up module (0.4 m2) of TFC hollow fibre membrane for organic solvent forward osmosis process was successfully fabricated. • High porosity (79%) and low structural parameter (217 μm) for membrane substrate was achieved. • Membrane exhibited excellent acetone and IPA solvent flux of 13.9 LMH and 0.63 LMH, respectively, using a 2 M PEG-400 draw solution. • A pharmaceutical stream was concentrated to a factor of 16 with low specific reverse solute flux [ABSTRACT FROM AUTHOR]

A scaled-up hollow fibre thin-film composite (TFC) module was successfully developed for organic solvent forward osmosis (OSFO) application in the pharmaceutical industry. The membrane consists of cross-linked P84 polyimide substrate with a polyamide selective layer, formed via interfacial polymerisation. The performance of the lab-scale module was compared to the scaled-up module in reverse osmosis and forward osmosis modes. The results from both tests revealed that the solvent permeability of the scaled-up module decreased while its selectivity increased slightly. This might be caused by the uneven distribution of liquids during interfacial polymerisation, leading to varied membrane performance. The scaled-up module was further tested for OSFO performance using a range of PEG-400 concentrations (0.5–2 M) in acetone and isopropanol as draw solutions. At 2 M PEG-400 concentration, the module demonstrated high isopropanol and acetone permeability of 0.63 LMH and 13.9 LMH, respectively. Moreover, the reverse solute flux of PEG-400 in acetone and isopropanol were relatively low at 0.188 g/l and 0.153 g/l, respectively. The module was further tested for OSFO application in the pharmaceutical industry by concentrating levofloxacin in acetone, using 2 M PEG-400 as draw solution. The process was able to concentrate levofloxacin from 1000 ppm to 16,000 ppm with very low reverse solute flux of 0.178 g/l. Therefore, this work presents a scalable TFC membrane for OSFO application in the pharmaceutical industry. [Display omitted] • Scaled-up module (0.4 m2) of TFC hollow fibre membrane for organic solvent forward osmosis process was successfully fabricated. • High porosity (79%) and low structural parameter (217 μm) for membrane substrate was achieved. • Membrane exhibited excellent acetone and IPA solvent flux of 13.9 LMH and 0.63 LMH, respectively, using a 2 M PEG-400 draw solution. • A pharmaceutical stream was concentrated to a factor of 16 with low specific reverse solute flux [ABSTRACT FROM AUTHOR]

Abstract: Polyamide thin film composite (TFC) membranes with tailored porous substrate and rejection layer are promising for forward osmosis (FO) applications. The current study investigates the effect of rejection layer synthesis conditions on the performance of the resulting TFC polyamide FO membranes. The influence of monomer concentrations (i.e., m-phenylenediamine (MPD) and trimesoyl chloride (TMC) concentrations) on the membrane separation properties as well as FO performance was systematically studied. A strong trade-off between the water permeability and salt rejection was observed, where increasing the TMC concentration or reducing the MPD concentration resulted in higher membrane permeability but lower salt rejection. In FO tests, membranes with poor salt rejection had severe solute reverse diffusion, which enhanced the internal concentration polarization (ICP). It was found that the FO water flux was governed by both the membrane water permeability and its solute rejection. For a membrane with higher water permeability but lower solute rejection, the reduced membrane frictional resistance was compensated by the simultaneously more severe solute-reverse-diffusion-induced ICP. The net effect on the FO water flux depends on the competition of these two opposing mechanisms. Under conditions where solute reverse diffusion may cause severe ICP (e.g., high draw solution concentration and high water flux level), membranes need be optimized to achieve a high salt rejection even if this is at the expense of lower water permeability. [Copyright &y& Elsevier]