Search

The present study investigates the influence of organic acids, added to the electrolytic solution, on the structure, morphology, and corrosion behaviour of plasma electrolytic oxidation (PEO) coatings produced on titanium grade 2. Particular attention is paid to the role of functional groups in the modification of the oxide's properties. For this reason, all three selected acids, namely glutaric, glutamic, and tartaric acid, display two carboxylic groups, thus they interact with the substrate material mainly through –COO− adsorption. However, glutamic acid also has an amine group, while tartaric acid has two hydroxyl groups. The presence of such additional functional groups is found to impact the formation of the PEO coatings. According to scanning electron microscopy (SEM) analyses, the number of defects and their dimension increase with an increasing number of active groups present in the organic molecules. Then, when glutaric acid with only two carboxyl groups, is employed as an additive, smaller pores are produced. The dimension of defects increases when glutamic and tartaric acid are used. X-ray diffraction (XRD) testing demonstrates that rutile and anatase are present in all the coatings and that when using tartaric acid, a relatively high level of amorphism is reached. The electrochemical and corrosion behaviours are evaluated by potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) performed in a heated sulphuric acid solution. It is found that all types of coatings provide protection against corrosion, with oxides produced using glutamic acid showing the lowest corrosion current density (0.58 mA·m−2) and low corrosion rate (1.02 μm·y−1). [ABSTRACT FROM AUTHOR]

Inhibitors for the prevention of corrosion in reinforced concrete are chemical substances able to reduce carbon steel reinforcements corrosion without altering the overall properties of concrete. Today, many commercially available substances have a negative impact on human safety during either the inhibitor synthesis, their handling or application in field. Green corrosion inhibitors are nontoxic, biodegradable and environmentally biocompatible substances. They are generally made of extracts from natural plants or waste, which are abundantly available in several countries. The majority of green inhibitor molecules usually contain multiple bonds, aromatic rings, polar functional groups and electronegative atoms as P, N, S or O; the latter are able to coordinate with metal cations to form protective layers on the metallic surface of the reinforcements, so as to inhibit the development (initiation and/or propagation) of the corrosion process. In this review, the most recent achievements on the study and investigation of green corrosion inhibitors for concrete structures are presented and discussed. Inhibitors are classified based on their nature and inhibition mechanism. The inhibition effectiveness of the substances is compared with the well-established effective nitrite-based inhibitor, distinguishing between accelerated and long-term tests. Based on the available data, a summary of corrosion inhibitors efficiency is reported. [ABSTRACT FROM AUTHOR]

This research describes the influence of two types of particles, namely rutile and anatase microparticles (average d < 5 µm), on the morphology, structure, and anticorrosive properties of PEO coatings on titanium produced in an alkaline solution based on NaOH and sodium metasilicates. The paper reports the experimental results relating to the study of the influence of the electrical regime and working frequency of the anodizing treatment on the interaction between the particles, the substrate, and the oxide to determine the optimal conditions that favour the incorporation of the particles and the production of a thick oxide. PEO coatings are characterized by using a scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) analysis, and X-ray diffraction (XRD) testing. The electrochemical behaviour is evaluated by free corrosion potential monitoring and electrochemical impedance spectroscopy analysis (EIS) performed in a sulphuric acid solution. The particles are successfully incorporated into the coating under any electrical condition and at any frequency. However, only treatments carried out at 1000 Hz allow the production of coatings that combine a large thickness (up to 50 µm) and improved anticorrosion behaviour. In contrast, oxide layers produced at 20 Hz and in DC show a quite damaged structure, affecting their anticorrosion behaviour and resulting in lower corrosion potential and impedance values. [ABSTRACT FROM AUTHOR]

This study deals with the anodisation of titanium grade 2 in 0.5‐M sulphuric acid using a pulsed signal in a unipolar regime. The electrical parameters investigated are voltage, frequency and duty cycle. The use of duty cycles with a high percentage of anodic polarisation (90%), combined with high frequencies (1000 Hz) and the higher voltage tested (220 V), favoured the establishment of a plasma regime involving strong dielectric discharges, allowing the growth of thicker oxides but with rough architecture. The corrosion resistance of the formed film has been characterised by potentiodynamic tests in 0.5‐M NaBr for localised corrosion resistance and by immersion tests in 10% v/v sulphuric acid solution for a uniform corrosion assessment. Current–time curves, visual observations and electron microscope analysis (scanning electron microscopy, energy‐dispersive X‐ray spectroscopy) were the tools selected to provide a correlation between technological parameters and oxide growth mechanism. For localised and uniform corrosion, anodisation at 220 V with a high level of anodic polarisation (90%) and frequency (1000 Hz) was verified to be particularly advantageous. [ABSTRACT FROM AUTHOR]