Search

Indium tin oxide (ITO) has important application in photoelectronic and photonic devices, demanding effective approach and appropriate parameters to modulate the ITO properties. The effects of laser annealing at 1064 nm with different pulse width (875 ps, 10 ns, and 300 ns) on optical and nonlinear optical properties of ITO films were investigated. Compared with 875 ps and 10 ns, laser annealing at 300 ns significantly improved the near-infrared transmittance of ITO films. The change arises from the elimination of oxygen vacancies and reduction of tin oxides, resulting in the decrease of carrier concentration. Finite element simulations indicate that laser annealing with pulse width of 875 ps and 10 ns have high instantaneous peak temperatures of 1128.5 K and 783 K, respectively, while the temperature accumulation between pulses is negligible. On the contrary, the laser annealing with a pulse width of 300 nshas lower peak transient temperature of 343 K but high static residence temperature of 973 K. The results reveal that the modification of ITO films depends more on the static average temperature rather than the instantaneous peak temperature. The modulation of carrier dynamics in both amplitude and temporal domain was demonstrated after 300 ns laser annealing, achieving ultrafast transient response approximately 150 fs. This work provides theoretical and experimental basis for us to select suitable laser conditions for directional annealing of ITO film to make it suitable for the applications of broad optical spectrum photovoltaic devices or ultrafast optical exchange for high-speed data processing. • Laser annealing (LA) is shown for three pulse widths at approximately 0.2 J/cm2. • LA at 300 ns significantly improves the near-infrared transparency due to the reduction of carrier absorption. • Tailorable amplitude and time scale of carrier transient response are achieved by LA, with ultrafast response time 150 fs. • The modification of ITO properties depends on the static temperature rather than transient peak temperature. [ABSTRACT FROM AUTHOR]

Liquid crystal polarization gratings (LCPGs) possess unique optical properties and therefore are widely used in laser systems. Therefore, developing our understanding of the laser damage resistance of LCPGs is critical for future high-intensity laser applications. In this study, the LCPGs (Λ = 8 μm) were fabricated from liquid crystal polymer (LCP) films with photo-alignment technology, which had a small-angle (∼7.51°) diffraction order with high diffraction efficiency (∼92 %) under chiral polarized incidence at 1064 nm. The diffraction efficiency and polarization of each diffraction order were determined by the polarization of the incident light. The damage characteristics of the LCPGs were investigated using a chiral polarized nanosecond laser at 1064 nm in a one-on-one test. The laser-induced damage thresholds (LIDTs) of left-handed circular polarization (LHCP) and right-handed circular polarization (RHCP) were 8.0 J/cm2 and 8.5 J/cm2, respectively. For comparison, the LIDTs of S-polarization and P-polarization were 7.8 J/cm2 and 8.4 J/cm2, respectively. All the damage occurred at the interface between the LCP layer and the substrate when the laser fluence was near the LIDT, and the damage morphology was observed with a scanning electron microscope (SEM), including flat pits, cracks, and bumps at the edge of the pits. The results indicate that the LIDTs and damage morphology of the LCPGs were insensitive to the polarization of the irradiation. The electrical effects of differently polarized irradiation on the LCPGs were simulated using the finite element method (FEM). The electric field distribution was symmetrical under irradiation by LHCP and RHCP lasers. However, the distribution of the electric field under different linearly polarized irradiation conditions were distinct. Based on these findings, we believe that the contribution of chiral polarized irradiation to the damage was consistent and that the LIDTs were similar. This study has important implications for the application and development of LCPGs in high-intensity laser systems. • The laser-induced damage of liquid crystal polarization gratings (LCPGs) is first proposed. • We investigated the laser-induced damage of the LCPGs using a nanosecond pulsed laser with chiral polarized irradiation. • This study provides reference for the application and development of LCPGs in high-intensity laser systems. [ABSTRACT FROM AUTHOR]