Search

The adsorption of hydrogen, ethylene, acetylene, cyclohexane and benzene was studied on both the (111) and stepped [6(111) × (100)] crystal surfaces of iridium. The techniques used were low energy electron diffraction, Auger electron spectroscopy, and thermal desorption mass spectrometry. At 30°C, acetylene, ethylene and benzene are adsorbed with a sticking probability near unity. The sticking probability of cyclohexane is less than 0.1 on both surfaces. Heating the (111) surface above 800°C, in the presence of the hydrocarbons, results in the formation of an ordered carbonaceous overlayer with a diffraction pattern corresponding to a (9 × 9) surface structure. No indication for ordering of the carbonaceous residue was found on the stepped iridium surface in these experimental conditions. The hydrocarbon molecules form only poorly ordered surface structures on both iridium surfaces when the adsorption is carried out at 30°C. Benzene is the only gas that can be desorbed from the surfaces in large amounts by heating. Ethylene remains largely on the surface, only a few percent is removed by heating while acetylene and cyclohexane cannot be desorbed at all. When adsorption is carried out at 30°C and the crystal is subsequently flashed to high temperature, hydrogen is liberated from the surface. The hydrogen desorption spectra from the iridium surfaces exposed to C2H4, C2H2, or C6H6 exhibit two hydrogen desorption peaks, one around 200°C and the second around 350°C. The temperatures where these peaks appear vary slightly with the type of hydrocarbon. The relative intensities of these two peaks depend strongly on the surface used. Arguments are presented that decomposition of the hydrocarbon molecules (C-H bond breaking nd possibly also C-C bond breaking) occurs easier on the stepped iridium surface than on the (111) surface. Hydrogen is desorbed at a higher temperature from an iridium surface possessing a high density of surface imperfections than from a perfect iridium (111) surface. The results are compared with those obtained previously on similar crystal surfaces of platinum. It appears that C-H bond breaking occurs more easily on iridium than on platinum.

The adsorption of CO, O2, and H2O was studied on both the (111) and [6(111) × (100)] crystal faces of iridium. The techniques used were LEED, AES, and thermal desorption. Marked differences were found in surface structures and heats of adsorption on these crystal faces. Oxygen is adsorbed in a single bonding state on the (111) face. On the stepped iridium surface an additional bonding state with a higher heat of adsorption was detected which can be attributed to oxygen adsorbed at steps. On both (111) and stepped iridium crystal faces the adsorption of oxygen at room temperature produced a (2 × 1) surface structure. Two surface structures were found for CO adsorbed on Ir(111); a (√3 × √3)R30° at an exposure of 1.5–2.5 L and a (2√3 × 2√3)R30° at higher coverage. No indication for ordering of adsorbed CO was found on the Ir(S)-[6(111) × (100)] surface. No significant differences in thermal desorption spectra of CO were found on these two faces. H2O is not adsorbed at 300 K on either iridium crystal face. The reaction of CO with O2 was studied on Ir(111) and the results are discussed. The influence of steps on the adsorption behaviour of CO and O2 on iridium and the correlation with the results found previously on the same platinum crystal faces are discussed.