Search

Acetylation is a breakthrough in wood modification and has been established on industrial scale. However, concerns have been raised regarding the stability of acetylated wood under elevated temperatures, particularly during post hot-pressing processes to manufacture products such as laminated veneer lumber (LVL). At around 150 °C, the added acetyl groups might cleave off (“de-acetylation”) and by that release sorption sites for water. This would increase the moisture uptake of the modified wood. In this study, the impact of hot-pressing at 150 °C on the stability of acetylated beech veneers and LVL was investigated. Fourier transform infrared (FTIR) spectroscopy showed that the chemical composition of acetylated veneers seemed to be unaffected after the heat treatment. Dynamic vapor sorption (DVS) analysis and long-term storing over saturated salt-solutions in miniature climate chambers, indicated no de-acetylation on the basis of negligible changes in wood-water interactions. The number of hydroxyl groups of heat-treated acetylated samples was similar to that of not heat-treated ones, indicating the persistence of the effects of acetylation. By the present study, a certain resilience of acetylated wood towards elevated temperature, like it may occur during hot-pressing of acetylated veneers, became apparent and illustrated the thermal stability of this chemical modification approach. [ABSTRACT FROM AUTHOR]

The combination of different wood-modification technologies to obtain improved performance is increasingly receiving attention in research. In this study, Scots pine (Pinus sylvestris) sapwood was impregnated with furfuryl alcohol (FFA) in pure aqueous 20, 40, and 60% solution strength without adding any catalyst. In a second step, the FFA was polymerized while simultaneously performing thermal modification in a closed system at 130, 150, or 180 °C. After leaching and ageing tests, the nine different combinations were tested in use class 4 applications (in contact with or very close to the ground and frequently wet) according to CEN/TS 15083-2 (2005) decay laboratory test. It was noted that even the minimum-intensity combination of 20% FFA at 130 °C resulted in maximum durability class (DC) 1 performance. On the contrary, DC 4 was assigned to thermally modified control samples, even at the maximum intensity of thermal modification. Similarly, for FFA modifications, previous research has suggested that an uptake of 35% solution strength is required to obtain an adequate durability performance in use class 4 applications. High levels of resistance against termites were also noted by corresponding termite lab tests. Moisture studies showed the combined treatments resulted in improved stability and reduced moisture uptakes. Thus, the results obtained by this study revealed synergistic performance effects, which originate from the combined thermo-chemical modification approach, and which were higher than simple accumulation of the individual performance of purely thermally or chemically modified wood. Thus, the presented findings have provided positive implications for industrial applications of thermo-chemical modification techniques and offers an array of new research opportunities. [ABSTRACT FROM AUTHOR]

The application of tree of heaven (Ailanthus altissima (Mill.) Swingle) is constrained by its poor durability and dimensional stability. Despite exhibiting promising physical and mechanical properties comparable to ash wood (Fraxinus excelsior L.), it is regarded as an invasive species and receives limited attention in wood property enhancement research. This study subjected tree of heaven to heat treatment at 180 °C and 200 °C to investigate its sorption characteristics using dynamic vapor sorption tests. The results revealed a 13% reduction in equilibrium moisture content at 95% relative humidity and 25 °C after thermal modification at 180 °C and a 25% reduction after thermal modification at 200 °C. Increasing the treatment temperature lowered the moisture content ratio to 0.76 and shortened the conditioning time by up to 10%. The highest hysteresis, ranging from 3.39% to 3.88%, was observed at 70% relative humidity. [ABSTRACT FROM AUTHOR]

Wood modification with thermosetting resins results in improved dimensional stability and durability. However, the treatment does not enhance fire resistance. To address this, Scots pine sapwood (Pinus sylvestris L.) was impregnated with thermosetting resins such as 1,3-dimethylol-4,5-dihydroxyethyleneurea, phenol-formaldehyde resin and melamine-formaldehyde resin, along with a phosphorus polyol as the flame retardant. Both weight percent gain and cell wall bulking were measured to investigate the deposition of resin and phosphorus polyol. Fire resistance was assessed through thermogravimetric analysis, Bunsen burner test and mass loss calorimeter. The inclusion of a phosphate polyol improved thermal stability, reduced flammability and heat release. Melamine-formaldehyde resin combined with phosphorus polyol demonstrated self-extinguishing capability with the heat release rate comparable to non-combustible materials inside 400 s. Moreover, the total heat release within 600 s shows an 84% reduction compared to untreated wood. [ABSTRACT FROM AUTHOR]