Search

Defect‐engineering is a viable strategy to improve the activity of nanocatalysts for the oxygen evolution reaction (OER), whose slow kinetics still strongly limits the broad market penetration of electrochemical water splitting as a sustainable technology for large‐scale hydrogen production. High‐entropy spinel oxides (HESOs) are in focus due to their great potential as low‐cost OER electrocatalysts. In this work, electrospun HESO nanofibers (NFs), based on (Cr,Mn,Fe,Co,Ni), (Cr,Mn,Fe,Co,Zn) and (Cr,Mn,Fe,Ni,Zn) combinations, with granular architecture and oxygen‐deficient surface are produced by calcination at low temperature (600 or 500 °C), characterized by a combination of benchtop analytical techniques and evaluated as electrocatalysts for OER in alkaline medium. The variation of HESO composition and calcination temperature produces complex and interdependent changes in the morphology of the fibers, crystallinity and inversion degree of the spinel oxide, concentration of the oxygen‐vacancies, cation distribution in the lattice, which mirror on different electrochemical properties of the fibers. The best electrocatalytic performance (overpotential and Tafel slope at 10 mA cm−2: 360 mV and 41 mV dec−1, respectively) pertains to (Cr1/5Mn1/5Fe1/5Co1/5Ni1/5)3O4 NFs calcined at 500 °C and results from the lower outer 3d‐electron number, eg filling closer to its optimal value and higher occupation of 16d sites by the most redox‐active species. [ABSTRACT FROM AUTHOR]

We report CNT/Al2O3 core–shell nanostructures for the electrochemical detection of dihydroxybenzene (DHB) isomers. Amorphous films of Al2O3 (1.2–15.4 nm in thickness) are uniformly deposited onto the inner and outer walls of CNTs by atomic layer deposition. The effect of the Al2O3 shell thickness on the electrochemical detection of dihydroxybenzene isomers was explored using cyclic and square-wave voltammetry. The best sensing properties are found at a shell thickness of approx. 2.4 nm (CNT/Al2O3(9) sensor), where the oxidation peak currents (sensor-signal) increased ca. 10 times as compared to a sensor fabricated with non-coated CNTs. All of the three DHB isomers (hydroquinone, catechol and resorcinol) are independently detected in the concentration ranges of 2–1000 μmol L−1, 0.5–700 μmol L−1 and 3.5–500 μmol L−1, respectively. The sensors show reliable repeatability, reproducibility, long-term stability, and applicability in the analysis of real samples. Based on these findings, a plausible mechanism is proposed highlighting the role of the Al2O3–shell. [ABSTRACT FROM AUTHOR]

We report CNT/Al2O3 core-shell nanostructures for the electrochemical detection of dihydroxybenzene (DHB) isomers. Amorphous films of Al2O3 (1.2-15.4 nm in thickness) are uniformly deposited onto the inner and outer walls of CNTs by atomic layer deposition. The effect of the Al2O3 shell thickness on the electrochemical detection of dihydroxybenzene isomers was explored using cyclic and square-wave voltammetry. The best sensing properties are found at a shell thickness of approx. 2.4 nm (CNT/Al2O3(9) sensor), where the oxidation peak currents (sensor-signal) increased ca. 10 times as compared to a sensor fabricated with non-coated CNTs. All of the three DHB isomers (hydroquinone, catechol and resorcinol) are independently detected in the concentration ranges of 2-1000 μmol L-1, 0.5-700 μmol L-1 and 3.5-500 μmol L-1, respectively. The sensors show reliable repeatability, reproducibility, long-term stability, and applicability in the analysis of real samples. Based on these findings, a plausible mechanism is proposed highlighting the role of the Al2O3-shell.