Search

Indium tin oxide (ITO) has important application in photoelectronic and photonic devices, demanding effective approach and appropriate parameters to modulate the ITO properties. The effects of laser annealing at 1064 nm with different pulse width (875 ps, 10 ns, and 300 ns) on optical and nonlinear optical properties of ITO films were investigated. Compared with 875 ps and 10 ns, laser annealing at 300 ns significantly improved the near-infrared transmittance of ITO films. The change arises from the elimination of oxygen vacancies and reduction of tin oxides, resulting in the decrease of carrier concentration. Finite element simulations indicate that laser annealing with pulse width of 875 ps and 10 ns have high instantaneous peak temperatures of 1128.5 K and 783 K, respectively, while the temperature accumulation between pulses is negligible. On the contrary, the laser annealing with a pulse width of 300 nshas lower peak transient temperature of 343 K but high static residence temperature of 973 K. The results reveal that the modification of ITO films depends more on the static average temperature rather than the instantaneous peak temperature. The modulation of carrier dynamics in both amplitude and temporal domain was demonstrated after 300 ns laser annealing, achieving ultrafast transient response approximately 150 fs. This work provides theoretical and experimental basis for us to select suitable laser conditions for directional annealing of ITO film to make it suitable for the applications of broad optical spectrum photovoltaic devices or ultrafast optical exchange for high-speed data processing. • Laser annealing (LA) is shown for three pulse widths at approximately 0.2 J/cm2. • LA at 300 ns significantly improves the near-infrared transparency due to the reduction of carrier absorption. • Tailorable amplitude and time scale of carrier transient response are achieved by LA, with ultrafast response time 150 fs. • The modification of ITO properties depends on the static temperature rather than transient peak temperature. [ABSTRACT FROM AUTHOR]

Different laser damage testing protocols, including 1-on-1, S-on-1, and Raster Scan, were conducted on 532 nm polarizers to evaluate the damage resistance and mechanisms. A comparison of the laser-induced damage thresholds (LIDTs) revealed different damage characteristics and major contributions to film failure for different polarizations. For P polarization, the LIDTs for the three test protocols were nearly the same because of the stabilization of two typical damage morphologies of flat-bottomed pits and mussel damage pits. For S polarization, the LIDTs for multiple pulses were lowest, where absorptive defect-induced damage was revealed. The damage characteristics of 532 nm polarizers and 1064 nm polarizers have been also compared. The mussel damage pits, which are similar to the typical damage morphologies of ultraviolet (UV) laser damage to fused silica, were observed for the first time in coatings of 532 nm polarizers. This suggests that, the polishing-induced subsurface damage of fused silica substrates may tend to be excited by a short-wavelength laser rather than the fundamental wavelength. • The damage resistance and damage characteristics of 532 nm polarizers in different laser damage test protocols, including 1-on-1, S-on-1, and Raster Scan, have been summarized, as a reference for thin-film optics in high-power laser applications. • The damage characteristics of 532 nm polarizers and 1064 nm polarizers were compared. The subsurface damage of fused silica substrates is easily excited by short-wavelength lasers. • Mussel pits, associated with the ultraviolet laser damage of fused silica, were observed in the coatings for the first time. [ABSTRACT FROM AUTHOR]