Search

Purpose: To investigate the effect of Colloidal Platinum Nanoparticles (CPN) on the bond strength between dentin and 4-META/MMA-TBB resin using different concentrations of CPN. Materials and Methods: Twenty-five extracted human third molars were stored in 0.5% chloramine T. The occlusal dentin slices were prepared by grinding occlusal surfaces of each tooth and polishing with 600-grit silicon carbide paper under running water. One control and four experimental groups (2 specimens per group) were used as follows: a) dentin surfaces treated with 10-3 solution, followed by rinsing with water and subsequently an acrylic rod bonded with hand-mixed 4META/MMA-TBB resin (Super-Bond C&B, Sun Medical) (control); b) dentin surfaces treated with 10-3 etching solution, followed by rinsing with water and application of CPN (100% or 10%) as a primer solution for 60 s and rinsed with water for 20 s, then an acrylic rod bonded with Super-Bond C&B(Etch-CPN [100% or 10%]); c) dentin surfaces treated with CPN (100% or 10%) for 60 s, rinsed with water for 20 s, followed by application of 10-3 solution, then an acrylic rod bonded with Super-Bond C&B (CPN-Etch [100% or 10%]). After storage in 37°C water, specimens were sectioned into beams (cross-sectional area: 1 mm2) for microtensile bond strength testing at a crosshead speed of 1mm/min. The data were analyzed using the Games-Howell method (p < 0.05; n = 15). Results: Etch-CPN (100), CPN-Etch(100) and CPN-Etch (10) showed significantly higher bond strengths compared to the control. When using 10% CPN, the highest bond strength was demonstrated. The bond strength of 4META/MMA-TBB resin was approximately doubled by CPN application. Conclusion: The results of this study showed that higher bond strengths are obtained when treating dentin with a lower concentration of CPN. Further evaluation to optimize conditions such as the application time and rinsing time are required. [ABSTRACT FROM AUTHOR]

Purpose: To morphologically evaluate the interface between a conventional glass-ionomer cement (GIC) and dentin one day after placement, as well as the changes at the interface after one year of aging/functioning in monkey teeth., Materials and Methods: On the buccal surfaces of seven intact teeth in each of two monkeys, shallow class V cavities were prepared, which were then filled with Fuji IX GP (GC) to provide 1-year in vivo data. A year later, two more teeth in each monkey were similarly prepared and restored for the 1-day in vivo group. The following day, the restored teeth were extracted and the restoration interfaces observed using transmission electron microscopy (TEM). In addition, restorations were similarly placed in two extracted human teeth (control, 1-day in vitro group) and observed a day after placement using TEM., Results: The 1-day in vivo and in vitro results showed that the GIC appeared to bond to dentin through a demineralized zone similar to the hybrid layer produced by resinous adhesives. However, the interface between GIC and dentin after 1 year in vivo appeared to change over time: many needle-like crystals were detected within the remineralized layer and along the collagen fibrils. Slow diffusion of ions resulted in pores, which filled with mineral crystals and made the pores smaller., Conclusion: The interface between GIC and dentin morphologically changes over time, and recrystallization or remineralization at the interface may occur (1 year in vivo).

Purpose: To evaluate the hydrolytic stability of three one-step self-etching adhesives (1-SEAs) bonded to dentin through bond strength testing and ultra-morphological interfacial analysis before and after long-term thermocycling., Materials and Methods: Eighteen flattened mid-coronal dentin surfaces of extracted human molars were subjected to bonding treatment using three 1-SEAs (Clearfil S3 Bond, Kuraray (S3), G-Bond, GC (GB), Absolute, Dentsply-Sankin (AB)), after which the bonded surfaces were built up with composite. After storage overnight at 37°C, the specimens were sectioned into slabs and further trimmed into an hourglass shape with an interface area of approximately 1 mm2. The specimens were left untouched (control) or were thermocycled for 100,000 cycles. The microtensile bond strength (μTBS) was measured and the ultrastructure of the adhesive/dentin interface characterized using transmission electron microscopy (TEM)., Results: Long-term thermocycling significantly decreased the μTBS of all one-step adhesives tested (p < 0.05, one way ANOVA and Games-Howell test). TEM revealed a similar interfacial ultrastructure before and after thermocycling for S3. For GB, many voids were observed at the interface after 100,000 thermocycles. Regarding AB, collagen fibrils could no longer be clearly observed upon staining, while the adjacent unaffected dentin was rich in voids., Conclusion: The bond strength and ultramorphological data demonstrated that the bond of 1-SEAs to dentin degrades with time, although the degree of degradation is obviously material dependent.