Search

Chemical modification of the surface of halloysite nanotubes (HNT) by alkalization (with sodium hydroxide (NaOH)) and grafting with silanes (bis(trimethylsilyl)amine (HMDS)) was carried out. The efficiency of the alkalization and grafting process was evaluated by X–ray diffraction (XRD), Fourier–transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and the nitrogen adsorption method were used. XRD and FTIR analysis confirmed the formation of bonds of trimethylsilyl groups to the HNT surface which changed the nature of the surface from hydrophilic to hydrophobic. In addition, it was noted that grafting with silanes decreases by 7.2% the specific surface area of the halloysite compared to the alkalized material. High–density polyethylene (HDPE) composites with halloysite (HNT), alkalized halloysite (alk–HNT), and HMDS–modified halloysite (m–HNT) were processed in the molten state in a Brabender mixer chamber. On SEM/EDS micrographs of HDPE composites with silanized HNT, a change in surface characteristics from smooth to ductile was observed. Higher melting point values based on differential scanning calorimetry (DSC) analysis of HDPE composites with 5%wt silanized halloysite in comparison with HNT and alk–HNT of, respectively, 2.2% and 1.4% were found, which indicates a slight beneficial influence of the filler on the quality of ordering of the crystalline phase of the matrix. [ABSTRACT FROM AUTHOR]

The article presents research on the thermal decomposition of individual ingredients and compositions that are physical mixtures of emulsion poly(vinyl chloride) (PVC), cadmium yellow, and stearic acid. The results of the tests were TG, DTA, and DTG graphs. From their course, the initial decomposition temperatures, maximum decomposition rate, and final temperatures were determined, and changes in the mass of samples and the values of thermal effects were calculated. The influence of pigment and stearic acid on the thermal decomposition of PVC was investigated. Cadmium yellow, modified in an alkaline medium and containing hydroxyl groups, was also used for the tests. It was found that the presence of both pigment and stearic acid had a retarding effect on the initiation of thermal decomposition of PVC. The addition of CdS modified in an alkaline environment had a more or less similar effect on the initial decomposition temperature of PVC. Depending on the composition of the polymer and the value of the final temperature, different values of thermal effects and the amount of products formed were indicated. [ABSTRACT FROM AUTHOR]

Copyright of Polimery is the property of Industrial Chemistry Research Institute and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

The results of a study on latexes obtained by emulsion copolymerization of acrylic, methacrylic and vinyl monomers without surfactants are presented. The monomers included ethyl acrylate and butyl acrylate, methyl and butyl methacrylate and methacrylic acid. The yield of the copolymerization reaction, the polymer concentration in the latex, the pH, surface tension, intrinsic viscosity number, Huggins constant, the molecular weight of the polymer and the particle size in the latex were determined. The stability of the latexes was tested by determining the values of non‐overt and overt coagulation thresholds. The values of the limiting equivalent conductivity and the anode zeta potential were determined. The relative hardness of latex membranes and their mass change after hot water extraction were investigated. The relationships between the properties of individual latexes were established. The main aim of the research was to determine the influence of copolymer composition on the electrokinetic properties of polymer particles in latex. They determine the possibility of developing a new type of paint for electrophoretic painting with the use of latexes. © 2022 Society of Industrial Chemistry. [ABSTRACT FROM AUTHOR]

The modification of poly(vinyl chloride) (PVC) by polyhedral silsesquioxane containing both methacryl and octyl groups (MeOctPOSS) was the task of studies. The PVC nanocomposites with MeOctPOSS concentration between 1 and 10 wt% were prepared by melt mixing processing, and the homogeneity of MeOctPOSS dispersion in the polymeric matrix was confirmed by scanning electron microscopy and energy dispersive spectroscopy observations. The influence of MeOctPOSS on glass transition temperature (Tg) determined by means of dynamic mechanical thermal analysis (DMTA) and differential scanning calorimetry (DSC) was observed, whereas, higher the measurement frequency, higher the glass transition temperature was noted. The MeOctPOSS concentration‐dependent PVC glass transition temperature was shifted from 73.8°C to about 68°C (ƒ = 1 Hz) and from 76.5°C to 70.8°C (ƒ = 10 Hz) for increasing additive content. Similar result of decreasing Tg value was observed by DSC method. An introduction of 10 wt% of MeOctPOSS into the PVC matrix results in a visible decrease of the maximum value of loss modulus (G′) of approximately 12% and 18% by 1 Hz and 10 Hz, respectively, as well as in a significant reduction of the static elastic modulus. It was stated that the polyhedral oligomeric silsesquioxanes with both methacryl and octyl groups may act as plasticizers of the PVC matrix. J. VINYL ADDIT. TECHNOL., 25:E48–E54, 2019. © 2018 Society of Plastics Engineers [ABSTRACT FROM AUTHOR]

Copyright of Polimery is the property of Industrial Chemistry Research Institute and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Copyright of Polimery is the property of Industrial Chemistry Research Institute and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

This study investigates the effects of the addition of tungsten on the structure, phase composition, textural properties and activities of β-SiC-based catalysts in the aqueous phase hydrogenation of furfural. Carbothermal reduction of SiO2 in the presence of WO3 at 1550 °C in argon resulted in the formation of WxC-β-SiC nanocomposite powders with significant variations in particle morphology and content of WxC-tipped β-SiC nano-whiskers, as revealed by TEM and SEM-EDS. The specific surface area (SSA) of the nanocomposite strongly depended on the amount of tungsten and had a notable impact on its catalytic properties for the production of furfuryl alcohol (FA) and tetrahydrofurfuryl alcohol (THFA). Nanocomposite WxC-β-SiC catalysts with 10 wt % W in the starting mixture had the highest SSA and the smallest WxC crystallites. Some 10 wt % W nanocomposite catalysts demonstrated up to 90% yield of THFA, in particular in the reduction of furfural derived from biomass, although the reproducible performance of such catalysts has yet to be achieved. [ABSTRACT FROM AUTHOR]

A functional magnesium hydroxide/lignin hybrid system was prepared by grinding and mixing the pure precursors using a planetary ball mill. In addition, the thermal stability was assessed based on the total mass loss of the hybrid system within the temperature range of 30-1000 °C, which amounted to 38%. Moreover, the average particle size was at 4.9 μm as determined by the laser diffraction method. The effect of addition of the prepared and characterized Mg(OH)2/lignin hybrid filler at concentrations ranging from 2.5 wt % to 10 wt % on the processing as well as mechanical and thermal properties of composites on the matrix of the unplasticized PVC compound was also evaluated. The addition of a filler to the poly(vinyl chloride) matrix causes a significant improvement of its thermal stability, which is approximately three times higher compared to a polymer without a filler. Furthermore, the prepared composites are additionally characterized by advantageous mechanical properties, especially higher Young's modulus. A 10% increase in the oxygen index of PVC composites upon addition of 10 wt % hybrid fillers has also been observed, which contributes to an extended range of their application under conditions that require notable fire resistance. [ABSTRACT FROM AUTHOR]

Copyright of Polimery is the property of Industrial Chemistry Research Institute and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)