Search

In this work, we fabricated a polycrystalline Tb2FeCrO6 double perovskite (DP) oxide by a solid-state reaction method and determined its structural, magnetic, and magnetocaloric (MC) properties. The Tb2FeCrO6 DP oxide was found to crystallize in a DP-type structure with the Pbnm space group and to undergo a paramagnetic-to-antiferromagnetic transition at a temperature of ~ 8.5 K. A large low-temperature MC effect was observed in the Tb2FeCrO6 DP oxide. The MC parameters in terms of maximum magnetic entropy changes, temperature-averaged entropy change (5 K), and relative cooling power for Tb2FeCrO6 DP oxide under a magnetic field change of 0–7 T were 12.9 J/kg K, 12.7 J/kg K, and 341.4 J/kg, respectively. These parameters were consistent with similarly high levels in recently updated MC materials, making the material a suitable candidate for low-temperature magnetic cooling applications. [ABSTRACT FROM AUTHOR]

We herein investigated four rare earth (RE)-based oxides, the RE 2 SiO 5 (RE = Gd, Dy, Ho, and Er) silicates, regarding their structural and cryogenic magnetic properties. All the RE 2 SiO 5 silicates are found to crystallized in a monoclinic structure. X-ray photoemission spectroscopy spectra illustrate that RE , Si and O elements in RE 2 SiO 5 silicates are present as RE 3+, Si4+, and O2−, respectively. The Dy 2 SiO 5 reveals a first-order magnetic transition around 4.5 K. The magnetic phase transition temperatures are probably below 2 K for the RE 2 SiO 5 (RE = Gd, Ho, and Er) silicates. Large cryogenic magnetocaloric effects (MCE) and good magnetocaloric performances were observed in the RE 2 SiO 5 silicates. The MCE parameters in terms of the maximum magnetic entropy changes, the temperature-averaged entropy change (5 K-lift) and refrigerant capacity under a magnetic field change of 0–5 T are determined to be 35.5, 30.4 J/kgK, and 215.7 J/kg for Gd 2 SiO 5 , to be 13.3, 12.9 J/kgK, and 190.5 J/kg for Dy 2 SiO 5 , to be 15.3, 15.1 J/kgK, and 274.1 J/kg for Ho 2 SiO 5 and to be 17.9, 16.5 J/kgK, and 181.14 J/kg for Er 2 SiO 5 , respectively. These derived values of MCE parameters of the RE 2 SiO 5 silicates, especially for Gd 2 SiO 5 , are at similarly high level with or better than those of the updated candidate materials, making them also of potential for practical magnetic refrigeration applications. [ABSTRACT FROM AUTHOR]

• The RE 2 Ga 2 Mg (RE = Tm, Er, Ho) compounds were fabricated. • The magnetic and magnetocaloric properties were investigated. • Large conventional and inverse magnetocaloric effects were observed. • The Tm 2 Ga 2 Mg is considerable for cryogenic magnetic cooling. The Mo 2 FeB 2 -type compounds RE 2 Ga 2 Mg (RE = Tm, Er, Ho) (space group P 4/ mbm) exhibit a large magnetocaloric (MC) effect which makes them promising for use in cryogenic magnetic cooling applications. They exhibit low temperature metamagnetic nature below their Néel temperatures of 6.8, 11.7 and 18.4 K for Tm 2 Ga 2 Mg, Er 2 Ga 2 Mg and Ho 2 Ga 2 Mg, respectively. The magnetic entropy change, the temperature-averaged entropy change (3 K-lift), and the relative cooling power under a magnetic field change of 0–7 T are 15.6, 15.4 J/kgK and 275.8 J/kg for Tm 2 Ga 2 Mg; 13.2, 13.0 J/kgK and 268.0 J/kg for Er 2 Ga 2 Mg; as well as 9.1, 9.0 J/kgK and 223.0 J/kg for Ho 2 Ga 2 Mg, respectively. [ABSTRACT FROM AUTHOR]