In this paper, the systematic evolution process of self-assembled Au droplets is successfully demonstrated on GaAs (111)A, (110), (100), and (111)B. On various GaAs substrates, self-assembled Au clusters begin to nucleate at around 300°C, and then, they develop into wiggly Au nanostructures at 350°C. Between 400°C and 550°C, the self-assembled dome-shaped Au droplets with fine uniformity are fabricated with various sizes and densities based on the Volmer-Weber growth mode. Depending on the annealing temperature, the size including the average height and lateral diameter and the density of Au droplets show the opposite trend of increased size with correspondingly decreased density as a function of the annealing temperature due to the difference in the diffusion length of adatoms at varied activation energy. Under an identical growth condition, depending on the surface index, the size and density of Au droplets show a clear distinction, observed throughout the temperature range. The results are systematically analyzed and discussed in terms of atomic force microscopy (AFM) images, cross-sectional line profiles, and Fourier filter transform (FFT) power spectra as well as the summary plots of the size and density. [ABSTRACT FROM AUTHOR]

The fabrication of self-assembled Au droplets is successfully demonstrated on various GaAs ( n11)B, where n is 2, 4, 5, 7, 8, and 9, by the systematic variation of the Au deposition amount (DA) from 2 to 12 nm with subsequent annealing at 550°C. Under an identical growth condition, the self-assembled Au droplets of mini to supersizes are successfully synthesized via the Volmer-Weber growth mode. Depending on the DA, an apparent evolution is clearly observed in terms of the average height (AH), lateral diameter (LD), and average density (AD). For example, compared with the mini Au droplets with a DA of 2 nm, AH of 22.5 nm, and LD of 86.5 nm, the super Au droplets with 12-nm DA show significantly increased AH of 316% and LD of 320%, reaching an AH of 71.1 nm and LD of 276.8 nm on GaAs (211)B. In addition, accompanied with the dimensional expansion, the AD of Au droplets drastically swings on 2 orders of magnitudes from 3.2 × 10 to 4.2 × 10 cm. The results are systematically analyzed with respect to the atomic force microscopy (AFM) and scanning electron microscopy (SEM) images, energy-dispersive X-ray spectrometry (EDS) spectra, cross-sectional line profiles, Fourier filter transform (FFT) power spectra, and root-mean-square (RMS) roughness as well as the droplet dimension and density summary, respectively. [ABSTRACT FROM AUTHOR]