Search

Abstract: An electrochemical circuit to record time–temperature history has been realized by using the propagation of over-oxidation fronts in stripes of poly(3,4-ethylenedioxythiopehene) blended with poly(styrenesulfonate) (PEDOT:PSS). The over-oxidation front propagation has been characterized and related to the phase change of polyethylene glycol (PEG) electrolytes. The electrolytes were chosen to have a phase transition in the temperature interval to be monitored, resulting in large conductivity variations and thereby an easily interpreted output. A demonstrator has been fabricated and shown to detect a temperature increase and a following temperature decrease. This very simple device is cheap to produce and could be used to monitor the temperature of packages. [ABSTRACT FROM AUTHOR]

Abstract: Poly(3,4-ethylenedioxythiophene) chemically doped with poly(styrene sulfonic acid) (PEDOT:PSS) is a material system commonly used as a conductive and transparent coating in several important electronic applications. The material is also electrochemically active and exhibits electrochromic (EC) properties making it suitable as the active element in EC display applications. In this work uniformly coated PEDOT:PSS layers were used both as the pixel electrode and as the counter electrode in EC display components. The pixel and counter electrodes were separated by a whitish opaque and water-based polyelectrolyte and the thicknesses of the two EC layers were varied independently in order to optimize the color contrast of the display element. A color contrast (ΔE ∗, CIE L ∗ a ∗ b ∗ color space) exceeding 40 was obtained with maintained relatively short switching time at an operational voltage less than 2V. [Copyright &y& Elsevier]

Advances in organic electronics necessitates, ultrathin and miniaturized implantable energy storage modules. Here, an approach for the fabrication of on-chip, ultraflexible electrochemical capacitors is demonstrated. Two different electroactive conjugated polymers are utilized in a fabrication route that allows the patterning of finger electrodes for an ultraflexible energy storage technology. A strategy is demonstrated to realize supercapacitors with a total device thickness of 4 μm, including substrate, polymer electrode, and electrolyte. Interdigitated 20-finger electrodes from either Poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) or polythiophene functionalized with tetraethylene glycol side chains P(g42T-T), with 50 μm or 90 μm electrode spacings, are fabricated using a parylene peel off method, followed by electrolyte deposition. The miniaturized devices show 0.77 mF/cm2 areal capacitance for PEDOT:PSS and 0.06 mF/cm2 for P(g42T-T). Furthermore, the devices exhibit excellent mechanical durability, showing robust operational performance at a bending radius of 6.5 mm. [Display omitted] • Scalable fabrication route for polymer IDE structures using parylene peel off method. • PEDOT:PSS and P(g42T-T) microsupercapacitors with more than 0.6 mF/cm2 capacitance. • Ultrathin organic electronics device technology with total thickness of 4 μm. • Excellent mechanical durability, showing robust operational performance at a bending radius of 6.5 mm. [ABSTRACT FROM AUTHOR]

Polyelectrolytes are promising electronicallyinsulating layers for low-voltage organic field effect transistors.However, the polyelectrolyte–semiconductor interface is difficultto manufacture due to challenges in wettability. We introduce an amphiphilicsemiconducting copolymer which, when spread as a thin film, can changeits surface from hydrophobic to hydrophilic upon exposure to water.This peculiar wettability is exploited in the fabrication of polyelectrolyte-gatedfield-effect transistors operating below 0.5 V. The prepared amphiphilicsemiconducting copolymer is based on a hydrophobic regioregular poly(3-hexylthiophene)(P3HT) covalently linked to a hydrophilic poly(sulfonated)-based randomblock. Such a copolymer is obtained in a three-step strategy combiningGrignard metathesis (GRIM), atom transfer radical polymerization (ATRP)processes, and a postmodification method. The structure of the diblockcopolymer was characterized using FT-IR, 1H NMR spectroscopy,and gel permeation chromatography (GPC). [ABSTRACT FROM AUTHOR]