The failure mode is a dominant factor of mechanical performance of braided composite tube subjected to axial compression. The failure mode was modified by tailoring stack-up sequence of composite tubes hybridized by bi/tri-axial braided laminate. The thermal photographing and micro-CT scanning methods were employed to monitor the in-situ damage progression and post-mortem specimen, respectively. The results show that the delamination was easy to be induced at the interface nearby tri-axial braided laminate. It attributes to the combination between the crack caused by local buckling of the axial yarns and the crack caused by shear deformation of braiding yarns. By the illumination of this behavior, delamination is controlled to occur at the different position along thickness direction of braided tube by adjusting the stacking sequence of braided laminates. When delamination position transfer from the inner/outer sides to the middle of tube wall, the failure mode transfer from the progressive folding to splaying, which increase the specific energy absorption by 45.77%. [ABSTRACT FROM AUTHOR]

Accurately identifying various meso-morphological features and sub-phases within the damaged braided composite fabric is crucial for assessing the mechanical properties of composites under complex loading conditions and different processing parameters. However, obtaining 3D reconstructions that can be quantitatively analyzed is still a challenge, primarily due to the low contrast of the meso-morphological features (yarn tow and matrix crack networks). In this work, a new data enhancement algorithm is proposed to generate a realistic-looking artificial training dataset for enriching the information of the meso-morphological features. Then, the effect of various training networks and training parameters (the size of real and hybrid training dataset, number of epochs) on segmentation performance were examined. Finally, the meso-morphological features were statistically analyzed to accurately evaluate the mechanical properties of the composite material. The work presented here provides an effective tool that enables the quantitative analysis of the dynamic crack evolution process under the axial load of the composite materials. [Display omitted] [ABSTRACT FROM AUTHOR]